Preparation of a series of fine chemicals by blast furnace slag

更新时间：2025-12-10

- Preparation of a series of fine chemicals by blast furnace slag
- CIESC Journal Issue 9, Pages: 3988-3994(2016)
- 作者机构：
  
  1. 安徽工业大学教育部冶金减排与资源综合利用重点实验室,安徽,马鞍山,243002
  2. 安徽工业大学冶金工程与资源综合利用安徽省重点实验室,安徽,马鞍山,243002
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20160220
  CLC： Q170.9
- Online First：05 September 2016，
  
  Published：05 September 2016
- 稿件说明：
移动端阅览
SHEN Xingmei, LI Liaosha, WU Xingrong, et al. Preparation of a series of fine chemicals by blast furnace slag[J]. CIESC Journal, 2016, (9): 3988-3994.
DOI：

SHEN Xingmei, LI Liaosha, WU Xingrong, et al. Preparation of a series of fine chemicals by blast furnace slag[J]. CIESC Journal, 2016, (9): 3988-3994. DOI： 10.11949/j.issn.0438-1157.20160220.

摘要

以高炉渣为主要原料，在前期工作基础上，通过更进一步深入研究，开发出高炉渣制备系列精细化工品的完整工艺路线。采用硫酸酸解高炉渣的方法，获得产品石膏；制备超细硅酸铝的最佳水渣比为7：1，体系pH控制为4.0，通过加入铝片的方式进行除铁；制备镁铝尖晶石的最佳尿素质量百分比为65%，最佳除铁方法为向前体溶液中加入5% Na2S2O4。采用高炉渣制备得到的3种产品，其化学成分均符合相关标准。该工艺路线具有流程短、成本低等优点；渣中有价组分得以全部利用，无残渣排放，环境效益明显。

Abstract

On the basis of previous works

preparation of a series of fine chemicals by blast furnace slag was researched further and deeply

and the process route was developed. The first product

gypsum

was obtained by sulphuric acid hydrolysis. The optimum conditions for preparing aluminum silicate were:water-slag ratio 7:1

pH 4.0 and adding small pieces of Al plates to remove iron. The optimum conditions for preparing magnesium aluminum spinel were:mass percent of urea 65% and amount of Na2S2O4 5%. The chemical composition of the three products was in accord with the relative standards. This process had the advantages of short flow

low cost

etc. Almost all valuable contents in the slag were used

and no residue was discharged. Thus

it had better environmental benefit.

关键词

Keywords

references

Views

200

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Effect of ammonia concentration on dissolution rate of gypsum particles in phosphogypsum-ammonia-water reaction system for carbon sequestration

Research on the characterization of the molecular weight and its distribution of perfluoropolyether

Multi objective optimization of flow and heat transfer characteristics of modified manifold microchannel heat sink based on machine learning

Zn-doped PdO/ZrO2 with rich oxygen vacancies for the synthesis of diphenyl carbonate from CO2 and phenol

Thermal analysis of phase change suspension jet impinging on wall surface covered with variable-shape porous layer

Related Author

Lin WU

Ji LI

Jiahua ZHU

Yuan GONG

Jing GE

Related Institution

School of Chemical Engineering, Sichuan University

⁰