Synthesis, physical-mechanical properties and fire behaviors of polyurethane foam with reactive flame retardant and expandable graphite

YANG Rong; QIAO Hong; HU Wentian; XU Liang; SONG Yan; LI Jinchun

doi:10.11949/j.issn.0438-1157.20151564

您当前的位置：

首页 >

文章列表页 >

Synthesis, physical-mechanical properties and fire behaviors of polyurethane foam with reactive flame retardant and expandable graphite

更新时间：2025-12-10

- Synthesis, physical-mechanical properties and fire behaviors of polyurethane foam with reactive flame retardant and expandable graphite
- CIESC Journal Issue 5, Pages: 2169-2175(2016)
- 作者机构：
  
  常州大学材料科学与工程学院,江苏,常州,213000
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20151564
  CLC： 631
- Online First：05 May 2016，
  
  Published：05 May 2016
- 稿件说明：
移动端阅览
YANG Rong, QIAO Hong, HU Wentian, et al. Synthesis, physical-mechanical properties and fire behaviors of polyurethane foam with reactive flame retardant and expandable graphite[J]. CIESC Journal, 2016, (5): 2169-2175.
DOI：

YANG Rong, QIAO Hong, HU Wentian, et al. Synthesis, physical-mechanical properties and fire behaviors of polyurethane foam with reactive flame retardant and expandable graphite[J]. CIESC Journal, 2016, (5): 2169-2175. DOI： 10.11949/j.issn.0438-1157.20151564.

摘要

将反应型阻燃剂六(4-磷酸二乙酯羟甲基苯氧基)环三磷腈(HPHPCP)和可膨胀石墨(EG)复配

制备了阻燃聚氨酯泡沫

详细研究了复配阻燃剂对聚氨酯泡沫的物理力学性能、热稳定性以及阻燃性能的影响。结果表明

阻燃聚氨酯泡沫的密度和热导率随着复配阻燃剂中EG含量的增加而升高;压缩强度随着EG含量的增加呈现先增加后降低的趋势。热失重表明复配阻燃剂大大提高了聚氨酯泡沫的热稳定性。聚氨酯泡沫的初始分解温度(T10%)从212.9℃

分别提高到222.0、231.2和243.2℃;700℃残炭量从7.6%分别提高到26.3%、31.6%和37.9%。聚氨酯泡沫的阻燃性能随着复配阻燃剂中EG含量的增加而提高。阻燃聚氨酯泡沫的极限氧指数从19%提高到29%

均能通过UL-94水平燃烧HF-1等级和垂直燃烧V-0等级。

Abstract

Flame retardant polyurethane foams have been synthesized by using a new reactive flame retardant hexakis (4-diethyl phosphate hydroxymethyl phenoxy) cyclotriphosphazene (HPHPCP) and expandable graphite (EG). The effects of flame retardants on physical-mechanical properties

thermal stability and fire performances were investigated. In particular

the fire behaviour of the foams was studied by the oxygen index and UL-94 burning test. The results showed that the density of flame retardant foams increased with flame retardant compound. The compressive strength increased first and then declined with the decrease content of HPHPCP. However

an increase in the content of expandable graphite caused a worsening of insulating properties of PUF. The presence of HPHPCP mixture with EG brought an overall improvement in the thermal stability and fire behavior. The initial decomposition temperature (T10%)

maximum decomposition temperature (Tmax) and char residues at 700℃ increased with increasing content of EG in mixture flame retardant. Moreover

the oxygen index (OI) increased in a linear way and all flame retardant PUFs can pass UL-94 HF-1 and V-0 rating.

关键词

Keywords

references

Views

195

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Synthesis of phosphorus-nitrogen flame retardant based on cyclophosphonate and its application on rigid polyurethane foam

Recent progress in the preparation, structure, and application of thermal insulation materials

Preparation and heat resistance of cyanide-derived benzoxazine resins

Review on combustion behavior and flame retardant research of phenolic foams

Preparation and performance of base magnesium sulfate porous sound absorbing materials

Related Author

Mengdi LI

Bo WANG

Zhehui WANG

Ye ZHANG

Rong YANG

Jinchun LI

CHEN Xinyan

CHEN Yiling

Related Institution

School of Materials Science and Engineering, Jiangsu Key Laboratory of Environmentally Friendly Polymeric Materials, Changzhou University

Hubei Key Laboratory of Plasma Chemistry and Advanced Materials, School of Materials Science & Engineering, Wuhan Institute of Technology

School of Chemistry and Environmental Engineering, Yancheng Teachers University

School of Chemistry and Chemical Engineering, Nanjing University

School of Materials Science and Engineering, Shenyang University of Chemical Technology

⁰