Regulation of structure and catalytic performance of β-zeolite by post treatments

WANG Wennian; YUAN Delin; LI Hao; REN Shenyong; GUO Qiaoxia; SHEN Baojian

doi:10.11949/j.issn.0438-1157.20160340

您当前的位置：

首页 >

文章列表页 >

Regulation of structure and catalytic performance of β-zeolite by post treatments

更新时间：2025-12-10

- Regulation of structure and catalytic performance of β-zeolite by post treatments
- CIESC Journal Issue 8, Pages: 3429-3435(2016)
- 作者机构：
  
  1. 中国石油大学(北京)重质油国家重点实验室, CNPC催化重点实验室,北京,102249
  2. 中国石油大学(北京)理学院,北京,102249
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20160340
  CLC： E624.9
- Online First：05 August 2016，
  
  Published：05 August 2016
- 稿件说明：
移动端阅览
WANG Wennian, YUAN Delin, LI Hao, et al. Regulation of structure and catalytic performance of β-zeolite by post treatments[J]. CIESC Journal, 2016, (8): 3429-3435.
DOI：

WANG Wennian, YUAN Delin, LI Hao, et al. Regulation of structure and catalytic performance of β-zeolite by post treatments[J]. CIESC Journal, 2016, (8): 3429-3435. DOI： 10.11949/j.issn.0438-1157.20160340.

摘要

β沸石作为一种重要的酸催化剂，结构和酸性对其催化性质有重要影响。通过两种不同的联合处理方式（酸-焙烧处理、酸-水热处理）对其结构和性质进行了调变，并对改性所得的β沸石进行了低温氮气物理吸附、X射线电子能谱（XPS）和红外（IR）的表征分析，最后以正辛烷为原料在500℃下进行了催化裂化反应性能评价。研究发现，可通过不同的处理方法调变最终改性沸石的比表面积和两种Lewis酸性（L1445和L1455）。经焙烧和酸处理后所得样品较经水热和酸联合处理所得样品具有更好的正辛烷裂化活性。前者较高的BET比表面积和Lewis酸是其催化裂化活性好的原因。通过这两种不同的改性方式，β沸石的B酸和两种L酸酸量及其织构性质得到调变，从而使最终沸石的催化性能产生差异。

Abstract

β-Zeolite

an important acidic catalyst

its structure and acidity can significantly influence the catalytic activity. Through two combinational treatments of acid-calcination and acid-steaming

the structure and acidity of β-zeolite were tuned. After treatment

the modified β-zeolites was characterized by N2 adsorption and desorption

X-ray photoelectron spectroscopy (XPS)

and infrared spectra (IR). The activity for catalytic cracking of n-octane at 500℃ was evaluated. It showed that BET specific area and Lewis acid sites (L1445 and L1455) were tuned by different treatments. The catalyst by acid-calcination treatment exhibited better activity for catalytic cracking of n-octane than acid-steaming treatment. The higher BET surface area and the Lewis acid sites account for the higher catalytic cracking activity of the catalyst by acid-calcination treatment. The concentrations of Brønsted acid and two types of Lewis acid as well as textural properties were tuned

which lead to the difference in catalytic activity between the original and final β-zeolites.

关键词

Keywords

references

Views

210

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Brönsted equation kinetic modeling for quantitative relationship between activity and acidity strength distribution in oligomerization and aromatization of ethylene over ZSM-5 catalyst

Study on formaldehyde ethynylation performance of CuO nanocrystalline confined in SiO2 networks

Catalytic fast pyrolysis of biomass to aromatics over hierarchical HZSM-5

Cu-ZSM-11 catalysts prepared with microwave irradiation ion-exchange method and direct decomposition of NO over MeOx/Cu-ZSM-11 with microwave irradiation

Recent advances in atomic-scale in situ electron microscopy techniques for probing shape-selectivity of zeolites

Related Author

Fang JIN

Peng ZHANG

Guiying WU

Di WU

Haitao LI

Pingfan MENG

Yin ZHANG

Ruifang WU

Related Institution

Key Laboratory for Green Chemical Process of Ministry of Education, Hubei Key Laboratory of Novel Reactor and Green Chemical Technology, School of Chemical Engineering and Pharmacy, Wuhan Institute of Technology

Bryan Research & Engineering, LLC, Bryan

Engineering Research Center of Education for Fine Chemicals, School of Chemistry and Chemical Engineering, Shanxi University

Dalian Research Institute of Petroleum and Petrochemicals, SINOPEC

School of Chemistry and Materials Sciences, Heilongjiang University

⁰