Synthesis and properties of hierarchical structure silver micro-nanocrystals

NIE Shidong; LI Jiangtao; ZHANG Zhiying; LIU Yun; LIU Chunyan

doi:10.11949/j.issn.0438-1157.20180214

您当前的位置：

首页 >

文章列表页 >

Synthesis and properties of hierarchical structure silver micro-nanocrystals

更新时间：2025-12-10

- Synthesis and properties of hierarchical structure silver micro-nanocrystals
- CIESC Journal Issue 9, Pages: 4090-4096(2018)
- 作者机构：
  
  1. 中国科学院理化技术研究所光化学转换与功能材料重点实验室,北京,100190
  2. 中国科学院大学,北京,100049
  3. 中国科学院理化技术研究所功能晶体与激光技术重点实验室,北京,100190
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20180214
  CLC： 69
- Online First：05 September 2018，
  
  Published：05 September 2018
- 稿件说明：
移动端阅览
NIE Shidong, LI Jiangtao, ZHANG Zhiying, et al. Synthesis and properties of hierarchical structure silver micro-nanocrystals[J]. CIESC Journal, 2018, (9): 4090-4096.
DOI：

NIE Shidong, LI Jiangtao, ZHANG Zhiying, et al. Synthesis and properties of hierarchical structure silver micro-nanocrystals[J]. CIESC Journal, 2018, (9): 4090-4096. DOI： 10.11949/j.issn.0438-1157.20180214.

摘要

采用液相还原法，通过调控氧化剂硝酸银与还原剂抗坏血酸的摩尔比例制备出具有多级结构的花状及枝状银微-纳米晶，考察了反应介质对形貌及尺寸的影响。利用扫描电子显微镜（SEM）、X射线衍射仪（XRD）、表面增强拉曼光谱（SERS）、紫外-可见（UV-Vis）漫反射光谱等方法，对样品的形貌、微晶结构、光学及催化性能进行了研究。结果表明：花状及枝状多级结构银微-纳米晶均具有面心立方晶体结构，且（111）晶面为主要曝露晶面；表面增强拉曼光谱表明花状及枝状银微-纳米晶为基底时均表现出优异的表面增强拉曼效应；微结构上的差异使枝状银在紫外-可见漫反射光谱上352 nm处有较强的吸收峰；在银催化硼氢化钠还原4-硝基苯酚的实验中，多级结构枝状银表现出最优良的催化活性。

Abstract

The flower-like and dendritic silver micro-nanocrystals with multi-stage structure were prepared by liquid phase reduction method by adjusting the molar ratio of oxidant silver nitrate to reducing agent ascorbic acid. The effects of reaction media on the size and morphology of silver crystallite was investigated. The morphology

crystal structure

optical and catalytic properties of the products were studied by scanning electron microscopy (SEM)

X-ray diffraction (XRD)

surface enhanced Raman scattering spectroscopy (SERS) and UV-Vis reflectance spectroscopy (UV-Vis). The XRD results show that both the flower-like and dendritic silver micro-nanocrystals have face-centered cubic crystal structure

and (111) plane is the dominant crystal plane exposed on the surface of Ag crystals. The SERS surveys show that the hierarchical structure Ag micro-nanocrystals are excellent substrates for SERS. The UV-Vis diffuse reflectance spectra shows that the dendritic silver has a strong absorption peak at 352 nm because of the finer microstructure. The catalytic reduction experiment of 4-nitrophenol by sodium borohydride on the silver crystals reveals that the dendritic silver shows excellent catalytic activity.

关键词

Keywords

references

Views

101

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Effect of preparation conditions on low-temperature co-removal of COS and CS2 from modified calcium carbide slag

Research progress on gas pollutants removal by defective metal oxides

Preparation and purification of 6N electronic-grade deuterium gas

Study on formaldehyde ethynylation performance of CuO nanocrystalline confined in SiO2 networks

Degradation of bisphenol A by peroxymonosulfate activated by MnFe2O4 prepared by salt-assisted solution combustion synthesis

Related Author

TANG Yinxiang

ZHU Feng

FAN Yingying

LONG Yuxin

DAI Yong

DENG Chunling

HUANG Xiaofeng

YANG Shenghua

Related Institution

School of Environmental Science and Engineering, Kunming University of Science and Technology

College of Science, Kunming University of Science and Technology

State Key Laboratory of Clean and Efficient Coal Utilization, Taiyuan University of Technology

Key Laboratory of Coal Science and Technology, Ministry of Education, Taiyuan University of Technology

College of Environmental and Ecological Engineering, Taiyuan University of Technology

⁰