Development of inorganic nano particles modified sodium alginate hybrid membranes for pervaporation

NA Shasha; LI Weixing; XING Weihong

doi:10.11949/j.issn.0438-1157.20160111

您当前的位置：

首页 >

文章列表页 >

Development of inorganic nano particles modified sodium alginate hybrid membranes for pervaporation

更新时间：2025-12-10

- Development of inorganic nano particles modified sodium alginate hybrid membranes for pervaporation
- CIESC Journal Issue 9, Pages: 3730-3737(2016)
- 作者机构：
  
  南京工业大学化工学院, 材料化学工程国家重点实验室, 国家特种分离膜工程技术研究中心,江苏,南京,210009
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20160111
  CLC： Q028.8
- Online First：05 September 2016，
  
  Published：05 September 2016
- 稿件说明：
移动端阅览
NA Shasha, LI Weixing, XING Weihong. Development of inorganic nano particles modified sodium alginate hybrid membranes for pervaporation[J]. CIESC Journal, 2016, (9): 3730-3737.
DOI：

NA Shasha, LI Weixing, XING Weihong. Development of inorganic nano particles modified sodium alginate hybrid membranes for pervaporation[J]. CIESC Journal, 2016, (9): 3730-3737. DOI： 10.11949/j.issn.0438-1157.20160111.

摘要

为提高海藻酸钠（SA）膜的渗透汽化分离性能，分别采用纳米氧化铝、纳米氧化锆和纳米氧化钛对SA膜进行改性，对比分析了3种不同杂化膜渗透汽化分离性能的差异，并将分离性能较好的杂化膜应用到乙酸与乙醇酯化反应脱水的体系中。系统考察了无机纳米粒子含量对SA膜渗透汽化分离性能的影响，对杂化膜进行了接触角、傅里叶红外（FTIR）、扫描电子显微镜（SEM）、热重/差示扫描量热（TG/DSC）、X射线衍射（XRD）和拉伸强度等表征与分析。结果表明，无机纳米粒子能提高SA膜的热稳定性、机械强度和渗透通量，当无机纳米粒子与SA质量比为0.3时，掺杂TiO2、ZrO2和Al2O3的杂化膜二碘甲烷的接触角依次升高，同时渗透通量也依次升高。SA-0.3Al2O3杂化膜亲水性较好，然而SA-0.3ZrO2杂化膜分离性能最优，50℃下分离水含量10%的乙醇-水溶液，膜渗透通量达到336 g·m-2·h-1，渗透侧水含量99.97%，分离因子29990。酯化反应脱水实验表明，在80℃时，酯化反应脱水实验乙酸转化率均高于无脱水实验乙酸转化率，平衡转化率不断被打破，反应12 h后，转化率由平衡时的79.3%提高到93.9%。

Abstract

In order to improve the pervaporation performance of SA

nano-alumina

nano-zirconia and nano-titania were incorporated into SA solution

respectively. The difference of pervaporatin performance was analyzed

and the membrane that had better separation performance was selected for pervaporation (PV)-assisted esterification of acetic acid and ethanol. The effect of nano-particles content on the separation performance was investigated. The obtained membranes were characterized by scanning electron microscope (SEM)

Fourier transform infrared spectroscopy (FTIR)

X-ray diffraction (XRD)

thermogravimetry (TG) and differential scanning calorimetry (DSC). The thermal stability

tensile strength and permeate flux of hybrid membranes were enhanced after incorporating nano-particles into SA. When the mass ratio of nanoparticles to SA was 0.3

the methylene iodide contact angle of incorporated TiO2

ZrO2 and Al2O3 hybrid membranes increased

respectively. Meanwhile

the permeate flux increased at the same time. The hydrophilic property of SA-0.3Al2O3 membrane was the best; however

the separation performance of SA-0.3ZrO2 membrane was better. The permeate flux of SA-0.3ZrO2 membrane was 336 g·m-2·h-1 with water content 99.97% in the permeate side and separation factor 29990 when the amount of water in feed was 10% at 50℃. The conversion of esterification enhanced by pervaporation reached 93.9% in 12 h at 80℃.

关键词

Keywords

references

Views

156

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Fabrication of PVA/SA/CPO mixed matrix membranes via biomimetic mineralization for dehydration of esterification systems

Hydrophobic pervaporation membranes on polymer substrate for solvent recovery

Separation of neutral aromatic compounds from tobacco waste by ZIF-67/PDMS composite membrane

Research on temperature forecasting of polyester fiber esterification process based on federated learning

Advantages and risks of swirling cooling granulation towers

Related Author

ZHANG Yu

QIAN Xiliang

GAN Jiatian

ZOU Yun

TONG Zhangfa

ZHANG Yu

GAN Jiatian

ZOU Yun

Related Institution

Guangxi Key Laboratory of Petrochemical Resource Processing and Process Intensification Technology, School of Chemistry and Chemical Engineering, Guangxi University

University Engineering Research Center of Green Chemical New Materials, School of Chemistry and Chemical Engineering, Guangxi University

University Engineering Research Center of Green Chemical New Materials, School of Chemistry and Chemical Engineering, Guangxi University, Nanning, Guangxi 530004, PR. China

Center for Membrane and Water Science &Technology, Collaborative Innovation Center of Membrane Separation and Water Treatment of Zhejiang Province, Zhejiang University of Technology

College of Chemical Engineering, East China University of Science and Technology

⁰