Corrosion behavior of In625 alloy and 316L stainless steel in NaCl-CaCl<sub>2</sub>-MgCl<sub>2</sub> ternary eutectic molten salt

LIU Bo; WEI Xiaolan; WANG Weilong; SONG Ming; DING Jing

doi:10.11949/j.issn.0438-1157.20170131

您当前的位置：

首页 >

文章列表页 >

Corrosion behavior of In625 alloy and 316L stainless steel in NaCl-CaCl₂-MgCl₂ ternary eutectic molten salt

更新时间：2025-12-10

- Corrosion behavior of In625 alloy and 316L stainless steel in NaCl-CaCl₂-MgCl₂ ternary eutectic molten salt
- CIESC Journal Issue 8, Pages: 3202-3210(2017)
- 作者机构：
  
  1. 华南理工大学化学与化工学院,广东,广州,510640
  2. 中山大学工学院,广东,广州,510006
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20170131
  CLC： Q050.9+1
- Online First：05 August 2017，
  
  Published：05 August 2017
- 稿件说明：
移动端阅览
LIU Bo, WEI Xiaolan, WANG Weilong, et al. Corrosion behavior of In625 alloy and 316L stainless steel in NaCl-CaCl₂-MgCl₂ ternary eutectic molten salt[J]. CIESC Journal, 2017, (8): 3202-3210. DOI: 10.11949/j.issn.0438-1157.20170131.
DOI：

LIU Bo, WEI Xiaolan, WANG Weilong, et al. Corrosion behavior of In625 alloy and 316L stainless steel in NaCl-CaCl₂-MgCl₂ ternary eutectic molten salt[J]. CIESC Journal, 2017, (8): 3202-3210. DOI: 10.11949/j.issn.0438-1157.20170131. DOI：

摘要

为了解Cr元素对含铬合金在三元NaCl-CaCl2-MgCl2氯化物熔盐中腐蚀的影响机理，选择两种含铬合金镍基Inconel 625（In625）和铁基奥氏体316L型不锈钢，采用全浸没法分别研究它们在500~700℃下于三元氯化物NaCl-CaCl2-MgCl2低共熔盐中的腐蚀行为，以及接触空气程度与温度对腐蚀的影响。绘制了In625合金和316L不锈钢在熔盐中600℃下浸没21 d的腐蚀速率曲线。采用XRD（X射线衍射仪）、SEM（扫描电镜）和EDX（X射线能谱仪）对In625合金和316L不锈钢的腐蚀产物和截面形貌进行分析。结果表明：两种金属的腐蚀程度随着接触空气的量和腐蚀温度的增加而加大；600℃下腐蚀21 d后金属表面和截面的元素及形貌分析表明，Cr具有优先脱溶性；600℃下腐蚀21 d后在合金截面形成了贫Cr区域；致密的腐蚀层可以降低金属的腐蚀速率；在NaCl-CaCl2-MgCl2三元氯化物熔盐中镍基合金In625拥有比奥氏体不锈钢更好的耐腐蚀性能。

Abstract

Isothermal corrosion of 316L stainless steel and nickel based Inconel 625 alloy was evaluated by total immersion in eutectic NaCl-CaCl2-MgCl2 molten salt at 500-700℃.The effect of chromium (Cr)

air contact

and temperature on corrosion was studied. Corrosion dynamic and velocity curves of 316L and Inconel 625 alloy at 600℃ molten salt for 21 d were obtained. X-Ray diffraction (XRD)

scanning electron microscope (SEM) and X-ray energy spectrometer (EDX) were used to analyze corrosion products and cross section morphologies. The results show that mass loss of the steel and alloy increases with the increase of air contact and corrosion temperature. Element and morphology of metal surface and cross section after 21 d immersion at 600℃ indicate that Cr has a preferential solubility to other elements

which Cr depletion region was observed across cross-section. The dense layer of corrosion products can reduce corrosion rate. Inconel 625 exhibits better corrosion resistance than austenitic stainless steel in NaCl-CaCl2-MgCl2 eutectic molten salt.

关键词

Keywords

references

Views

273

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Corrosion health status assessment method for refining unit pipeline based on GLAE-MLP

Study on the protective behavior of heavy-duty anti-corrosive coatings/TA2 in simulated ultra-deep sea 10000 meters environment

Research progress on bio-based anti-corrosion coating

Research on fretting corrosion damage and life prediction of 316L stainless steel based on experiments and finite element analysis

Research progress on mechanism and control strategies of corrosion and plugging in generator stator copper conductors

Related Author

HU Jinqiu

MA Mingjun

ZHANG Laibin

DONG Jiayan

ZHANG Heqi

LU Weizhong

LI Guohua

WANG Hongfei

Related Institution

College of Safety and Ocean Engineering, China University of Petroleum

Key Laboratory of Oil and Gas Safety and Emergency Technology, Ministry of Emergency Management

Key Laboratory of Oil and Gas Production Equipment Quality Inspection and Health Diagnosis, State Administration for Market Regulation

College of Chemical Engineering, Zhejiang University of Technology

State Key Laboratory of Marine Critical Materials, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences

⁰

Corrosion behavior of In625 alloy and 316L stainless steel in NaCl-CaCl2-MgCl2 ternary eutectic molten salt

DOI：10.11949/j.issn.0438-1157.20170131

摘要

Abstract

关键词

Keywords

references

Corrosion behavior of In625 alloy and 316L stainless steel in NaCl-CaCl₂-MgCl₂ ternary eutectic molten salt