Coupling mechanism of viscose ash deposition and dewpoint corrosion in industrial coal-fired boiler

CHEN Heng; PAN Peiyuan; ZHAO Qinxin; LIANG Zhiyuan; WANG Yungang

doi:10.11949/j.issn.0438-1157.20170697

您当前的位置：

首页 >

文章列表页 >

Coupling mechanism of viscose ash deposition and dewpoint corrosion in industrial coal-fired boiler

更新时间：2025-12-10

- Coupling mechanism of viscose ash deposition and dewpoint corrosion in industrial coal-fired boiler
- CIESC Journal Issue 12, Pages: 4774-4783(2017)
- 作者机构：
  
  西安交通大学能源与动力工程学院热流科学与工程教育部重点实验室,陕西,西安,710049
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20170697
  CLC： K16
- Online First：05 December 2017，
  
  Published：05 December 2017
- 稿件说明：
移动端阅览
CHEN Heng, PAN Peiyuan, ZHAO Qinxin, et al. Coupling mechanism of viscose ash deposition and dewpoint corrosion in industrial coal-fired boiler[J]. CIESC Journal, 2017, (12): 4774-4783.
DOI：

CHEN Heng, PAN Peiyuan, ZHAO Qinxin, et al. Coupling mechanism of viscose ash deposition and dewpoint corrosion in industrial coal-fired boiler[J]. CIESC Journal, 2017, (12): 4774-4783. DOI： 10.11949/j.issn.0438-1157.20170697.

摘要

通过现场实验研究了燃煤工业锅炉的黏性积灰和露点腐蚀耦合机理，在现场测试了不同壁面温度（90、80、70、60、50和40℃）下20#碳钢实验段的积灰和腐蚀特性，然后利用XRF、XRD和SEM-EDS对灰样和金属试样进行了系统理化分析。结果表明，当壁面温度低至70℃时，H2SO4开始在壁面上冷凝并沉积，引起黏性积灰和露点腐蚀。随着壁面温度的降低，实验段上的积灰量和腐蚀层厚度不断增加。当壁面温度降至40℃时，HCl开始在壁面上冷凝并加重积灰和腐蚀。烟气中的飞灰可以通过吸附冷凝的酸液并与其反应来减少壁面的黏性积灰和露点腐蚀。燃煤工业锅炉的低温受热面宜控制壁面温度在70℃以上，以减少酸液冷凝造成的黏性积灰和露点腐蚀。

Abstract

Viscose ash deposition and dewpoint corrosion in an industrial coal-fired boiler were investigated by field study of temperature-controlled mild steel 20# test probes under different wall temperatures of 90℃

80℃

70℃

60℃

50℃ and 40℃. Ash deposits and metal samples were analyzed by X-ray fluorescence (XRF)

X-ray diffraction (XRD) and scanning electron microscope with energy dispersive X-ray spectroscopy (SEM-EDS). The results showed that when wall temperature fell to 70℃

viscose deposits and dewpoint corrosion began to form on probes due to condensation of H2SO4 on wall surface. The deposit accumulation and corrosion depth increased with the decrease of wall temperature

when wall temperature was lower than 80℃. At wall temperature of 40℃

HCl started condesing on wall surface which further enhanced ash deposition and corrosion. The coupling mechanism of viscose ash depostion and dewpoint corrosion was discussed and it was proposed that fly ash in flue gas could absorb and react with acid condensation to reduce viscose ash deposit and corrossion. Therefore

in order to avoid or reduce deposition and corrosion

it is recommended that low-temperature heating surface in industrial coal-fired boilers should be maintained above 70℃.

关键词

Keywords

references

Views

185

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

In-plant experimental study on desulfurized flue gas corrosion

Characteristics of ash deposit and dew point corrosion in biofuel boiler

Analysis and formation mechanism of condensates on surface of flue gas cooler of coal-fired power plant

Corrosion health status assessment method for refining unit pipeline based on GLAE-MLP

Study on the protective behavior of heavy-duty anti-corrosive coatings/TA2 in simulated ultra-deep sea 10000 meters environment

Related Author

Peiyuan PAN

Heng CHEN

Jian JIAO

Zhiyuan LIANG

Qinxin ZHAO

MA Haidong

WANG Yungang

ZHAO Qinxin

Related Institution

Key Laboratory of Thermo-Fluid Science and Engineering of MOE, School of Energy and Power Engineering, Xi’an Jiaotong University, Shaanxi

Key Laboratory of Thermo-Fluid Science and Engineering(Ministry of Education), Xi'an Jiaotong University

Key Laboratory of Thermo-Fluid Science and Engineering, Ministry of Education, Xi'an Jiaotong University

College of Safety and Ocean Engineering, China University of Petroleum

Key Laboratory of Oil and Gas Safety and Emergency Technology, Ministry of Emergency Management

⁰