Preparation and characterization of superhydrophobic rutile titania-silica nano complex oxides

HOU Leixin; FANG Li; YAN Guanghong; WANG Yongkang

doi:10.11949/j.issn.0438-1157.20160782

您当前的位置：

首页 >

文章列表页 >

Preparation and characterization of superhydrophobic rutile titania-silica nano complex oxides

更新时间：2025-11-26

- Preparation and characterization of superhydrophobic rutile titania-silica nano complex oxides
- CIESC Journal Issue 1, Pages: 444-451(2017)
- 作者机构：
  
  1. 山西大学化学化工学院,山西,太原,030006
  2. 山西亮龙涂料有限公司,山西,晋中,030600
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20160782
  CLC： 648
- Online First：05 January 2017，
  
  Published：05 January 2017
- 稿件说明：
移动端阅览
HOU Leixin, FANG Li, YAN Guanghong, et al. Preparation and characterization of superhydrophobic rutile titania-silica nano complex oxides[J]. CIESC Journal, 2017, (1): 444-451.
DOI：

HOU Leixin, FANG Li, YAN Guanghong, et al. Preparation and characterization of superhydrophobic rutile titania-silica nano complex oxides[J]. CIESC Journal, 2017, (1): 444-451. DOI： 10.11949/j.issn.0438-1157.20160782.

摘要

以正硅酸乙酯为硅源、钛酸异丙酯为钛源，采用改进的溶胶-凝胶法制备了不同钛硅摩尔比的复合气凝胶，在不同温度下进行煅烧，得到金红石型钛硅（TiO2-SiO2）复合氧化物纳米颗粒，然后通过三甲基氯硅烷（TMCS）改性，制得超疏水金红石型TiO2-SiO2纳米材料。探讨了钛硅摩尔比和煅烧温度对钛硅复合氧化物纳米颗粒晶型的影响，并通过XRD、XPS、BET、SEM和FTIR等手段对产物进行了表征，采用水接触角测试（WCA）对纳米材料改性后的疏水性能进行了表征。结果表明：当钛硅摩尔比为5：1时制得的气凝胶在1100℃煅烧及TMCS改性后，所制备的超疏水金红石型纳米钛硅复合氧化物的比表面积大，疏水性能优异，其比表面积达348 m2·g-1，水接触角达到154.7°，在构建具有纳微分层结构的外墙装饰材料的面漆方面具有潜在的应用前景。

Abstract

Superhydrophobic titania-silica nano complex oxides were synthesized from tetraethylorthosilicate(TEOS) and titanium isopropoxide(TTIP) by an improved sol-gel method followed with high temperature calcination and modification with trimethylchlorosilane(TMCS).The obtained nano complex oxides were characterized by XRD

XPS

BET

SEM and FTIR

and water contact angle.Crystal polymorphism of the nano complex oxides was investigated to explore influence of titania-silica molar ratio as well as calcination temperature on crystal structure.The results showed that rutile crystal structure was achieved at titania-silica molar ratio of 5:1 and calcination temperature of 1100℃.After TCMS surface modification

the superhydrophobic rutile TiO2-SiO2 nano complex oxides exhibited large specific surface area(up to 348 m2·g-1) and excellent hydrophobicity(water contact angle of 154.7°)

which could have a potential application for constructing micro-nano hierarchy-structured top coating of outside wall-decorating materials.

关键词

Keywords

references

Views

300

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Research progress of ionic liquids in preparation of ZnO nanomaterials

Effect of sintering additives on properties of silicon carbide porous ceramics prepared at low temperature

Regulation of support structure by TiO2 deposition and its effect on performance of GO membranes

Synthesis and characterization of copper-based graphene composite catalyst

Effects of sintering parameters on performance of Ni porous wick

Related Author

Tingting CHEN

Jiongting YIN

Yingjie XU

Jian ZHOU

Qian JIANG

Yi YANG

Shasha FENG

Zhaoxiang ZHONG

Related Institution

College of Chemistry and Chemical Engineering, Shaoxing University

National Engineering Research Center for Special Separation Membrane, College of Chemical Engineering, Nanjing Tech University

School of Chemical Engineering, Hebei University of Technology

College of Chemical Engineering, Hunan Collaborative Innovation Center of New Chemical Technologies for Environmental Benignity and Efficient Resource Utilization, Xiangtan University

Institute of Marine Engineering and Thermal Science

⁰