Kinetic study on thermal decomposition of GFRP under γ irradiation

ZHENG Lifang; WANG Zhaozhong; XIE Yajie; YUE Lina; WANG Li

doi:10.11949/j.issn.0438-1157.20180175

您当前的位置：

首页 >

文章列表页 >

Kinetic study on thermal decomposition of GFRP under γ irradiation

更新时间：2025-12-10

- Kinetic study on thermal decomposition of GFRP under γ irradiation
- CIESC Journal Issue S1, Pages: 161-169(2018)
- 作者机构：
  
  1. 北京科技大学机械工程学院,北京,100083
  2. 北京科技大学材料科学与工程学院,北京,100083
  3. 华北科技学院环境工程学院,北京,101601
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20180175
  CLC： B332TL349
- Online First：30 September 2018，
  
  Published：30 September 2018
- 稿件说明：
移动端阅览
ZHENG Lifang, WANG Zhaozhong, XIE Yajie, et al. Kinetic study on thermal decomposition of GFRP under γ irradiation[J]. CIESC Journal, 2018, (S1): 161-169.
DOI：

ZHENG Lifang, WANG Zhaozhong, XIE Yajie, et al. Kinetic study on thermal decomposition of GFRP under γ irradiation[J]. CIESC Journal, 2018, (S1): 161-169. DOI： 10.11949/j.issn.0438-1157.20180175.

摘要

玻璃纤维增强塑料（GFRP）因其良好的热绝缘性能和力学性能，在高能物理和核物理实验领域被用来制作支撑设备，而高能物理和核物理实验会对其支撑设备产生一定的γ和中子辐照，为保证GFRP支撑设备在γ辐照条件下的结构稳定性，需研究辐照对其热分解性能的影响。结果表明，GFRP在氮气氛围中的热分解可分为3个阶段；GFRP失重率随辐照剂量的增大而增大；辐照使GFRP的活化能增加，Friedman法计算得出平均活化能由辐照前的96.1 kJ·mol-1增加到200 kGy辐照后的116.6 kJ·mol-1，Flynn-Wall-Ozawa（FWO）法计算得出平均活化能由辐照前的107.6 kJ·mol-1增加到200 kGy辐照后的125.4 kJ·mol-1。扫描电镜对微观形貌观察发现辐照后环氧树脂与玻璃纤维结合度降低，差示扫描量热法分析得出辐照使环氧树脂进一步固化反应。

Abstract

Glass fiber reinforced plastic (GFRP) is used as support material for high energy physics and nuclear physics experiments due to its excellent thermal insulation and mechanical performance. High-energy physics and nuclear physics experiments produce large amounts of γ and neutron irradiation to the support material. In order to ensure the stability of GFRP under γ-irradiation conditions

the kinetic model of pyrolysis needs to be establish to calculate the activation energy under different irradiation doses. The obtained results show that the pyrolysis process of GFRP in a nitrogen atmosphere can be divided into three stages

the main mass loss stage occurs at 200-470℃. With the increase of radiation dose

the mass loss rate of GFRP increased. After 20

100 and 200 kGy γ irradiation

the mass loss rate of GFRP increased from 31.1% to 32.7%

35.5% and 37.5%

respectively

by 2%

3.9% and 4.4%. With the heating rate increased the mass loss rate increased significantly. After 200 kGy γ irradiation

the average activation energy of GFRP calculated by Friedman method was increased from 96.1 kJ·mol-1 to 116.6 kJ·mol-1

which increased by 21.3%. The average activation energy of GFRP calculated by FWO method was increased from 107.6 kJ·mol-1 to 125.4 kJ·mol-1

which increased by 16.5%. Microstructure analysis by SEM found that the binding degree of the glass fiber and the epoxy declines after γ irradiation

differential scanning calorimetry indicates that the curing reaction occur of epoxy in the irradiation process.

关键词

Keywords

references

Views

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Preparation of C/TiO2-SO42- and their water splitting performance

Characterization of co-pyrolysis of pine sawdust and coal slime under isothermal conditions in micro fluidized bed reactor

Influence mechanism of H2S on reactivity of NiFe2O4 oxygen carriers for chemical looping combustion

Preparation and performance of Pr3+: Y2SiO5/TiO2 composites deposited on activated carbon fiber

Grafting of organic polymer in pores of macroporous silica vesicle material

Related Author

WANG Mingxing

LIU Lulu

REN Chao

YANG Renchun

TENG Xuegang

WANG Yan

GUO Feiqiang

LI Tiantao

Related Institution

School of Biological and Chemical Engineering, Anhui Polytechnic University

School of Mechanical Engineering, Shandong University

School of Electrical and Power Engineering, China University of Mining and Technology

State Key Laboratory of Coal Combustion, Huazhong University of Science and Technology

School of Environmental and Biological Engineering, Nanjing University of Science and Technology

⁰