Separation of n-butyl acetate from aqueous solution using PDMS membrane filled with hydrophobic SiO<sub>2</sub>

MU Chunxia; ZHANG Shiyu; ZOU Yun; LIU Xiangjun; DONG Yanbo; CUI Xuemin; TONG Zhangfa

doi:10.11949/j.issn.0438-1157.20161508

您当前的位置：

首页 >

文章列表页 >

Separation of n-butyl acetate from aqueous solution using PDMS membrane filled with hydrophobic SiO₂

更新时间：2025-12-10

- Separation of n-butyl acetate from aqueous solution using PDMS membrane filled with hydrophobic SiO₂
- CIESC Journal Issue 6, Pages: 2407-2414(2017)
- 作者机构：
  
  广西大学化学化工学院, 广西石化资源加工及过程强化技术重点实验室,广西,南宁,530004
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20161508
  CLC： Q028.8
- Online First：05 June 2017，
  
  Published：05 June 2017
- 稿件说明：
移动端阅览
MU Chunxia, ZHANG Shiyu, ZOU Yun, et al. Separation of n-butyl acetate from aqueous solution using PDMS membrane filled with hydrophobic SiO₂[J]. CIESC Journal, 2017, (6): 2407-2414. DOI: 10.11949/j.issn.0438-1157.20161508.
DOI：

MU Chunxia, ZHANG Shiyu, ZOU Yun, et al. Separation of n-butyl acetate from aqueous solution using PDMS membrane filled with hydrophobic SiO₂[J]. CIESC Journal, 2017, (6): 2407-2414. DOI: 10.11949/j.issn.0438-1157.20161508. DOI：

摘要

以聚偏氟乙烯（PVDF）为支撑层，选用疏水性纳米SiO2粉体作为改性剂，制备出聚二甲基硅氧烷（PDMS）复合膜材料，并用于乙酸正丁酯/水溶液的渗透汽化分离。采用SEM、FTIR、XRD、拉伸实验、接触角及正电子湮没寿命谱测定等对膜材料物理化学性能进行了表征，考察了膜材料的溶胀行为及渗透汽化性能。结果表明，SiO2在PDMS膜中分散均匀，且没有发生化学作用，并提高了膜材料的机械强度和疏水性。随着SiO2添加量增加，膜在乙酸正丁酯溶液中的溶胀度先升后降，渗透通量呈下降趋势，而分离因子先增大后减小。当SiO2添加量为4%（质量）时，随进料浓度的增加，渗透通量增大，分离因子先增大后减小；随着温度升高，渗透通量增大，分离因子减小；渗透通量和分离因子最大值分别为240 g·m-2·h-1和542。

Abstract

The modified polydimethysiloxane (PDMS) hybrid membranes with hydrophobic nano SiO2 as filler and using PVDF film as support layer were prepared for pervaporation of n-butyl acetate from aqueous solution. The physciochemical properties of membranes were characterized by SEM

FTIR

XRD

tensile testing

contact angle and positron annihilation lifetime spectroscopy(PALS). The effects of the loading of SiO2

feed concentration

feed temperature on swelling behavior and pervaporation performance were studied. The results indicated that SiO2 particles dispersed uniformly in the membrane material and no chemical change occurred between SiO2 and PDMS polymer chain. The mechanical strength and hydrophobic properties of the filled film were obviously improved by incorporation of SiO2. With the increase of SiO2 content

the adsorption capacity of n-butyl acetate increased and then decreased

while the permeation flux decreased and the separation factor increased initially and then decreased. When SiO2 content was 4%(mass)

the permeation flux increased while the separation factor increased initially and then decreased with the rise of the feed concentration. The permeation flux increased with increase of the feed temperature

however

the separation factor decreased. The maximum values of the permeation flux and the separation factor were 240 g·m-2·h-1 and 542 respectively.

关键词

Keywords

references

Views

350

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Preparation of PDMS/ZSM-5 membranes and pervaporation separation of n-butyl acetate and ethyl acetate from aqueous media

Preparation and pervaporation performance of PDMS/rutin-modified β-CD-MOFs mixed matrix membranes for 2-phenylethanol separation

Combining paraffin@silica nanocapsules with carbon fiber to develop a phase change thermal interface material for efficient heat dissipation

Enhancing ethanol production efficiency by ZIF-L/PDMS mixed matrix membrane via vapor permeation-fermentation coupling process

Preparation of ZSM-5 zeolite membrane and its application in desalination

Related Author

Tingting HU

Luoyi LU

Wei WANG

Yun ZOU

Zhangfa TONG

Yanqing LIU

GUANG Yisheng

ZHANG Xinru

Related Institution

Guangxi Key Laboratory of Petrochemical Resource Processing and Process Intensification Technology, School of Chemistry and Chemical Engineering, Guangxi University

Shanxi Key Laboratory of Gas Energy Efficient and Clean Utilization

College of Chemistry and Chemical Engineering, Taiyuan University of Technology

South China University of Technology-Zhuhai Institute of Modern Industrial Innovation

Guangdong Engineering Technology Research Center of Efficient Heat Storage and Application, South China University of Technology

⁰

Separation of n-butyl acetate from aqueous solution using PDMS membrane filled with hydrophobic SiO2

DOI：10.11949/j.issn.0438-1157.20161508

摘要

Abstract

关键词

Keywords

references

Separation of n-butyl acetate from aqueous solution using PDMS membrane filled with hydrophobic SiO₂