SO<sub>2</sub> corrosion resistance of composite ceramic coating for boiler heating surface

WANG Jinqing; CHI Zuohe; YUAN Yichao; YU Jiahao; ZHANG Guangxue

doi:10.11949/j.issn.0438-1157.20170273

您当前的位置：

首页 >

文章列表页 >

SO₂ corrosion resistance of composite ceramic coating for boiler heating surface

更新时间：2025-12-10

- SO₂ corrosion resistance of composite ceramic coating for boiler heating surface
- CIESC Journal Issue 11, Pages: 4221-4228(2017)
- 作者机构：
  
  1. 中国计量大学计量测试工程学院,浙江,杭州,310018
  2. 上海理工大学上海市动力工程多相流动与传热重点实验室,上海,200093
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20170273
  CLC： K08
- Online First：05 November 2017，
  
  Published：05 November 2017
- 稿件说明：
移动端阅览
WANG Jinqing, CHI Zuohe, YUAN Yichao, et al. SO₂ corrosion resistance of composite ceramic coating for boiler heating surface[J]. CIESC Journal, 2017, (11): 4221-4228. DOI: 10.11949/j.issn.0438-1157.20170273.
DOI：

WANG Jinqing, CHI Zuohe, YUAN Yichao, et al. SO₂ corrosion resistance of composite ceramic coating for boiler heating surface[J]. CIESC Journal, 2017, (11): 4221-4228. DOI: 10.11949/j.issn.0438-1157.20170273. DOI：

摘要

针对燃煤锅炉受热面存在的高温腐蚀问题，采用料浆法在20G钢材表面制备复合陶瓷涂层，烧结后的复合陶瓷涂层表面较为致密，涂层与基材具有良好的结合状态。对喷涂及未喷涂陶瓷涂层钢片在SO2腐蚀气氛环境下的抗高温腐蚀性能进行试验，并采用热分析动力学方法对试验数据进行处理，结果表明，在400~500℃温度范围内，两种试样的腐蚀过程均符合一维扩散反应动力学模式，计算求得喷涂涂层钢片腐蚀反应活化能低于未喷涂涂层钢片，涂层具有较好的抗高温腐蚀性能。对腐蚀试验后试样的形貌、成分和物相分析结果显示，涂层在SO2气氛下腐蚀后，表面生成K2SO4晶粒，但由于涂层较为致密，阻止了S的扩散，内部基本没有检测到K2SO4的存在。

Abstract

To address high-temperature corrosion at heating surface of coal-fired boilers

a composite ceramic coating on surface of 20G steel sheet was prepared by slurry method. After sintering

the composite ceramic coating had a relatively dense surface and good bonding to the substrate. Both uncoated and ceramic-coated steel sheets were studied for high-temperature corrosion resistance in sulfur dioxide (SO2) by thermal kinetic analysis method. The results show that corrosion of the coated and uncoated steel sheets adheres to one dimensional diffusion reaction kinetic model at 400-500℃. Although activation energy of coated steel corrosion was lower than the uncoated one

the coating provided preferable high-temperature corrosion resistance. After exposure to SO2

the appearance

element contents and phase structure of the sheets were characterized. Potassium sulfate (K2SO4) crystal grains were found to form on the coating surface. However

K2SO4 was not detected inside coating because relatively dense coating blocked sulfur diffusion.

关键词

Keywords

references

Views

193

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

In-plant experimental study on desulfurized flue gas corrosion

Kinetic modelling and experimental studies on SO3 generation in flue gas for coal-fired boiler

Characteristics of ash deposit and dew point corrosion in biofuel boiler

Design and analysis of plastic fin-tube heat exchanger for flue gas heat recovery

Corrosion health status assessment method for refining unit pipeline based on GLAE-MLP

Related Author

Peiyuan PAN

Heng CHEN

Jian JIAO

Zhiyuan LIANG

Qinxin ZHAO

XIANG Baixiang

YANG Hairui

LÜ Junfu

Related Institution

Key Laboratory of Thermo-Fluid Science and Engineering of MOE, School of Energy and Power Engineering, Xi’an Jiaotong University, Shaanxi

Department of Thermal Engineering, Tsinghua University

Key Laboratory of Thermo-Fluid Science and Engineering(Ministry of Education), Xi'an Jiaotong University

Key Laboratory of Condition Monitoring and Control for Power Plant Equipment, Ministry of Education, School of Energy, Power and Mechanical Engineering, North China Electric Power University

College of Safety and Ocean Engineering, China University of Petroleum

⁰

SO2 corrosion resistance of composite ceramic coating for boiler heating surface

DOI：10.11949/j.issn.0438-1157.20170273

摘要

Abstract

关键词

Keywords

references

SO₂ corrosion resistance of composite ceramic coating for boiler heating surface