Synthesis process optimization and degradation properties of PLA/PBAu block copolymer

CUI Lingna; LIU Yuejun

doi:10.11949/j.issn.0438-1157.20180255

您当前的位置：

首页 >

文章列表页 >

Synthesis process optimization and degradation properties of PLA/PBAu block copolymer

更新时间：2025-12-10

- Synthesis process optimization and degradation properties of PLA/PBAu block copolymer
- CIESC Journal Issue 9, Pages: 4075-4082(2018)
- 作者机构：
  
  湖南工业大学先进包装材料与技术湖南省重点实验室,湖南,株洲,412007
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20180255
  CLC： B34
- Online First：05 September 2018，
  
  Published：05 September 2018
- 稿件说明：
移动端阅览
CUI Lingna, LIU Yuejun. Synthesis process optimization and degradation properties of PLA/PBAu block copolymer[J]. CIESC Journal, 2018, (9): 4075-4082.
DOI：

CUI Lingna, LIU Yuejun. Synthesis process optimization and degradation properties of PLA/PBAu block copolymer[J]. CIESC Journal, 2018, (9): 4075-4082. DOI： 10.11949/j.issn.0438-1157.20180255.

摘要

以端羟基聚乳酸（PLA）、聚己二酸-丁二醇-尿素（PBAu）为预聚物，六亚甲基二异氰酸酯（HDI）为扩链剂，制备出一种新型PLA/PBAu嵌段共聚物。研究了扩链剂用量、扩链温度以及催化剂用量对PLA/PBAu嵌段共聚物分子量的影响，确定了合成PLA/PBAu嵌段共聚物的最佳工艺条件。采用核磁共振、凝胶渗透色谱、差示扫描量热仪、扫描电镜等对共聚物薄膜结构及性能进行表征。结果表明：成功合成了PLA/PBAu嵌段共聚物，分子量可达10×104，玻璃化转变温度约为41℃；并且随着PBAu含量的增加，共聚物的结晶度逐渐增加。以NaOH溶液为模拟液进行加速降解实验发现，当PBAu含量为30%时，可以显著提高嵌段共聚物的降解速率，并且通过调节PLA、PBAu预聚物的含量，可以控制嵌段共聚物的降解速率。

Abstract

A novel PLA/PBAu block copolymer was synthesized by using the hydroxyl terminated poly(lactic acid) (PLA) and poly(butyl acrylate urea) (PBAu) as prepolymer and the hexamethylene diisocyanate (HDI) as chain extender. To determine the optimum synthesis condition for the chain extension

the effects of the amount of chain extender

the chain extension temperature and the amount of catalyst on the PLA/PBAu block copolymer molecular weight were studied. The structure and properties of the films were studied by nuclear magnetic resonance

gel permeation chromatograph

differential scanning calorimetry and scanning electron microscope. The results showed that the PLA/PBAu block copolymer was successfully synthesized

and the molecular weight of the copolymer can reach to 105 with glass transition temperature of 41℃. The crystallization of copolymer films increased with the increase of PBAu content. The accelerated degradation experiment of block copolymers was studied with NaOH solution as the degradation solution. The results showed the degradation rate of copolymer can be significantly improved when the content of PBAu was 30%. The degradation rate of block copolymer could be controlled by adjusting the content of PLA and PBAu prepolymer.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Effect on dithiosalicylic acid derivative on properties of photocuring materials

Review on synthesis of polyether-co-polyester from copolymerization of epoxides and lactones

Synthesis and properties of novel poly(triazole ester) and poly(triazole ether) resins

Preparation of attapulgite/polystyrene hybrid particles via simultaneous reverse and normal initiation atom transfer radical polymerization

Preparation of poly(styrene-b-butyl acrylate-b-styrene) copolymers by single electron transfer-degenerative chain transfer living free radical miniemulsion polymerization

Related Author

Xiaobing JU

Xuechun LI

Fang SUN

Hongjuan GAO

Weimin REN

Haijun WANG

Luyu WANG

Mingming MA

Related Institution

College of Chemistry, Beijing University of Chemical Technology

Anqing Research Institute, Beijing University of Chemical Technology

State Key Laboratory of Fine Chemicals, Dalian University of Technology

Key Laboratory of Specially Functional Polymeric Materials and Related Technology of Ministry of Education, East China University of Science and Technology

National Experimental Demonstration Center for Materials Science and Engineering, School of Materials Science and Engineering, Changzhou University

⁰