Synthesis and properties of bisoxalatoborate spiro cyclic quaternary ammonium salt in supercapacitors

ZHANG Qing; YU Xinwei; CHEN Yao; ZHENG Wenzhi; YU Ziwen; ZHENG Cheng; CHEN Shengzhou; LIU Hui

doi:10.11949/j.issn.0438-1157.20151170

您当前的位置：

首页 >

文章列表页 >

Synthesis and properties of bisoxalatoborate spiro cyclic quaternary ammonium salt in supercapacitors

更新时间：2025-12-10

- Synthesis and properties of bisoxalatoborate spiro cyclic quaternary ammonium salt in supercapacitors
- CIESC Journal Issue 4, Pages: 1594-1600(2016)
- 作者机构：
  
  广州大学化学化工学院,广东,广州,510006
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20151170
  CLC： Q150.4
- Online First：05 April 2016，
  
  Published：05 April 2016
- 稿件说明：
移动端阅览
ZHANG Qing, YU Xinwei, CHEN Yao, et al. Synthesis and properties of bisoxalatoborate spiro cyclic quaternary ammonium salt in supercapacitors[J]. CIESC Journal, 2016, (4): 1594-1600.
DOI：

ZHANG Qing, YU Xinwei, CHEN Yao, et al. Synthesis and properties of bisoxalatoborate spiro cyclic quaternary ammonium salt in supercapacitors[J]. CIESC Journal, 2016, (4): 1594-1600. DOI： 10.11949/j.issn.0438-1157.20151170.

摘要

以溴代8-氧杂-螺[4

5]季铵盐(ASB)、二水草酸(OD)、硼酸(BA)为原料

通过离子交换法制备电解质双草酸硼酸螺环季铵盐(BSQA)

通过核磁共振(13C NMR)和液相色谱-质谱联用(LC-MS)分析对其进行表征

验证了其结构。采用正交实验对合成工艺进行优化

优化工艺条件为nASB:nBA 2.8:1

反应时间4 h

反应温度90℃

溴代螺环季铵盐的转化率为90.2%。将BSQA、市售四氟硼酸四乙基铵(ET4NBF4)分别与乙腈配制成电解液并模拟组装成超级电容器并测试电化学性能。结果表明

BSQA电解液工作电压达3.0 V

充放电效率达94.89%

能量密度达11.63 W·h·kg-1

产品电化学性能优于常用的有机电解质ET4NBF4

适用于更高的工作电压。

Abstract

Synthesis of bisoxalatoborate spiro cyclic quaternary ammonium salt (BSQA) from 8-oxa-5-azonia- spiro[4

5]decane bromide(ASB)

oxalate dihydrate(OD) and boric acid (BA) was by means of ion exchange. Its structure was verified by 13C NMR and LC-MS. Synthesis of BSQA was optimized by using orthogonal test. The optimized conditions were as follows: molar ratio of nASB:nBA was 2.8:1

reaction time was 4 h and reaction temperature was 90℃. Finally

the conversion rate of ASB was 90.2% in this optimized condition. Two kinds of electrolyte that made from BSQA

ET4NBF4 with acetonitrile separately were applied in simulated supercapacitor to test the electrochemical performance. The result showed that the operating voltage can be 3.0V with charge/ discharge efficiency of 94.89% and the energy density of 11.63 W·h·kg-1. The product was better than ET4NBF4 which was usually used as organic electrolyte in the electrochemical performance with a higher operating voltage.

关键词

Keywords

references

Views

779

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Adsorption and energy storage properties of electrolyte ions on nanorippled graphene surfaces

Effect of electrolyte types on the storage behaviors of anions and cations for dual-ion batteries

Synthesis of FeF3 nanoparticles covered by vertical porous carbon for high performance Li-ion battery cathode

Influence of cobalt-manganese ratio adjustment on the properties of LiNi0.8Co0.10-yMn0.05+yAl0.05O2 materials

Research progress of synthesis and properties of coal-based zero-dimensional nanocarbon materials and their applications in energy conversion and storage

Related Author

SONG Fenhong

YE Shurong

MA Jiaming

MA Long

ZHANG Ruibo

FAN Jing

ZHANG Mengmeng

YAN Dong

Related Institution

School of Energy and Power Engineering, Northeast Electric Power University

School of Mechanical Engineering, Northeast Electric Power University

School of Chemical Engineering, Dalian University of Technology

College of Chemical Engineering, Nanjing Tech University

Key Laboratory of Interface Science and Engineering in Advanced Materials, Ministry of Education, Taiyuan University of Technology

⁰