Preparation of platanus leaf-based activated carbon and its application to supercapacitors

ZHOU Wangfan; CHEN Xin; CAO Hongliang; WANG Haiyan; ZHAO Yangzhi; JIA Xiaobo; WANG Man

doi:10.11949/j.issn.0438-1157.20170096

您当前的位置：

首页 >

文章列表页 >

Preparation of platanus leaf-based activated carbon and its application to supercapacitors

更新时间：2025-12-10

- Preparation of platanus leaf-based activated carbon and its application to supercapacitors
- CIESC Journal Issue 7, Pages: 2918-2924(2017)
- 作者机构：
  
  1. 华东理工大学材料科学与工程学院, 超细材料制备与应用教育部重点实验室, 上海市先进聚合物材料重点实验室,上海,200237
  2. 中国科学院上海微系统与信息技术研究所信息功能材料国家重点实验室,上海,200050
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20170096
  CLC： B32TB34
- Online First：05 July 2017，
  
  Published：05 July 2017
- 稿件说明：
移动端阅览
ZHOU Wangfan, CHEN Xin, CAO Hongliang, et al. Preparation of platanus leaf-based activated carbon and its application to supercapacitors[J]. CIESC Journal, 2017, (7): 2918-2924.
DOI：

ZHOU Wangfan, CHEN Xin, CAO Hongliang, et al. Preparation of platanus leaf-based activated carbon and its application to supercapacitors[J]. CIESC Journal, 2017, (7): 2918-2924. DOI： 10.11949/j.issn.0438-1157.20170096.

摘要

以生物质法国梧桐枯叶为原料，将炭化的枯叶通过KOH化学活化处理，制备法国梧桐枯叶基活性炭（PLAC）。采用扫描电子显微镜（SEM）、X射线能量色散谱（EDS）、X射线光电子能谱（XPS）、傅里叶变换红外光谱（FTIR）、氮气吸脱附对法国梧桐基枯叶活性炭的形貌、成分、比表面积、孔径分布等进行表征；运用三电极电化学体系，通过循环伏安，恒流充放电，循环稳定性测试，电化学阻抗谱分析法国梧桐枯叶基活性炭的超级电容器电极性能。结果显示，在800℃下碳化，通过KOH活化处理的法国梧桐基活性炭制备的电极，在1 A·g-1电流密度下，比电容达到266 F·g-1。电极在5 A·g-1的电流密度下循环2000次后，比容量仍保留 97.0%，展示出良好的电极性能。

Abstract

Platanus leaf-based activated carbon (PLAC) was synthesized through high temperature carbonization and KOH chemical activation

using dry platanus leaves as raw materials. Scanning electron microscopy (SEM)

energy dispersive spectrometry (EDS)

X-ray photoelectron spectroscopy (XPS)

Fourier transform infrared spectroscopy (FTIR) and nitrogen adsorption-desorption techniques were used to characterize the morphology

composition

specific surface area and pore size distribution of the PLAC. The cyclic voltammetric (CV)

galvanostatic charge/discharge (GCD) and electrochemical impedance spectroscopy (EIS) characterizations were performed with a three electrode electrochemical system

to study the supercapacitor electrode performance of the PLAC. The result shows that the PLAC electrode obtained under 800℃ carbonization and KOH chemical activation has specific capacitance of 266 F·g-1 at 1 A·g-1

and it can remain 97.0% of the initial capacitance after 2000 cycles at 5 A·g-1

demonstrating good electrode properties.

关键词

Keywords

references

Views

391

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

An environmentally friendly activated carbon supercapacitor electrode material preparation with expired sliced bread

Preparation of cellulose-derived biomass porous carbon and its supercapacitor performance

Synthesis of nitrogen doped hierarchically porous carbon nanosheets for supercapacitor by mixed salt template

Electrochemical properties of supercapacitor electrode materials made from needle coke

Preparation of coral-like nitrogen-doped porous carbons and its supercapacitive properties

Related Author

Jie XU

Xin CHEN

Lingling WANG

Jianxin CHEN

Ruijie ZHU

Nan SHENG

Chunyu ZHU

Zhonghao RAO

Related Institution

Key Laboratory for Ultrafine Materials of Ministry of Education, Shanghai Key Laboratory of Advanced Polymeric Materials, School of Materials Science and Engineering, East China University of Science and Technology

School of Low-carbon Energy and Power Engineering, China University of Mining and Technology

Division of Applied Chemistry, Faculty of Engineering, Hokkaido University, Sapporo

School of Energy and Environment, Hebei University of Technology

School of Chemistry and Chemical Engineering, Anhui University of Technology, Maanshan

⁰