Impact of B2O3 loading on sulfur-resistant methanation activity of MoO3/CeO2-Al2O3 catalyst

LIU Zhen; WANG Baowei; WANG Weihan; MENG Dajun; LI Zhenhua; MA Xinbin

doi:10.11949/j.issn.0438-1157.20160317

您当前的位置：

首页 >

文章列表页 >

Impact of B₂O₃ loading on sulfur-resistant methanation activity of MoO₃/CeO₂-Al₂O₃ catalyst

更新时间：2025-12-10

- Impact of B₂O₃ loading on sulfur-resistant methanation activity of MoO₃/CeO₂-Al₂O₃ catalyst
- CIESC Journal Issue 9, Pages: 3672-3677(2016)
- 作者机构：
  
  天津大学化工学院绿色合成与转化教育部重点实验室,天津,300072
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20160317
  CLC： Q028.8
- Online First：05 September 2016，
  
  Published：05 September 2016
- 稿件说明：
移动端阅览
LIU Zhen, WANG Baowei, WANG Weihan, et al. Impact of B₂O₃ loading on sulfur-resistant methanation activity of MoO₃/CeO₂-Al₂O₃ catalyst[J]. CIESC Journal, 2016, (9): 3672-3677. DOI: 10.11949/j.issn.0438-1157.20160317.
DOI：

LIU Zhen, WANG Baowei, WANG Weihan, et al. Impact of B₂O₃ loading on sulfur-resistant methanation activity of MoO₃/CeO₂-Al₂O₃ catalyst[J]. CIESC Journal, 2016, (9): 3672-3677. DOI: 10.11949/j.issn.0438-1157.20160317. DOI：

摘要

考察B2O3负载量对于MoO3/CeO2-Al2O3催化剂对耐硫甲烷化活性的影响，利用BET、XRD、TEM、NH3-TPD等手段对催化剂进行了表征。结果表明，催化剂的耐硫甲烷化活性随B2O3负载量增加呈现先升高后降低的变化规律；当B2O3负载量为0.5%时，催化剂的耐硫甲烷化活性最高，CO转化率达到55%。结合表征分析，发现添加B2O3会影响催化剂载体的结构和表面酸度，从而影响活性组分的分散程度，进而影响MoO3/CeO2-Al2O3催化剂的耐硫甲烷化性能。催化剂的晶化程度太高或单位面积上的强酸量太多均不利于甲烷化反应；较好的活性组分分散度有利于催化剂甲烷化活性的提高。

Abstract

Synthetic natural gas (SNG) production from coal is considered again due to rising prices for natural gas

the wish for less dependency from natural gas imports and the opportunity of reducing green house gases. The technical

economic and ecological feasibility of SNG with Mo-based catalysts showed water-gas shift and sulfur-resistant methanation has been studied. In this paper the impact of B2O3 loading on the MoO3/CeO2-Al2O3 catalysts for sulfur-resistant methanation was investigated. The catalysts were prepared by impregnation method and characterized by means of BET

XRD

TEM and NH3-TPD. The results showed that the sulfur-resistant methanation activity of MoO3/CeO2-Al2O3 catalysts were increased at first and then decreased as the increase of B2O3 loading. The catalyst adding 0.5% B2O3 showed the highest activity and the conversion of CO was 55%. The characterization results indicated that the addition of B2O3 had influences on the structure and surface acidity of catalysts and the dispersion of active components

which further impacted the activity of catalysts. High-crystallization and enhancement of strong acid quantity were not beneficial to the sulfur-resistant methanation

while the high dispersion of active components was favorable to the improvement of the catalyst activity.

关键词

Keywords

references

Views

187

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Preparation of WO3/TiO2-ZrO2 catalyst for selective catalytic reduction and mechanism of NH3 activation

Crystal structures, electronic structures and conductivity of Si highly doped RuO2

Removal of marine diesel engine exhaust pollutants with DOC+SCR technologies

Wet process of elemental mercury removal using Ag@AgCl-BiOCl photocatalyst under fluorescent light irradiation

Preparation of C/TiO2-SO42- and their water splitting performance

Related Author

WANG Longfei

ZHANG Yaping

GUO Wanqiu

SHEN Kai

ZHENG Pengfei

YANG Linjun

TANG Zhongzhi

WANG Qifan

Related Institution

School of Chemical Engineering and Energy, Zhengzhou University

Key Laboratory of Energy Thermal Conversion and Control of Ministry of Education, School of Energy and Environment, Southeast University

Fujian Institute of Metallurgical Engineering

Institute of Materials Research, Fuzhou University

College of Materials Science and Engineering, Fuzhou University

⁰