Effects of different accelerated tests on failure process of epoxy/polyurethane coating

HU Mingtao; JU Pengfei; ZHAO Xuhui; TANG Yuming; ZUO Yu

doi:10.11949/j.issn.0438-1157.20180256

您当前的位置：

首页 >

文章列表页 >

Effects of different accelerated tests on failure process of epoxy/polyurethane coating

更新时间：2025-12-10

- Effects of different accelerated tests on failure process of epoxy/polyurethane coating
- CIESC Journal Issue 8, Pages: 3548-3556(2018)
- 作者机构：
  
  1. 北京化工大学材料科学与工程学院,北京,100029
  2. 上海航天设备制造总厂,上海,200245
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20180256
  CLC： G174.46
- Online First：05 August 2018，
  
  Published：05 August 2018
- 稿件说明：
移动端阅览
HU Mingtao, JU Pengfei, ZHAO Xuhui, et al. Effects of different accelerated tests on failure process of epoxy/polyurethane coating[J]. CIESC Journal, 2018, (8): 3548-3556.
DOI：

HU Mingtao, JU Pengfei, ZHAO Xuhui, et al. Effects of different accelerated tests on failure process of epoxy/polyurethane coating[J]. CIESC Journal, 2018, (8): 3548-3556. DOI： 10.11949/j.issn.0438-1157.20180256.

摘要

研究了模拟南海海洋大气环境下铝合金表面环氧锌黄/丙烯酸聚氨酯涂层体系的失效过程，通过循环加速、紫外/冷凝和中性盐雾的对比试验，探讨了在循环加速试验中紫外-冷凝试验和盐雾试验分别对复合涂层失效过程以及对聚氨酯面漆和环氧底漆失效机制的影响。结果表明，紫外-冷凝过程对丙烯酸聚氨酯面漆有较强的破坏作用，但对复合涂层体系整体的阻抗变化影响较小；紫外-冷凝过程中，位于面漆玻璃化转变温度范围内的试验温度，以及紫外光对氨基甲酸酯基团的破坏作用，是导致面漆发生破坏的主要原因。盐雾试验对面漆的失光率和色差变化影响不大，但连续的盐雾渗透对涂层体系的阻抗下降具有明显的加速作用，同时导致涂层与基材的附着力显著降低。相比单独的紫外-冷凝试验或盐雾试验，循环加速试验综合考虑了南海海洋大气中强太阳辐射、高温高湿、高盐分和温差等环境因素，能更准确反映南海大气环境中复合涂层的失效过程。

Abstract

Failure process of epoxy zinc yellow primer/acrylic polyurethane coating system on aluminum alloy substrate was studied under simulated ocean atmosphere environment. By comparative evaluation at cyclic acceleration

UV/condensation and neutral salt spray conditions

effects on failure modes of epoxy primer

polyurethane topcoat and composite coating were assessed. Results showed that UV/condensation had strong destructive effect on acrylic polyurethane topcoat

but had little effect on impedance change of overall composite coating. During UV/condensation process

experimental temperature within glass transition temperature of topcoat and UV damage on carbamate group were main reasons for topcoat destruction. Salt spray had minimal effect on change of gloss loss and color difference

whereas consistent salt spray infiltration obviously accelerated impedance decrease of the coating system and caused significant reduction of adhesion between primer and substrate. Compared to UV/condensation or salt spray test alone

cyclic accelerated tests considered influences of different environmental factors such as strong solar radiation

high temperature and humidity

high salinity and temperature difference in ocean atmosphere of the South Sea

which can more accurately reflect failure process of the coating system in the region.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Study on the protective behavior of heavy-duty anti-corrosive coatings/TA2 in simulated ultra-deep sea 10000 meters environment

Preparation and properties of superhydrophobic aluminum alloy via chemical-electrochemical synergistic etching

Corrosion behavior and coating performance of carbon steel in HCl/NaOH thermal medium in wide temperature zone

Study of anode materials for electrocatalytic decomposition of liquid ammonia

Study on the occurrence and development mechanism of pipeline corrosion behind butterfly valve

Related Author

ZHANG Heqi

LU Weizhong

LI Guohua

WANG Hongfei

CHEN Ying

ZHAO Bin

LIAO Jing

REN Yanjie

Related Institution

College of Chemical Engineering, Zhejiang University of Technology

State Key Laboratory of Marine Critical Materials, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences

School of Materials Science and Chemical Engineering, Ningbo University

College of Energy and Power Engineering, Changsha University of Science and Technology

College of Intelligent Manufacturing and Energy Engineering, Zhejiang University of Science and Technology

⁰