Separation performance of CO<sub>2</sub>/CH<sub>4</sub> on porous carbons derived from glucose

WANG Li; WANG Xingjie; LI Hao; CHEN Yongwei; LI Zhong

doi:10.11949/j.issn.0438-1157.20171368

您当前的位置：

首页 >

文章列表页 >

Separation performance of CO₂/CH₄ on porous carbons derived from glucose

更新时间：2025-12-10

- Separation performance of CO₂/CH₄ on porous carbons derived from glucose
- CIESC Journal Issue 2, Pages: 733-740(2018)
- 作者机构：
  
  1. 华南理工大学化学与化工学院,广东,广州,510640
  2. 亚热带建筑科学国家重点实验室,广东,广州,510640
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20171368
  CLC： 647.3
- Online First：05 February 2018，
  
  Published：05 February 2018
- 稿件说明：
移动端阅览
WANG Li, WANG Xingjie, LI Hao, et al. Separation performance of CO₂/CH₄ on porous carbons derived from glucose[J]. CIESC Journal, 2018, (2): 733-740. DOI: 10.11949/j.issn.0438-1157.20171368.
DOI：

WANG Li, WANG Xingjie, LI Hao, et al. Separation performance of CO₂/CH₄ on porous carbons derived from glucose[J]. CIESC Journal, 2018, (2): 733-740. DOI: 10.11949/j.issn.0438-1157.20171368. DOI：

摘要

以淀粉糖（主要成分为葡萄糖）为碳前体，制备了一系列多孔碳材料（C-GLCs-800），对其进行孔隙结构分析，并应用FT-IR、SEM、TGA对其进行了表征，测定了材料在288、298和308 K下的CO2和CH4吸附等温线，根据IAST理论预测了材料对CO2/CH4二元体系的吸附选择性。实验结果显示，活化条件对材料的孔隙结构有明显影响，随着KOH/C质量比的增加，所制备的C-GLCs-800比表面积和总孔容先增加后降低。其中C-GLC-800-4的BET比表面积高达3153 m2·g-1，总孔容为2.056 cm3·g-1。C-GLC-800-2的窄微孔（Vd<1 nm，孔容0.3538 cm3·g-1）含量最高，为30.63%。C-GLC-800-2在298 K和105 Pa下对CO2吸附量高达3.96 mmol·g-1，明显高于许多传统吸附材料和MOFs材料在相同条件下对CO2的吸附容量。应用Clausiuse-Clapeyron方程计算了CO2和CH4在材料上的吸附热，应用IAST理论计算了CO2/CH4的吸附选择性，结果显示C-GLC-800-2对CO2/CH4的吸附选择性为8.35。

Abstract

A series of glucose-based porous carbons (C-GLCs-800) were developed by simple carbonization and KOH activation

and characterized by scanning emission microscopy (SEM)

nitrogen sorption

Fourier transformed infrared (FI-TR) and thermogravimetric analysis (TGA). Pure component adsorption isotherms of CO2 and CH4 were measured separately at 288

298

and 308 K. The ideal adsorbed solution theory (IAST) model was used to estimate adsorption selectivity of the samples for CO2/CH4 binary mixtures. Results showed that the specific surface area and total pore volume of C-GLCs-800 increased at first and then decreased with the ratio of KOH/C at which the samples were activated. The BET surface area and total pore volume of C-GLC-800-4 reached as high as 3153 m2·g-1 of 2.056 cm3·g-1

respectively. The narrow micropores voulme of C-GLC-800-2 reached as high as 0.3538 cm3·g-1. The C-GLC-800-2 exhibited an extraordinary CO2 adsorption capacity of 3.96 mmol·g-1 at 298 K under 105 Pa

which was comparable to many traditional adsorbents and MOFs. The isosteric heats of CO2 adsorption on C-GLC-800-2 was higher than that of CH4. The IAST-predicted CO2/CH4 selectivity was about 8.35.

关键词

Keywords

references

Views

233

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Adsorption characteristics of CH4 and CO2 on Silurian shale in Sichuan Basin

The analysis of energy efficiency for TVSA-based direct air capture system

Metal-organic framework encapsulating carbon nanotubes for trace CO2 separation

Preparation and adsorption properties of temperature sensitive poly(N-isopropylacrylamide) /monosodium glutamate/ chitosan composites

Influence mechanism of free guest molecules in liquid phase on decomposition kinetics of CO₂-CH₄ hydrates

Related Author

YANG Fei

YUE Changtao

LI Shuyuan

MA Yue

XU Xinyi

LIU Shaonan

WU Junye

WANG Kuihua

Related Institution

College of Science, China University of Petroleum

Institute of Refrigeration and Cryogenics, Shanghai Jiao Tong University

State Key Laboratory of Multiphase Flow in Power Engineering, Xi’an Jiaotong University

College of Mechanical Engineering, Xi’an Shiyou University

School of Chemistry and Chemical Engineering, Xi'an University of Architecture and Technology

⁰

Separation performance of CO2/CH4 on porous carbons derived from glucose

DOI：10.11949/j.issn.0438-1157.20171368

摘要

Abstract

关键词

Keywords

references

Separation performance of CO₂/CH₄ on porous carbons derived from glucose