Preparation and characterization of AgO ordered array electrode materials

TIAN Hua; ZHANG Zhiying; LIU Chunyan

doi:10.11949/j.issn.0438-1157.20180190

您当前的位置：

首页 >

文章列表页 >

Preparation and characterization of AgO ordered array electrode materials

更新时间：2025-12-10

- Preparation and characterization of AgO ordered array electrode materials
- CIESC Journal Issue 8, Pages: 3711-3716(2018)
- 作者机构：
  
  1. 光化学转换与功能材料重点实验室, 中国科学院理化技术研究所,北京,100190
  2. 中国科学院大学,北京,100049
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20180190
  CLC： Q152
- Online First：05 August 2018，
  
  Published：05 August 2018
- 稿件说明：
移动端阅览
TIAN Hua, ZHANG Zhiying, LIU Chunyan. Preparation and characterization of AgO ordered array electrode materials[J]. CIESC Journal, 2018, (8): 3711-3716.
DOI：

TIAN Hua, ZHANG Zhiying, LIU Chunyan. Preparation and characterization of AgO ordered array electrode materials[J]. CIESC Journal, 2018, (8): 3711-3716. DOI： 10.11949/j.issn.0438-1157.20180190.

摘要

在浓氢氧化钠溶液中，通过电化学方法氧化银纳米颗粒制备得到AgO有序阵列结构电极材料。性能表征表明，所制备的AgO材料具有独特的直通孔阵列结构，有利于电解质溶液在孔隙中的扩散，可直接用作Al/AgO电池阴极，无需黏结剂等。与常规AgO阴极材料相比，同等条件下，以AgO有序阵列结构材料为阴极所组成电池的放电性能大幅提高，3 C倍率下质量比容量可达422.6 mA·h·g-1，电极活性材料的利用率为97.8%，7 C倍率下质量比容量依然有387.8 mA·h·g-1，活性物质利用率89.7%。同时，循环性能相比传统电极也得到大幅提升，在第10个循环时依然保持着405.2 mA·h·g-1的质量比容量。制备方法易于操作且高效环保，有利于工业化生产；所得材料具有独特结构和性能优势。

Abstract

AgO ordered array materials were synthesized by electrochemical oxidization of Ag naoparticles in sodium hydroxide solution. As the characterizations of properties revealed

the prepared AgO material has unique straight-through hollow structure

bringing a positive effect on the dispersion of electrolyte inside materials

which would result in better electrochemical properties of corresponding batteries. Thus prepared AgO material could be used as an electrode directly without any binders. The electrode offered a discharge capacity of 422.6 mA·h·g-1 at 3 C rate and utilization ratio of electrode material could reach 97.8% as a cathode of Al/AgO battery (stopping potential is 0.5 V and reference electrode is Ag/Ag+ electrode). There was still a capacity of 387.8 mA·h·g-1 at 7 C rate with utilization ratio 89.7%. Meanwhile

the cycling performance was also improved and a specific capacity of 405.2 mA·h·g-1 could still be offered at the 10th cycle. The work provides a facile and eco-friendly method and the prepared AgO materials would have unique advantages in practical applications.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Investigation on synthesis conditions of LiNi1-x-yCoxMnyO2 cathode material via co-precipitation

Preparation of monodisper microsphere by controlled droplet solidification

Investigation on the static properties and annihilation characteristics of particle clusters in gas-solid fluidized beds

Research on mesoscale flow characteristics of particles in a riser

High-performance electrocatalytic semi-hydrogenation of acetylene to ethylene via MOF derived Cu/N-C catalyst

Related Author

GENG Shujun

HUANG Qingshan

ZHU Quanhong

JIN Yongcheng

YANG Chao

LI Chunlin

XIE Hua

LIU Na

Related Institution

Qingdao Institute of Bioenergy and Bioprocess Technology, Chinese Academy of Sciences

Key Laboratory of Green Process and Engineering, Institute of Process Engineering, Chinese Academy of Sciences

Dalian Institute of Chemical Physics, Chinese Academy of Sciences

State Key Laboratory of Mesoscience and Engineering, Institute of Process Engineering, Chinese Academy of Sciences

School of Chemical Engineering, University of Chinese Academy of Sciences

⁰