Synthesis of pyridinium based polymerized ionic liquid and its adsorptive desulfurization performance for thiophenic sulfurs from oil

LI Chunxi; XU Huihui; ZHU Xuexi; LU Yingzhou; MENG Hong

doi:10.11949/j.issn.0438-1157.20160104

您当前的位置：

首页 >

文章列表页 >

Synthesis of pyridinium based polymerized ionic liquid and its adsorptive desulfurization performance for thiophenic sulfurs from oil

更新时间：2025-11-26

- Synthesis of pyridinium based polymerized ionic liquid and its adsorptive desulfurization performance for thiophenic sulfurs from oil
- CIESC Journal Issue 7, Pages: 2880-2886(2016)
- 作者机构：
  
  1. 北京化工大学化工资源有效利用国家重点实验室,北京,100029
  2. 北京化工大学化学工程学院,北京,100029
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20160104
  CLC： 632.19
- Online First：05 July 2016，
  
  Published：05 July 2016
- 稿件说明：
移动端阅览
LI Chunxi, XU Huihui, ZHU Xuexi, et al. Synthesis of pyridinium based polymerized ionic liquid and its adsorptive desulfurization performance for thiophenic sulfurs from oil[J]. CIESC Journal, 2016, (7): 2880-2886.
DOI：

LI Chunxi, XU Huihui, ZHU Xuexi, et al. Synthesis of pyridinium based polymerized ionic liquid and its adsorptive desulfurization performance for thiophenic sulfurs from oil[J]. CIESC Journal, 2016, (7): 2880-2886. DOI： 10.11949/j.issn.0438-1157.20160104.

摘要

以4-乙烯基吡啶（VP）和1

4-对二氯苄（PXDC）为原料，通过自由基聚合和季铵化交联反应，制得了一种高度交联的离子液体聚合物——PVP-PXDC。采用凝胶渗透色谱法、元素分析法、红外光谱分析法、扫描电镜、热重分析及比表面积分析等分析方法对离子聚合物的组成、结构、形貌、热稳定性及比表面积、孔结构参数等进行了表征，并考察了吸附剂的脱硫性能。结果表明，先通过聚合得到重均分子量16万以上的PVP线性聚合物，再在DMF溶剂中按VP与PXDC摩尔比2：1加入交联剂，可得到平均孔径为17.8 nm聚合离子液体介孔材料，其热分解温度在250℃以上，比表面积为56.9 m2·g-1。在油/剂质量比50：1和30℃条件下，其对1000 mg·kg-1模型油中二苯并噻吩（DBT）、苯并噻吩（BT）和噻吩（T）的吸附量分别为5.65、5.48和4.53 mg S·g-1，远高于常规吡啶基离子液体，吸附等温线符合Freundlich方程。

Abstract

By using 4-vinyl pyridine (VP) and p-xylylene dichloride (PXDC)

a PVP-PXDC

a highly crosslinked polymerized ionic liquid

was synthesized through radical polymerization and quaternary crosslinking reaction. In terms of composition

structure

morphology

thermal stability

specific surface area and pore structure of the ionic liquid polymer

it has been characterized by techniques of gel permeation chromatography

elemental analysis

infrared spectroscopy

scanning electron microscopy

thermo gravimetric analyzer and N2-adsorption

respectively

followed by the performance evaluation as adsorbent for desulfurization. It showed that the mesoporous ionic liquid polymer features 17.8 nm of average pore size

56.9 m2·g-1 of specific area of and above 250℃ of decomposition temperature. The ionic liquid polymer was achieved by synthesis of the linear PVP polymer (160000 of weight-based mean molecular weight) followed by crosslinking with PXDC at molar ratio of VP/PXDC of 2:1 in DMF solvent. Its adsorption capacities for 1000 mg·kg-1 DBT

BT and T in a representative oil

are 5.65

5.48 and 4.53 mg S·g-1 at 303 K and mass ratio of oil/adsorbent of 50:1

respectively

which are much higher than those of conventional pyridinium based ionic liquids. Moreover

the adsorption isotherms follow Freundlich equation.

关键词

Keywords

references

Views

311

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Research progress of hydrogen sulfide deep adsorption materials

Construction of transition metal-based nitrogen-doped carbon and their desulfurization performance

Ultramicroporous MOF with multiple adsorption sites for CH4/N2 separation

Preparation of acid-rich 13X molecular sieve and its ultra-deep adsorption removal of mercaptan in biodiesel

Construction of amorphous NiP@γ-Al2O3 catalyst rich in Niδ+ for petroleum resin hydrogenation with enhanced hydrogenation and desulfurization activity

Related Author

Tao YU

Yundong WANG

Zuohua LIU

Jianxiu MA

Yu JING

JIN Changzhou

YIN Mengyang

WANG Haochen

Related Institution

State Key Laboratory of Chemical Engineering, Department of Chemical Engineering, Tsinghua University

School of Chemistry and Chemical Engineering, Chongqing University

Linggas Materials Tianjin Ltd.

College of Resources and Environment, Henan Agricultural University

College of Chemical Engineering, Qinghai University

⁰