Characteristics of solid-waste-based sulfoaluminate cementitious material being used in 3D printing and process simulation

REN Changzai; WANG Wenlong; LI Guolin; WANG Biao

doi:10.11949/j.issn.0438-1157.20171555

您当前的位置：

首页 >

文章列表页 >

Characteristics of solid-waste-based sulfoaluminate cementitious material being used in 3D printing and process simulation

更新时间：2025-12-10

- Characteristics of solid-waste-based sulfoaluminate cementitious material being used in 3D printing and process simulation
- CIESC Journal Issue 7, Pages: 3270-3278(2018)
- 作者机构：
  
  1. 山东大学燃煤污染物减排国家工程实验室,山东,济南,250061
  2. 新疆工程学院电力工程系,新疆,乌鲁木齐,830091
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20171555
  CLC： B34
- Online First：05 July 2018，
  
  Published：05 July 2018
- 稿件说明：
移动端阅览
REN Changzai, WANG Wenlong, LI Guolin, et al. Characteristics of solid-waste-based sulfoaluminate cementitious material being used in 3D printing and process simulation[J]. CIESC Journal, 2018, (7): 3270-3278.
DOI：

REN Changzai, WANG Wenlong, LI Guolin, et al. Characteristics of solid-waste-based sulfoaluminate cementitious material being used in 3D printing and process simulation[J]. CIESC Journal, 2018, (7): 3270-3278. DOI： 10.11949/j.issn.0438-1157.20171555.

摘要

为了解决建筑3D打印材料的性能、成本及技术应用等问题，通过以工业固体废弃物为原料制备了硫铝酸盐胶凝基质材料，配以促凝剂、缓凝剂等形成的建筑3D打印粉体，并应用多物理场耦合软件对同一喷嘴结构不同水灰比（W/C）下喷出浆体速度及质量的影响规律进行仿真计算。结果表明：以工业固体废弃物为原料能成功制备达到GB-2007-R525的硫铝酸盐胶凝材料，且经过外加剂改性后凝结时间可控制在10～30 min，2 h抗压强度15～20 MPa，后期强度稳定；水灰比高于0.6，打印浆体出现堆叠、坍塌的现象，影响打印精度及打印构件质量；水灰比低于0.4，喷射浆体会出现拖尾，影响打印速度，最终确定水灰比在0.5附近较适合相应尺寸喷嘴的3D打印应用。

Abstract

To obtain high performance

low cost and extend technology application

industrial solid wastes were used to prepare sulfoaluminate cementitious material (SCM)

which was then processed into three-dimensional (3D) printing materials by using a suitable accelerator and retarder. Multidiscipline coupled-field analysis was used to determine the influence of slurry velocity and the quality that results from different water-cement ratios with the same nozzle diameter. It was proved that the SCM prepared from industrial solid wastes could meet the national standard GB-2007-R525. After improving their properties

the SCMs exhibit advantages of a controlled setting time of between 10 and 30 min

a rapid hardening and an early stable strength. The hydrated-specimen compressive strength reached 15-20 MPa after 2 h of curing. When the water-cement ratio of the 3D printing-material slurry exceeded 0.6

stacking and collapse phenomena might be resulted. When the water-cement ratio was below 0.4

the jetted slurry showed tailing phenomena that could affect the printing speed. A water-cement ratio of~0.5 with its corresponding nozzle size was most suitable for 3D printing applications.

关键词

Keywords

references

Views

129

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Characteristics of dehydrated sludge based on chemical modification: low temperature hot-air drying

Thermo-gas-elastic coupling performance analysis of high-speed and high-temperature foil face seals

Research on the process path of sodium-based dry desulfurization ash combined with fly ash decalcification

Process parameters in the cooperative synthesis of polymorphic micro/nano calcium carbonate from power plant desulfurization gypsum and flue gas

Heat transfer characteristics during transcritical depressurization transient process in circulating fluidized bed

Related Author

LI Haiyan

LIU Huan

WANG Jiaxing

JIN Minghao

DENG Hongping

LU Geng

ZHANG Xiuju

YAO Hong

Related Institution

State Key Laboratory of Coal Combustion, School of Energy and Power Engineering, Huazhong University of Science and Technology

EU Institute for Clean and Renewable Energy, Huazhong University of Science and Technology,,, China

College of Mechanical and Electical Engineering, China Jiliang University

AECC Changjiang Engine Co., Ltd.

College of Mechanical Engineering, Zhejiang University of Technology

⁰