Electrochemical reaction and surface tension change of Wood liquid alloy in NaOH solution

ZHANG Guodi; LI Fuxiang; CHEN Jianhong; CAO Rui; LIN Qiaoli

doi:10.11949/j.issn.0438-1157.20160946

您当前的位置：

首页 >

文章列表页 >

Electrochemical reaction and surface tension change of Wood liquid alloy in NaOH solution

更新时间：2025-12-10

- Electrochemical reaction and surface tension change of Wood liquid alloy in NaOH solution
- CIESC Journal Issue 3, Pages: 1122-1128(2017)
- 作者机构：
  
  兰州理工大学材料科学与工程学院, 省部共建有色金属先进加工与再利用国家重点实验室,甘肃,兰州,730050
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20160946
  CLC： 646
- Online First：05 March 2017，
  
  Published：05 March 2017
- 稿件说明：
移动端阅览
ZHANG Guodi, LI Fuxiang, CHEN Jianhong, et al. Electrochemical reaction and surface tension change of Wood liquid alloy in NaOH solution[J]. CIESC Journal, 2017, (3): 1122-1128.
DOI：

ZHANG Guodi, LI Fuxiang, CHEN Jianhong, et al. Electrochemical reaction and surface tension change of Wood liquid alloy in NaOH solution[J]. CIESC Journal, 2017, (3): 1122-1128. DOI： 10.11949/j.issn.0438-1157.20160946.

摘要

通过改变液体金属在NaOH溶液中所处的环境介质，利用石墨电极对其施加电场，研究了液态金属的表面张力、界面电化学反应、氧化膜的产生、溶液中电润湿等动态过程。实验发现Wood合金液滴在阳极发生电化学反应产生的氧化膜会迅速减小表面张力并发生铺展，在阴极发生还原反应会使带氧化膜的金属在3 s内恢复到原状，电毛细作用力使氧化膜破裂，各氧化物与NaOH反应产生Sn（OH）62-、SnO32-、SnO22-、PbO32-、Cd（OH）42-使溶液的颜色发生改变，溶液中生成Bi2O3-Bi（OH）3白色共聚物。薄膜电介质层润湿和溶液中电润湿机理在本质上相同，表面张力随着电压的增大而减小并发生明显的电润湿铺展过程，但由于金属液滴通过电化学反应所能吸附的OH-数量有限，润湿角存在饱和性。

Abstract

By variation of liquid Wood metal's environment in NaOH solution and application of electric field with graphite electrode

surface tension of the liquid metal

interfacial electrochemical reaction

generation of oxidation film

and other dynamic processes were studied. The results showed that thin oxidation film on the surface of Wood alloy droplets which was formed by anodic oxidation reaction quickly reduced surface tension of Wood alloy and the oxidation film on surface of liquid alloy droplets would return to neutral state by cathodic reduction reaction within 3 seconds. The electrical capillary force broke the oxide film so that metal oxides reacted with NaOH to generate ions of Sn(OH)62-、SnO32-、SnO22-、PbO32-、Cd(OH)42- which altered solution colors with a white precipitate of Bi2O3-Bi(OH)3 copolymer. The dielectric wetting and solution electrowetting on thin film essentially had the same mechanism. With the increase of voltage

the surface tension was decreased and electrowetting spreading process was occurred obviously

but the wetting angle exhibited saturation as a result of limited number of OH- ions adsorbed on alloy droplets by electrochemical reactions.

关键词

Keywords

references

Views

187

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Electrochemical behavior and copper electrodeposition mechanism of Cu-Al bimetallic composite ionic liquid

Advances in the synthesis of propylene oxide via propylene epoxidation

Research on application of alloy catalysts in electrochemical ammonia synthesis

Mechanism and research progress of transition metal-based materials in electrocatalytic HMF oxidation reaction

Optimized preparation of carbon black/PTFE composite-modified graphite felt cathode and the mechanism on high-efficiency electrochemical production of H2O2

Related Author

Ping OUYANG

Rui ZHANG

Jian ZHOU

Haiyan LIU

Zhichang LIU

Chunming XU

Xianghai MENG

WANG Zhen

Related Institution

State Key Laboratory of Heavy Oil Processing, China University of Petroleum

Lanzhou Petrochemical Research Center, Petrochemical Research Institute, PetroChina

National Institute of Clean-and-Low-Carbon Energy, China Energy Investment

State Key Laboratory of Chemical Engineering and Low-carbon Technology, School of Chemical Engineering and Technology, Tianjin University

School of Civil Engineering, Yantai University

⁰