Preparation and dehumidification properties of sodium alginate-cellulose acetate composite membranes

XU Jingcui; ZHANG Chuanyu; GE Tianshu; DAI Yanjun; WANG Ruzhu

doi:10.11949/j.issn.0438-1157.20160791

您当前的位置：

首页 >

文章列表页 >

Preparation and dehumidification properties of sodium alginate-cellulose acetate composite membranes

更新时间：2025-11-26

- Preparation and dehumidification properties of sodium alginate-cellulose acetate composite membranes
- CIESC Journal Issue 1, Pages: 256-263(2017)
- 作者机构：
  
  上海交通大学制冷与低温工程研究所,上海,200240
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20160791
  CLC： K124
- Online First：05 January 2017，
  
  Published：05 January 2017
- 稿件说明：
移动端阅览
XU Jingcui, ZHANG Chuanyu, GE Tianshu, et al. Preparation and dehumidification properties of sodium alginate-cellulose acetate composite membranes[J]. CIESC Journal, 2017, (1): 256-263.
DOI：

XU Jingcui, ZHANG Chuanyu, GE Tianshu, et al. Preparation and dehumidification properties of sodium alginate-cellulose acetate composite membranes[J]. CIESC Journal, 2017, (1): 256-263. DOI： 10.11949/j.issn.0438-1157.20160791.

摘要

为提高膜式全热交换器的除湿效率，以海藻酸钠为表面活性层，醋酸纤维素膜为支撑层，氯化锂为亲水添加剂制备了一种新型除湿复合膜。测试了复合膜的水蒸气透过量和水溶性，对薄膜结构进行表征及分析了应用复合膜的全热交换器的传质系数。研究结果表明：复合膜的水蒸气透过量随氯化锂含量增加而高达4.42×10-5g·m-2·s-1·Pa-1，是无氯化锂复合膜的1.56倍，商用纸膜的2.63倍。表面活性层水溶性介于18.29%~28.55%之间，具有一定的防水耐水性。热重曲线表明通入55℃干燥空气复合膜可实现再生，红外光谱图显示出海藻酸钠为复合膜引进大量亲水性羟基。最后，将复合膜应用到全热交换器中，并与商用纸膜换热器在传质系数上进行了分析比较。

Abstract

In order to improve dehumidification efficiencies of membrane-based energy recovery ventilator(ERV)

composite membranes based on cellulose acetate

sodium alginate and lithium chloride(LiCl) were fabricated.Cellulose acetate was adopted as supporting constructions and sodium alginate and LiCl were the corresponding active layer and hydrophilic additive.Then their key characteristics were tested and analyzed to investigate practical performance in the ERV.The highest permeance of composite membranes reaches up to 4.42×10-5g·m-2·s-1·Pa-1

which is 1.56 and 2.63 times higher than those of the asymmetric membrane without LiCl and the traditional commercial paper

respectively.Water solubility of the modified active layer ranges from 18.29% to 28.55% for cross-linking improves the waterproofness.Moreover

thermal gravity curves indicate membranes can be regenerated by contacting 55℃ dry air.Fourier transform infrared spectra illustrates that there are plenty of hydrophilic hydroxyl groups on the surface of composite membranes.Finally

the total mass transfer of ERV composed by the composite membranes is analyzed and compared with the commercial one.These properties demonstrate this membrane has great potential to be applied on the ERV.

关键词

Keywords

references

Views

279

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Recent progress in the preparation, structure, and application of thermal insulation materials

Advances in lignin-derived carbon anodes for alkali metal ion batteries

Preparation and application of polyimide-based aerogels

Preparation and performance of para-aramid aerogel powders

Method of determining optimum mass ratio of fatty acids in composite phase change materials for thermal energy storage

Related Author

CHEN Xinyan

CHEN Yiling

PENG Xinbo

HU Jingjie

JIANG Xueliang

YOU Feng

Lei ZHONG

Xueqing QIU

Related Institution

Hubei Key Laboratory of Plasma Chemistry and Advanced Materials, School of Materials Science & Engineering, Wuhan Institute of Technology

School of Chemical Engineering and Light Industry, Guangdong University of Technology

Guangdong Provincial Key Laboratory of Plant Resources Biorefinery

School of Advanced Manufacturing, Guangdong University of Technology

College of Chemical and Biological Engineering, Zhejiang University

⁰