Synthesis of mesoporous titanosilicates from industrial by-product hexafluosilicic acid and application for catalytic cyclohexene epoxidation

JIN Fang; LIU Tieliang; WANG Xianqiao; WU Yuanxin

doi:10.11949/j.issn.0438-1157.20160187

您当前的位置：

首页 >

文章列表页 >

Synthesis of mesoporous titanosilicates from industrial by-product hexafluosilicic acid and application for catalytic cyclohexene epoxidation

更新时间：2025-11-26

- Synthesis of mesoporous titanosilicates from industrial by-product hexafluosilicic acid and application for catalytic cyclohexene epoxidation
- CIESC Journal Vol. 67, Issue 10, Pages: 4176-4186(2016)
- 作者机构：
  
  武汉工程大学化工与制药学院, 绿色化工过程教育部重点实验室, 湖北省新型反应器与绿色化学工艺重点实验室,湖北,武汉,430073
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20160187
  CLC： Q028.8
- Online First：05 October 2016，
  
  Published：05 October 2016
- 稿件说明：
移动端阅览
JIN Fang, LIU Tieliang, WANG Xianqiao, et al. Synthesis of mesoporous titanosilicates from industrial by-product hexafluosilicic acid and application for catalytic cyclohexene epoxidation[J]. CIESC Journal, 2016, 67(10): 4176-4186.
DOI：

JIN Fang, LIU Tieliang, WANG Xianqiao, et al. Synthesis of mesoporous titanosilicates from industrial by-product hexafluosilicic acid and application for catalytic cyclohexene epoxidation[J]. CIESC Journal, 2016, 67(10): 4176-4186. DOI： 10.11949/j.issn.0438-1157.20160187.

摘要

利用磷肥工业副产的氟硅酸为原料，在十六烷基三甲基溴化铵（CTAB）溶液中与氨水和钛酸四丁酯（TBOT）反应，水热陈化制取钛硅介孔分子筛，通过改变水热时间、CTAB的加入量、硅钛比和模板剂的脱除方法研究实验条件对钛硅介孔分子筛的结构和性能的影响，采用氮气吸脱附、扫描电镜、透射电镜和固体紫外漫反射对样品进行表征。结果表明，SiO2:CTAB:TBOT:NH3:H2O的摩尔比为1:1.50:0.03:10:150，水浴时间为5 h时，所得样品的比表面积可达1116 m2·g-1，介孔体积为0.79 cm3·g-1。合成的钛硅介孔分子筛作为催化剂应用于环己烯环氧化反应，环己烯的转化率可达68.10%，环氧环己烷产物选择性为96.60%，Ti活性位的转化频率达到99.5 h-1。该方法可以提高磷肥副产低浓度氟硅酸的附加值，降低钛硅介孔分子筛催化剂的生产成本。

Abstract

The hexafluosilicic acid

a by-product in phosphate fertilizer industry

was used as the raw material for hydrothermal synthesis of mesoporous titanosilicates with cetyltrimethylammonium bromide (CTAB) as the cationic surfactant and ammonia as neutralization agent. The influence of synthesis conditions including hydrothermal time

the ratio of CTAB to silica

Si/Ti ratio

and surfactant removal methods on the structures and properties of mesoporous titanosilicates were investigated by characterization of the resulting product with techniques of X-ray diffraction (XRD)

nitrogen adsorption/desorption

scanning electron microscopy (SEM)

solid UV light scattering. At the optimized synthesis condition of the ratio of SiO2:CTAB:Ti(OC4H9)4:NH3:H2O=1:1.50:0.03:10:150 and the hydrothermal time of 5 h

mesoporous titanosilicate had specific surface area of 1116 m2·g-1 and porosity of 0.79 cm3·g-1. When used as catalyst for cyclohexene epoxidation. this mesoporous titanosilicate showed good catalytic activities with cyclohexene conversion of 68.10%

cyclohexene epoxide selectivity of 96.60%

and turnover frequencies of Ti active sites of 99.5 h-1. This new synthesis technique will greatly improve profit of phosphate fertilizer industry by utilizing the by-product hexafluosilicic acid for the production of value-added mesoporous titanosilicate.

关键词

Keywords

references

Views

240

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Zeolite catalysts for catalytic cracking of hydrocarbon to increase light olefins selectivity

One-step hydrothermal method toward preparation of Ni3S2@Mo2S3 high-efficient catalyst for oxygen evolution reaction in water electrolysis

Preparation of ethyl levulinate from cellulose catalyzed by dealuminated USY molecular sieves supporting copper

Combinatorial modification and catalytic performance of ZSM-5 zeolite by phosphorus and aluminum

Morphology-controlled synthesis of mesoporous alumina dependenton triblock copolymer

Related Author

LIU Qi

CHEN Zikang

PIAO Yu

XIAO Peng

GE Yafen

GONG Yanjun

Juan ZHAO

Mengcheng WU

Related Institution

State Key Laboratory of Heavy Oil Processing, Key Laboratory of Catalysis of CNPC, College of Chemical Engineering and Environment, China University of Petroleum

School of Chemistry and Chemical Engineering, Chongqing University

School of Chemical Engineering and Energy, Zhengzhou University

College of Mechanical and Electrical Engineering, Henan Agricultural University

State Key Laboratory of Heavy Oil Processing, the Key Laboratory of Catalysis of CNPC, China University of Petroleum

⁰