Characteristics of ash deposit and dew point corrosion in biofuel boiler

更新时间：2025-11-26

- Characteristics of ash deposit and dew point corrosion in biofuel boiler
- CIESC Journal Issue 12, Pages: 5237-5243(2016)
- 作者机构：
  
  西安交通大学热流科学与工程教育部重点实验室,陕西,西安,710049
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20160733
  CLC： K16
- Online First：05 December 2016，
  
  Published：05 December 2016
- 稿件说明：
移动端阅览
MA Haidong, WANG Yungang, ZHAO Qinxin, et al. Characteristics of ash deposit and dew point corrosion in biofuel boiler[J]. CIESC Journal, 2016, (12): 5237-5243.
DOI：

MA Haidong, WANG Yungang, ZHAO Qinxin, et al. Characteristics of ash deposit and dew point corrosion in biofuel boiler[J]. CIESC Journal, 2016, (12): 5237-5243. DOI： 10.11949/j.issn.0438-1157.20160733.

摘要

以ND钢为研究对象，选取316 L不锈钢为对比材料，主要研究了65 t·h-1生物质循环流化床锅炉烟气深度冷却条件下的积灰与露点腐蚀耦合特性。对积灰和腐蚀层进行了XRF、XRD、SEM和EDS分析。实验结果表明：实验管件表面沉积物可分为腐蚀层、耦合层和灰沉积层（NH4Cl、SiO2和（NH4）2SO4）。耦合层包含了灰沉积物和金属腐蚀产物，且与灰沉积层黏结紧密易剥落；腐蚀层多为金属的氯化物和氧化物，其厚度随实验进口水温降低而降低，当管壁温低于烟气水露点时，ND钢被腐蚀的程度急剧加重。在实验条件下，ND钢的抗露点腐蚀能力弱于316L不锈钢。

Abstract

The coupling characteristics between ash deposit and dew point corrosion of deep-cooling flue gas on ND steel and 316 L stainless steel(control) was investigated in a 65 t·h-1 circulating fluidized bed biofuel boiler. The ash deposit and corrosion layer were studied by X-ray fluorescence spectroscopy(XRF)

X-ray diffraction(XRD)

scanning electron microscope(SEM) and energy dispersive spectrometer(EDS). Results indicated that the deposits on tube surface could be classified as layers of corrosion

coupling and ash deposit(NH4Cl、SiO2 and(NH4)2SO4). The coupling layer contained ash deposit and metal corrosion by-product

which was prone to spall off because of strong adhesion to the ash deposit layer. The corrosion layer

mainly composed of metal compounds of chlorides and oxides

reduced dramatically in thickness with the decrease of inlet water temperature. The degree of corrosion of ND steel increased sharply when wall temperature was below water dew point of flue gas. ND steel showed corrosion resistance inferior to 316 L stainless steel at experimental conditions.

关键词

Keywords

references

Views

310

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

In-plant experimental study on desulfurized flue gas corrosion

Coupling mechanism of viscose ash deposition and dewpoint corrosion in industrial coal-fired boiler

SO2 corrosion resistance of composite ceramic coating for boiler heating surface

Analysis and formation mechanism of condensates on surface of flue gas cooler of coal-fired power plant

Design and analysis of plastic fin-tube heat exchanger for flue gas heat recovery

Related Author

Peiyuan PAN

Heng CHEN

Jian JIAO

Zhiyuan LIANG

Qinxin ZHAO

CHEN Heng

PAN Peiyuan

ZHAO Qinxin

Related Institution

Key Laboratory of Thermo-Fluid Science and Engineering of MOE, School of Energy and Power Engineering, Xi’an Jiaotong University, Shaanxi

Key Laboratory of Thermo-Fluid Science and Engineering of MOE, School of Energy and Power Engineering, Xi'an Jiaotong University

College of Metrological Technology and Engineering, China Jiliang University

Shanghai Key Laboratory of Multiphase Flow and Heat Transfer in Power Engineering, University of Shanghai for Science and Technology

Key Laboratory of Thermo-Fluid Science and Engineering, Ministry of Education, Xi'an Jiaotong University

⁰