Effect of pre-contact temperature on performance of DQC spherical catalyst in propylene polymerization

更新时间：2025-12-10

- Effect of pre-contact temperature on performance of DQC spherical catalyst in propylene polymerization
- CIESC Journal Issue 4, Pages: 1434-1441(2017)
- 作者机构：
  
  中国石油化工股份有限公司北京化工研究院,北京,100013
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20161119
  CLC： Q325.14
- Online First：05 April 2017，
  
  Published：05 April 2017
- 稿件说明：
移动端阅览
ZHANG Tianyi, XIA Xianzhi, LIU Yuexiang. Effect of pre-contact temperature on performance of DQC spherical catalyst in propylene polymerization[J]. CIESC Journal, 2017, (4): 1434-1441.
DOI：

ZHANG Tianyi, XIA Xianzhi, LIU Yuexiang. Effect of pre-contact temperature on performance of DQC spherical catalyst in propylene polymerization[J]. CIESC Journal, 2017, (4): 1434-1441. DOI： 10.11949/j.issn.0438-1157.20161119.

摘要

使用甲基环己基二甲氧基硅烷（C-donor）作为外给电子体，对聚丙烯DQC球形催化剂进行了预接触温度液相本体聚合研究。实验结果表明，预接触温度升高，DQC球形催化剂的聚合活性降低，得到聚合物的等规指数升高，熔融指数下降，得到的聚合物细粉含量增加。GPC测试结果表明，预接触温度升高，聚合物的分子量分布变宽，数均分子量和重均分子量降低。DSC测试结果表明，聚合物的熔融温度、熔融焓和结晶焓数值均有不同程度的提高，聚合物的结晶度提高。13C NMR测试结果表明，预接触温度升高，得到的聚合物全同立构三单元组mm序列结构和五单元组mmmm序列结构含量均增加。

Abstract

The pre-contact temperature of DQC catalyst system on liquid bulk polymerization of propylene was studied using cyclohexyl methyl dimethoxy silane (C-donor) as external donor. The results indicated that increase of pre-contact temperature caused decrease of polymerization activity of DQC catalyst

which yielded polymers with decreased melt index but increased isotactic index and fine powder content. Gel permeation chromatography (GPC) results showed that increase of pre-contact temperature broadened molecular weight distributions and decreased both number and weight average molecular weights. Differential scanning calorimetry (DSC) results exhibited that melting temperature

melting enthalpy

crystallization enthalpy

and crystallinity of polypropylenes increased to various degrees. 13C NMR results showed an increase of stereoregular sequences of triad mm and pentad mmmm with increase of pre-contact temperature.

关键词

Keywords

references

Views

282

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Synergistic metal-zeolite catalysis for conversion of polypropylene into aromatics

Crystallization behavior and properties of polypropylene and its copolymers modified with sorbitol nucleating agents

Performance of MgAl layered double hydroxides light stabilizer assembled via intermolecular forces

Nucleation effect of carboxylic acid modified alumina nanoparticles on polypropylene

Study on ammonium polyphosphate coated with melamine-epoxy resin and its application in PP

Related Author

WANG Wenjie

CHEN Wenyao

ZHOU Xinggui

ZHANG Jing

QIAN Huihui

DUAN Xuezhi

PAN Pengju

ZHENG Ying

Related Institution

State Key Laboratory of Chemical Engineering and Low-carbon Technology, School of Chemical Engineering, East China University of Science and Technology

State Key Laboratory of Chemical Engineering, College of Chemical and Biological Engineering, Zhejiang University

Polytechnic Institute, Zhejiang University

Institute of Zhejiang University-Quzhou

State Key Laboratory of Chemical Resource Engineering, Beijing Engineering Center for Hierarchical Catalysts, Beijing University of Chemical Technology

⁰