Preparation of porous magnesium phosphate material and its application in structural supercapacitors

MA Weiyuan; ZHANG Dong

doi:10.11949/j.issn.0438-1157.20180392

您当前的位置：

首页 >

文章列表页 >

Preparation of porous magnesium phosphate material and its application in structural supercapacitors

更新时间：2025-12-10

- Preparation of porous magnesium phosphate material and its application in structural supercapacitors
- CIESC Journal Issue 10, Pages: 4438-4448(2018)
- 作者机构：
  
  同济大学材料科学与工程学院, 先进土木工程材料教育部重点实验室,上海,201804
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20180392
  CLC： Q031.2
- Online First：05 October 2018，
  
  Published：05 October 2018
- 稿件说明：
移动端阅览
MA Weiyuan, ZHANG Dong. Preparation of porous magnesium phosphate material and its application in structural supercapacitors[J]. CIESC Journal, 2018, (10): 4438-4448.
DOI：

MA Weiyuan, ZHANG Dong. Preparation of porous magnesium phosphate material and its application in structural supercapacitors[J]. CIESC Journal, 2018, (10): 4438-4448. DOI： 10.11949/j.issn.0438-1157.20180392.

摘要

以NaHCO3为引气剂，利用化学发泡法制备磷酸镁多孔材料（MPCPM），该材料孔径发达、强度较高。利用MPCPM和KOH复合形成结构载体/电解质双连续相系统，并与石墨烯电极组装成一种新型结构超级电容器。研究发现，MPCPM孔隙连通度是影响结构超级电容器电学性能的主要因素。内部连通孔隙结构有利于离子的运输，从而改善结构超级电容器的储能容量。使用循环伏安、交流阻抗、恒流充放电以及抗压强度测试等方法研究化学发泡剂NaHCO3掺量及养护龄期对结构超级电容器电学性能和力学性能的影响。NaHCO3掺量为2.5%时比电容最高可达62.2 F·g-1，比不掺加NaHCO3时提高了34.1%。并且当NaHCO3掺量为2%其比电容为38.79 F·g-1，同时抗压强度高达18.76 MPa，显示出良好的多功能性。

Abstract

The magnesium phosphate based porous material (MPCPM) was prepared by chemical foaming method using NaHCO3 as an air entraining agent. The MPCPM was characteristic of developed pore structure and high strength

hence it is possible to develop a multifunctional composite which is prepared by the MPCPM supportor and KOH electrolyte. The composite was sandwiched by two graphene electrodes

then a novel structural supercapacitor was fabricated. Experimental results show that electrochemical properties of the structural supercapacitor can be attributed to the pore connectivity of MPCPM. The MPCPM contains a great amount of connected pores which can provide paths for ion motion and ion storage. The effects of the NaHCO3 content and the curing age on the electrochemical and mechanical properties of the structural supercapacitor were analyzed. CV

EIS and CD analyses reveal that the structural supercapacitor exhibits ideal capacitive behavior and charge/discharge performance. The maximum specific capacitance is as high as 62.2 F·g-1 with the NaHCO3 content at 2.5%

it is increased by 34.1% compared with the MPCPM without addition of NaHCO3. Moreover

the structural supercapacitor exhibits a specific capacitance of 38.79 F·g-1 and a compressive strength of 18.76 MPa with the NaHCO3 content at 2%. It can achieve a balance between electrochemical performance and mechanical property. And this novel structural supercapacitor may have potential application in multifunctional civil engineering structures.

关键词

Keywords

references

Views

128

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Influence of support on the performance of single atom electrocatalyst for ammonia synthesis and the control strategy

Research progress in preparation technology of pitch-based carbon anode materials for sodium-ion batteries

Advances in lignin-derived carbon anodes for alkali metal ion batteries

Adjusting carbonization process to optimize sodium storage performance of coal-based hard carbon anode

Study on sodium storage behavior of hard carbons derived from coal with different grades of metamorphism

Related Author

JI Zhijiao

ZHANG Xiaofang

GAN Wen

XUE Yunpeng

WU Xi

SUN Bo

LIU Yindong

QI Chuanlei

Related Institution

National Institute of Clean-and-Low-Carbon Energy

State Key Laboratory of Heavy Oil Processing, China University of Petroleum

PetroChemical Research Institute Company Limited, CNPC

School of Chemical Engineering and Light Industry, Guangdong University of Technology

Guangdong Provincial Key Laboratory of Plant Resources Biorefinery

⁰