Preparation of alkyl chain cross-linked sulfobutylated lignin and its application in dispersion of carbon nanotubes

ZENG Weimei; LI Yuan; LI Yuda; DENG Yonghong; QIU Xueqing

doi:10.11949/j.issn.0438-1157.20151035

您当前的位置：

首页 >

文章列表页 >

Preparation of alkyl chain cross-linked sulfobutylated lignin and its application in dispersion of carbon nanotubes

更新时间：2025-12-10

- Preparation of alkyl chain cross-linked sulfobutylated lignin and its application in dispersion of carbon nanotubes
- CIESC Journal Issue 1, Pages: 331-338(2016)
- 作者机构：
  
  华南理工大学化学与化工学院, 制浆造纸工程国家重点实验室,广东,广州,510641
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20151035
  CLC： 636.2
- Online First：05 January 2016，
  
  Published：05 January 2016
- 稿件说明：
移动端阅览
ZENG Weimei, LI Yuan, LI Yuda, et al. Preparation of alkyl chain cross-linked sulfobutylated lignin and its application in dispersion of carbon nanotubes[J]. CIESC Journal, 2016, (1): 331-338.
DOI：

ZENG Weimei, LI Yuan, LI Yuda, et al. Preparation of alkyl chain cross-linked sulfobutylated lignin and its application in dispersion of carbon nanotubes[J]. CIESC Journal, 2016, (1): 331-338. DOI： 10.11949/j.issn.0438-1157.20151035.

摘要

利用1

4-丁磺酸内酯作为磺化剂

6-二溴己烷作为烷基化桥联剂对碱木质素进行改性

通过一步反应制备了兼有烷基磺酸基和烷基链的交联结构的新型聚合物——烷基桥联丁基磺酸磺化木质素 (AASLS)

并系统研究了AASLS在碳纳米管(CNT)悬浮液体系的分散性能。结果表明

当分散剂质量掺量为2%时

AASLS分散的CNT悬浮液在660 nm处的吸收高于由聚苯乙烯磺酸钠(PSS)和聚乙烯吡咯烷酮(PVP)分散的CNT悬浮液

悬浮稳定性更高;透射电镜测试结果进一步表明AASLS的掺入有效解决了CNT的团聚问题;拉曼光谱表明

通过AASLS的非共价功能化修饰

CNT的I1350/I1580值有效降低;电化学测试表明AASLS与CNT形成的复合物在酸性电解液中可进行准可逆的氧化反应。

Abstract

Using 1

4-butane sultone as a sulfonating agent and C6H12Br2 as an alkyl chain cross-linking agent

a new family of water soluble alkyl chain cross-linked sulfobutylated lignosulfonates (AASLS) was readily prepared by one step reaction in water

which simultaneously improved sulfonation degree and molecular weight. FTIR

1H NMR

functional group content tests and GPC confirmed their cross-linked chemical structure and efficient nucleophilic substitution reaction mechanism. The dispersion properties of AASLS-carbon nanotubes (CNT) suspension system were systematically studied. The results showed that when the dosage was 2% (mass)

AASLS-CNT suspensions had a higher absorption at 660 nm with a higher suspension stability than that in polyvinyl pyrrolidone (PVP) and sodium polystyrene sulfonate (PSS). Moreover

the transmission electron microscopy (TEM) indicated that the incorporation of AASLS could effectively solve the problem of the agglomeration of CNT. The Raman absorption spectra showed that the I1350/I1580 value of CNT was effectively reduced by the non-covalent functionalization of AASLS

showing that the density of surface defects was decreased. In cyclic voltammogram (CV) test of AASLS-CNT

it was found that AASLS-CNT showed the quasi reversible redox behaviors.

关键词

Keywords

references

Views

319

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Research on the characterization of the molecular weight and its distribution of perfluoropolyether

Preparation and electrochemical performance of P-MXene Ti3C2Tx/CNT porous microsphere sulfur host composite materials

Metal-organic framework encapsulating carbon nanotubes for trace CO2 separation

Design and study on dual-layer rotor cage for ultrafine powder classification

Research progress of water-soluble polymer viscosity reducer

Related Author

LUO Qinjian

ZHANG Wenhui

QI Yuxuan

CUI Xili

XING Huabin

PENG Rui

LI Wei

CAO Yuyuan

Related Institution

College of Chemical and Biological Engineering, Zhejiang University

ZJU-Hangzhou Global Scientific and Technological Innovation Center

Guangxi Key Laboratory of Electromagnetic Chemical Functional Substances, School of Chemical and Biological Engineering, Guilin University of Technology

State Key Laboratory of Multiphase Flow in Power Engineering, Xi’an Jiaotong University

College of Mechanical Engineering, Xi’an Shiyou University

⁰