Preparation of PAN-H1.6Mn1.6O4 membrane and its adsorption properties in brine

WANG Jun; JIA Qingyuan; GUO Ruili; ZHANG Jianshu

doi:10.11949/j.issn.0438-1157.20151871

您当前的位置：

首页 >

文章列表页 >

Preparation of PAN-H_1.6Mn_1.6O₄ membrane and its adsorption properties in brine

更新时间：2025-11-26

- Preparation of PAN-H_1.6Mn_1.6O₄ membrane and its adsorption properties in brine
- CIESC Journal Vol. 67, Issue 10, Pages: 4282-4289(2016)
- 作者机构：
  
  石河子大学化学化工学院, 新疆兵团化工绿色过程重点实验室,新疆,石河子,832003
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20151871
  CLC： Q028.8TQ425.22
- Online First：05 October 2016，
  
  Published：05 October 2016
- 稿件说明：
移动端阅览
WANG Jun, JIA Qingyuan, GUO Ruili, et al. Preparation of PAN-H_1.6Mn_1.6O₄ membrane and its adsorption properties in brine[J]. CIESC Journal, 2016, 67(10): 4282-4289. DOI: 10.11949/j.issn.0438-1157.20151871.
DOI：

WANG Jun, JIA Qingyuan, GUO Ruili, et al. Preparation of PAN-H_1.6Mn_1.6O₄ membrane and its adsorption properties in brine[J]. CIESC Journal, 2016, 67(10): 4282-4289. DOI: 10.11949/j.issn.0438-1157.20151871. DOI：

摘要

采用亲水的PAN为成膜材料，制备了掺杂H1.6Mn1.6O4的PAN-H1.6Mn1.6O4锂离子筛膜。通过SEM、Li+静态吸附实验、（NH4）2S2O8对锂的洗脱实验和卤水中吸附实验，研究了锂离子筛的添加量对PAN-H1.6Mn1.6O4锂离子筛膜结构、Li+吸附-洗脱性能的影响。结果表明，PAN浓度为10%（质量），H1.6Mn1.6O4的添加量为50%（质量）时，PAN-H1.6Mn1.6O4离子筛膜的吸附量为17.45 mg·g-1，达到粉末状吸附量的88.0%。以（NH4）2S2O8为洗脱剂，当浓度为0.3 mol·L-1、液固比为600:1、时间为12 h时，锂洗脱量为17.23 mg·g-1，锰溶损率仅为1.14%。在含有Na+、K+、Mg2+和Ca2+的罗布泊老卤卤水中，锂离子筛膜对Li+有很高的选择性。在卤水中进行10次吸附与解吸循环，吸附量从11.64 mg·g-1下降到10.94 mg·g-1，吸附容量仅损失6.0%。总体结果表明亲水性载体对H1.6Mn1.6O4吸附容量影响较小，温和的洗脱剂对锂离子筛膜的化学稳定性有利。

Abstract

PAN-H1.6Mn1.6O4 lithium ion-sieve membrane was prepared by blend of lithium ion sieve (H1.6Mn1.6O4) with hydrophilic polymer poly(acrylonitrile) (PAN). The effects of adding amount of lithium ion sieve for PAN-H1.6Mn1.6O4 membrane structure and Li+ adsorption-desorption properties were investigated by SEM

Li+ static adsorption

(NH4)2S2O8 elution and adsorption experiments in brine. The results showed that the adsorption capacity of PAN-H1.6Mn1.6O4 membrane (17.45 mg·g-1) achieved to 88.0% of H1.6Mn1.6O4 powder when the concentration of PAN was 10% (mass) and the amount of loading of H1.6Mn1.6O4 was 50% (mass). In addition

when (NH4)2S2O8 solution was used as eluent with the eluent concentration

liquid-solid ratio and time of 0.3 mol·L-1

600:1 and 12 h

respectively

the amount of lithium ion elution was 17.23 mg·g-1 and the manganese loss of ratio was only 1.14%. The PAN-H1.6Mn1.6O4 membrane showed good selectivity for Li+ in Lop Nor brine containing other cations such as Na+

K+

Mg2+ and Ca2+. After ten times adsorption-desorption cycles in brine

the adsorption capacity of lithium ion was lost only 6.0% (from 11.64 mg·g-1 to 10.94 mg·g-1). Overall results demonstrated that using hydrophilic PAN carrier material had little effect on the adsorption capacity of H1.6Mn1.6O4 for lithium ion

and the mild eluent was favorable to chemical stability of lithium-ion sieve membrane.

关键词

Keywords

references

Views

263

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Preparation of ZTIF based hydrophobic micro-mesoporous carbon and their adsorption and separation performance of 5-hydroxymethylfurfural

Fine adjustment of elliptical windows of ZIFs and performances of adsorptive separation of furfural/5-hydroxymethylfurfural

Adaptive modeling of simulated moving bed based on KELM-ANFIS

Optimization of ultrasonic-assisted extraction of PPS oligomers from PPS industrial waste by response surface methodology

Methods of adaptive prediction and abnormal states traceability for sulphur content in flue gas desulfurization process

Related Author

LYU Tiantian

YUAN Min

WANG Jiang

GAO Meizhen

YANG Jiahui

XU Hong

DONG Jinxiang

SHI Qi

Related Institution

College of Chemical Engineering and Technology, Shanxi Key Laboratory of Chemical Product Engineering, Taiyuan University of Technology

College of Chemistry and Chemical Engineering, Taiyuan University of Technology

Key Laboratory of Advanced Control for Light Industry Process of the Ministry of Education, Jiangnan University

College of Chemical Engineering, Zhejiang University of Technology

Zhejiang Provincial Key Laboratory of Robotics and Intelligent Manufacturing Equipment Technology,Ningbo Institute of Material Technology and Engineering, Chinese Academy of Sciences

⁰