Fabrication of hierarchical ZSM-5 zeolite membranes for ultrafiltration

YAO Xun; PENG Li; XU Xiaohan; ZHANG Chun; GU Xuehong

doi:10.11949/j.issn.0438-1157.20170451

您当前的位置：

首页 >

文章列表页 >

Fabrication of hierarchical ZSM-5 zeolite membranes for ultrafiltration

更新时间：2025-12-10

- Fabrication of hierarchical ZSM-5 zeolite membranes for ultrafiltration
- CIESC Journal Issue 11, Pages: 4351-4358(2017)
- 作者机构：
  
  南京工业大学化工学院, 材料化学工程国家重点实验室, 国家特种分离膜工程技术研究中心,江苏,南京,210009
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20170451
  CLC： Q028.8
- Online First：05 November 2017，
  
  Published：05 November 2017
- 稿件说明：
移动端阅览
YAO Xun, PENG Li, XU Xiaohan, et al. Fabrication of hierarchical ZSM-5 zeolite membranes for ultrafiltration[J]. CIESC Journal, 2017, (11): 4351-4358.
DOI：

YAO Xun, PENG Li, XU Xiaohan, et al. Fabrication of hierarchical ZSM-5 zeolite membranes for ultrafiltration[J]. CIESC Journal, 2017, (11): 4351-4358. DOI： 10.11949/j.issn.0438-1157.20170451.

摘要

利用二次生长法，以十六烷基三甲基溴化铵（CTAB）为结构导向剂，一步水热合成了多级孔道ZSM-5分子筛膜。结果表明，CTAB球形胶束与分子筛颗粒自组装形成了介孔结构，同时，CTAB胶束及疏水长链抑制了晶体的长大。通过调整CTAB/SiO2摩尔比、合成温度及晶化时间等制膜条件，改变分子筛膜的晶体颗粒尺寸及膜层交联度，实现了分子筛膜介孔结构的有效调节，其孔径范围7~30 nm。在CTAB/SiO2摩尔比为0.05、合成温度180℃、时间20 h下，多级孔分子筛膜纯水渗透通量达到138 kg·m-2·h-1·MPa-1，截留分子量28500，对应平均孔径7.39 nm，达到小孔径超滤的标准。

Abstract

Hierarchical ZSM-5 zeolite membranes were synthesized through secondary growth method in the presence of small amount of cetyltrimethylammonium bromide (CTAB). The results show that CTAB spherical micelles and molecular sieve particles self-assembled to form ordered mesoporous structure. At the same time

the presence of CTAB micelles and hydrophobic long chains suppresses the growth of crystals. By adjusting the CTAB/SiO2 molar ratio

synthesis temperature or crystallization time

the crystal grain size and the crosslinking degree of the zeolite membranes were changed remarkably to realize the simple and effective regulation of the average pore size

ranging from 7 to 30 nm. Under the synthesis at 180℃ for 20 h and the CTAB/SiO2 molar ratio about 0.05

the obtained zeolite membrane exhibited a high water permeability of 138 kg·m-2·h-1·MPa-1

and a molecular weight cut-off(MWCO) of 28500

corresponding to the average pore size of 7.39 nm

achieving the standard of small aperture ultrafiltration.

关键词

Keywords

references

Views

253

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Preparation and performance of high-flux polysulfone ultrafiltration membrane by in-situ synthesis

Ultrafiltration membrane cleaning technology and mechanism based on seawater desalination pilot equipment

Progress research on development of membrane technology and materials for health industry

Preparation and properties of temperature-responsive PVDF/PGS-g-PNIPAM nanocomposite ultrafiltration membrane

Application of porous ceramic membranes for separation and purification of carbon quantum dots

Related Author

Kaizhen WANG

Shuhao WANG

Yunhao LI

Yong ZHOU

Congjie GAO

Xiaohan SUN

Xingtao YANG

Xiaodong ZHANG

Related Institution

College of Chemical Engineering, Zhejiang University of Technology

Center for Membrane Separation and Water Science & Technology, Zhejiang University of Technology

College of Environment and Safety Engineering, Qingdao University of Science & Technology

Qingdao Institute of Bioenergy and Bioprocess Technology, Chinese Academy of Sciences

Qingdao Befesa Seawater Desalination Co. Ltd.

⁰