Preparation and performance evaluation of Ni<sub>2</sub>P/SiO<sub>2</sub> catalysts for acetic acid hydrogenation to produce ethanol

REN Jie; HU Wangwei; YUAN Haikuan; SHEN Lian

doi:10.11949/j.issn.0438-1157.20170109

您当前的位置：

首页 >

文章列表页 >

Preparation and performance evaluation of Ni₂P/SiO₂ catalysts for acetic acid hydrogenation to produce ethanol

更新时间：2025-12-10

- Preparation and performance evaluation of Ni₂P/SiO₂ catalysts for acetic acid hydrogenation to produce ethanol
- CIESC Journal Issue 8, Pages: 3082-3088(2017)
- 作者机构：
  
  浙江工业大学化工学院,浙江,杭州,310014
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20170109
  CLC： Q032.41
- Online First：05 August 2017，
  
  Published：05 August 2017
- 稿件说明：
移动端阅览
REN Jie, HU Wangwei, YUAN Haikuan, et al. Preparation and performance evaluation of Ni₂P/SiO₂ catalysts for acetic acid hydrogenation to produce ethanol[J]. CIESC Journal, 2017, (8): 3082-3088. DOI: 10.11949/j.issn.0438-1157.20170109.
DOI：

REN Jie, HU Wangwei, YUAN Haikuan, et al. Preparation and performance evaluation of Ni₂P/SiO₂ catalysts for acetic acid hydrogenation to produce ethanol[J]. CIESC Journal, 2017, (8): 3082-3088. DOI: 10.11949/j.issn.0438-1157.20170109. DOI：

摘要

通过等体积浸渍和N2气流中热处理过程制备了系列氧化硅负载过渡金属磷化物催化剂，经乙酸加氢制乙醇反应实验和动力学分析评价催化剂性能。研究结果表明，随着反应温度从280℃升高到340℃，乙酸转化率和乙醇选择性均逐渐提高。随着催化剂制备的P/Ni摩尔比从2：1增大到4：1，催化剂活性和乙醇选择性均先增大后减小，P/Ni摩尔比为3：1催化剂性能较佳。250℃热处理制备催化剂的催化性能优于200℃及300℃。Ni2P/SiO2催化剂活性和乙醇选择性均高于Co2P/SiO2催化剂。用次磷酸钠作为磷补充源制备催化剂的性能优于次磷酸钾。采用较佳条件下制备的Ni2P/SiO2催化剂，在温度340℃、压力2.0 MPa、氢酸进料量比10：1、质量空速0.4 h-1条件下进行乙酸加氢反应，乙酸转化率为100%，乙醇选择性达到74.56%，并且适当升高反应温度会进一步提高乙醇选择性。

Abstract

A series of silica supported transition metal phosphide catalysts were prepared through isovolumetric impregnation and heat treatment under N2 protection. Their catalytic performances were evaluated by ethanol yield and reaction kinetics of acetic acid hydrogenation. Results showed that both conversion of acetic acid and ethanol selectivity were gradually increased with reaction temperature increasing from 280℃ to 340℃. With P/Ni molar ratio for catalyst preparation was increased from 2:1 to 4:1

the obtained catalysts exhibited first increase and then decrease in activity and selectivity with optimal performance at P/Ni=3:1. The catalyst prepared by heat treatment at 250℃ had better catalytic performances than those at 200℃ and 300℃. The activity and ethanol selectivity of Ni2P/SiO2 catalysts were higher than that of Co2P/SiO2 catalysts. Catalysts using sodium hypophosphite as phosphorus supplement had better performance than those of potassium hypophosphite. Under temperature at 340℃

pressure at 2.0 MPa

molar ratio of hydrogen to acetic acid at 10:1

and WHSV at 0.4 h-1

acetic acid hydrogenation over Ni2P/SiO2 prepared in better conditions showed 100% conversion of acetic acid and 74.56% selectivity of ethanol. In addition

ethanol selectivity could be further improved by appropriate increase of reaction temperature.

关键词

Keywords

references

Views

162

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

High-performance electrocatalytic semi-hydrogenation of acetylene to ethylene via MOF derived Cu/N-C catalyst

Effect of ammonia evaporation time on the reaction performance of hydrogenation of dimethyl oxalate to ethylene glycol over Cu/SiO2

Integrated production of 2-methyltetrahydrofuran through hydrogenation and dehydration of ethyl levulinate

Synthesis of a high-efficacy medium-entropy alloy catalyst via the recycling of spent batteries and its subsequent performance evaluation

Study on the catalytic hydrogenation of maleic anhydride by mesoporous carbon-supported Ni catalyst

Related Author

DU Zifu

XIE Xiaomi

ZHANG Mimi

LI Zuosi

WU Deyin

ZHOU Jianzhang

LI Rui

JIAN Xuan

Related Institution

Shaanxi Key Laboratory of Chemical Reaction Engineering, School of Chemistry and Chemical Engineering, Yan’an University, Yan’an

National Key Laboratory of Surface-Interface Chemistry, School of Chemistry and Chemical Engineering, Xiamen University

Key Laboratory of Atmospheric Complex Pollution Control and Synergistic Carbon Reduction of Shanxi Province, School of Environmental Science and Engineering, Taiyuan University of Technology

School of Chemistry and Chemical Engineering, Guangxi University

Guangxi Huayi Energy Chemical Co., Ltd.

⁰

Preparation and performance evaluation of Ni2P/SiO2 catalysts for acetic acid hydrogenation to produce ethanol

DOI：10.11949/j.issn.0438-1157.20170109

摘要

Abstract

关键词

Keywords

references

Preparation and performance evaluation of Ni₂P/SiO₂ catalysts for acetic acid hydrogenation to produce ethanol