New approach to prepare high purity and superfine alumina powder

更新时间：2025-12-10

- New approach to prepare high purity and superfine alumina powder
- CIESC Journal Issue 9, Pages: 3616-3622(2017)
- 作者机构：
  
  1. 青岛科技大学化工学院,山东,青岛,266042
  2. 中国科学院大连化学物理研究所,辽宁,大连,116023
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20170176
  CLC： Q133.1
- Online First：05 September 2017，
  
  Published：05 September 2017
- 稿件说明：
移动端阅览
NIE Yujuan, WANG Erdong, WANG Xuyun. New approach to prepare high purity and superfine alumina powder[J]. CIESC Journal, 2017, (9): 3616-3622.
DOI：

NIE Yujuan, WANG Erdong, WANG Xuyun. New approach to prepare high purity and superfine alumina powder[J]. CIESC Journal, 2017, (9): 3616-3622. DOI： 10.11949/j.issn.0438-1157.20170176.

摘要

以99.99% 高纯铝板为阳极原料，采用电化学方法制备氧化铝前体氢氧化铝，讨论分析了氢氧化铝的焙烧温度、保温时间对制备高纯超细氧化铝的影响，考察了不同电流密度放电对氧化铝形貌和粒度的影响。结果表明：在70 mA·cm-2的较高电流密度下铝/空气电池放电过程可得到平均粒度为268 nm的氢氧化铝；制备的氢氧化铝经洗涤，在1400℃焙烧，保温3 h，可得到平均粒度为200 nm，形貌为近似球状的99.99% 的超细氧化铝粉体；而低电流密度所得氧化铝颗粒团聚严重。主要原因是高电流密度使放电过程中产生的氢氧化铝晶体的介稳区宽度变窄所致。

Abstract

99.99% high-purity aluminum is introduced as anode material to obtain aluminum hydroxide

the precursor of alumina

by an electrochemical method. The influence of calcination temperature and holding time on preparing high purity and superfine alumina is discussed. And effects on morphology and size of alumina at different current densities are studied. Experimental results show that the average size of 268 nm aluminum hydroxide can be obtained at 70 mA·cm-2

a relative high current density in aluminum/air batteries. After washing aluminum hydroxide and roasting at 1400℃

holding 3 h

the average size of 200 nm and near-spherical alumina powder is received. However

alumina particles agglomerate seriously at low current densities

which is mainly caused by narrowing of metastable zone width at high current densities.

关键词

Keywords

references

Views

366

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Design and study on dual-layer rotor cage for ultrafine powder classification

The microscopic mechanism on MPP inhibiting explosion of Al-Mg alloy powder

Synthesis and slurry control of manganese oxide powder for direct ink writing electrode

Effect of Co on the pre-reduction process of WO3-Co3O4 and carbonization performance of its product

Experimental study on inhibition of methane explosion by polydopamine coated mixed powder

Related Author

YU Yuan

LI Xingshuai

LI Quan

WANG Shaorui

WANG Hu

LI Chao

LI Zhenbao

HE Hanbing

Related Institution

College of Mechanical and Electrical Engineering, Beijing University of Chemical Technology

School of Electronic Information Engineering, Lanzhou Institute of Technology

College of Petrochemical Technology, Lanzhou University of Technology

School of Materials Science and Engineering, Central South University

School of Metallurgy and Environment, Central South University

⁰