Hydrothermal synthesis of reduced graphene oxide with tunable conductivity

WENG Chengjie; SHI Yexun; HE Dafang; SHEN Liming; BAO Ningzhong

doi:10.11949/j.issn.0438-1157.20171582

您当前的位置：

首页 >

文章列表页 >

Hydrothermal synthesis of reduced graphene oxide with tunable conductivity

更新时间：2025-12-10

- Hydrothermal synthesis of reduced graphene oxide with tunable conductivity
- CIESC Journal Issue 7, Pages: 3263-3269(2018)
- 作者机构：
  
  1. 南京工业大学化工学院, 材料化学工程国家重点实验室,江苏,南京,210009
  2. 江苏省产业技术研究院石墨烯材料研究所,江苏,常州,213100
  3. 江南石墨烯研究院,江苏,常州,213149
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20171582
  CLC： B303
- Online First：05 July 2018，
  
  Published：05 July 2018
- 稿件说明：
移动端阅览
WENG Chengjie, SHI Yexun, HE Dafang, et al. Hydrothermal synthesis of reduced graphene oxide with tunable conductivity[J]. CIESC Journal, 2018, (7): 3263-3269.
DOI：

WENG Chengjie, SHI Yexun, HE Dafang, et al. Hydrothermal synthesis of reduced graphene oxide with tunable conductivity[J]. CIESC Journal, 2018, (7): 3263-3269. DOI： 10.11949/j.issn.0438-1157.20171582.

摘要

导电性可调控的还原氧化石墨烯（rGO）在结构功能材料和化工新材料等领域具有重要的应用前景。本文利用水热还原法实现了rGO的绿色制备，并通过调控反应温度和时间，获得了电导率可控的rGO产品，其电导率范围为10-4～1 S·cm-1。采用UV-vis、FT-IR、XPS、SEM、XRD和Raman等表征方法系统研究了rGO还原过程中结构与组成的变化。发现GO还原过程中，其含氧官能团于120℃时开始明显分解，高于140℃后含量显著降低，GO片层sp2区域逐渐恢复，电导率逐渐增大到1 S·cm-1，同时层间距从8.2 Å减少到3.6 Å（1 Å=0.1 nm）。对比热还原法，水热法有效避免了rGO片层的堆叠，产物分散性较好，有望规模化制备导电性可控的rGO产品。本研究成果对rGO生产和应用具有重要意义。

Abstract

Reduced graphene oxide (rGO) with tunable conductivity has great promise for potential applications in the fields of advanced structural-functional composites

new chemical materials and so on. In this research

environment-friendly hydrothermal method was applied to prepare rGO. The conductivity of the synthesized rGO can be controlled from 10-4 to 1 S·cm-1 by changing the hydrothermal reaction temperature and time. Various characterization techniques such as UV-vis

FT-IR

XPS

SEM

XRD

and Raman spectroscopy were used to analyze the composition and structure change of the rGO. The results showed that the oxygen contained functional groups on the rGO surface decomposed rapidly at ≥ 120℃

and the content of oxygen contained functional groups decreased drastically at ≥ 140℃. Meanwhile

the carbon sp2 region of the rGO was recovered gradually

which caused the conductivity increased to 1 S·cm-1 and the interlayer spacing decreased from 8.2 Å to 3.6 Å. Compared with thermal reduction method

hydrothermal method avoids the aggregation and stacking of the rGO

which has great significance in large-scale production of the rGO with tunable conductivity.

关键词

Keywords

references

Views

424

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Preparation of tungstate nanomaterials and research progress in electrochromic field

Thermoelectric transport properties of graphyne with different structures based on first principles

Chemical modification of nanocellulose via atom transfer radical polymerization: strategy, applications and challenges

Method of determining optimum mass ratio of fatty acids in composite phase change materials for thermal energy storage

Research progress on magnesium-based intercalated functional materials

Related Author

PENG Jian

SHEN Lukai

WANG Likun

XIN Lihong

LIU Yong

ZHAO Gaoling

MA Sainan

HAN Gaorong

Related Institution

Ningbo Innovation Center, Zhejiang University

College of Materials Science and Engineering, Zhejiang University

Freestyle Outdoor Living Company Limited

School of Mechanical Engineering, Beijing Institute of Petrochemical Technology

Innovation Center of Efficient Processing and Utilization of Forest Resources, College of Chemical Engineering, Nanjing Forestry University

⁰