β-Nucleation effects induced by long chain branching polypropylene

ZHOU Shuai; XIN Zhong; WANG Weixia; ZHAO Shicheng; SHI Yaoqi

doi:10.11949/j.issn.0438-1157.20150846

您当前的位置：

首页 >

文章列表页 >

β-Nucleation effects induced by long chain branching polypropylene

更新时间：2025-12-10

- β-Nucleation effects induced by long chain branching polypropylene
- CIESC Journal Issue 9, Pages: 3788-3794(2015)
- 作者机构：
  
  1. 华东理工大学化工学院, 化学工程联合国家重点实验室,上海,200237
  2. 华东理工大学化工学院, 上海市多相结构材料化学工程重点实验室,上海,200237
  3. 上海化工研究院, 上海市聚烯烃催化技术重点实验室,上海,200062
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20150846
  CLC： Q316.6
- Online First：05 September 2015，
  
  Published：05 September 2015
- 稿件说明：
移动端阅览
ZHOU Shuai, XIN Zhong, WANG Weixia, et al. β-Nucleation effects induced by long chain branching polypropylene[J]. CIESC Journal, 2015, (9): 3788-3794.
DOI：

ZHOU Shuai, XIN Zhong, WANG Weixia, et al. β-Nucleation effects induced by long chain branching polypropylene[J]. CIESC Journal, 2015, (9): 3788-3794. DOI： 10.11949/j.issn.0438-1157.20150846.

摘要

利用乙烯基聚二甲基硅氧烷/苯乙烯接枝型长支链聚丙烯(PP-g-VS/St)在剪切和快速降温过程中可以诱导形成β晶聚丙烯这一优势

研究了PP-g-VS/St在注塑加工过程中作为高分子β晶成核剂对等规聚丙烯(iPP)结晶温度、晶体结构及力学性能的影响。结果表明改性聚丙烯的结晶温度、β晶相对含量和力学性能随着PP-g-VS/St添加量的增加而增加。当PP-g-VS/St的添加量为50%(质量分数)时

改性聚丙烯的结晶温度相对于纯iPP提高约10℃

β晶相对含量达32.8%

冲击强度、弯曲模量和拉伸强度分别相对于纯iPP提高了355.3%、53.8%和15.9%。这些结果为聚丙烯高分子β晶型成核剂的设计提供了新思路。

Abstract

Taking advantages of long chain branching polypropylene based on grafting vinyl polydimethylsiloxane/ styrene (PP-g-VS/St) can generate β-crystal polypropylene under shear and high cooling rate condition

PP-g-VS/St was used as a polymeric β-nucleating agent for isotactic polypropylene (iPP) under injection modeling processing and its effects on the crystallization temperature

crystal structure and mechanical properties of iPP were investigated. The results indicated that the crystallization temperature

β-crystal relative content and mechanical properties of modified iPP were improved as increasing the content of PP-g-VS/St. The crystallization temperature of modified iPP with 50% (mass) PP-g-VS/St increased by 10℃ compared with that of virgin iPP and the β-crystal relative content reached 32.8%. The impact strength

flexural modulus and tensile strength were enhanced by 355.3%

53.8% and 15.9%

respectively

compared with those of virgin iPP. These results may provide a new method to design polymeric β-nucleating agent for iPP.

关键词

Keywords

references

Views

338

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Performance analysis and structural optimization of double-sided spiral groove-type dry gas seal

Preparation of biobased polyurethane adhesives for flexible packaging and their water-resistance and thermal stability assessment

Synthesis and properties of ternary random copolyester PBSF based on 2,5-furandicarboxylic acid

Intelligent optimization and deformation analysis of novel flexible dam foil face gas seal

Improved designs of negative Poisson’s ratio structure and their applications in aerospace engineering

Related Author

WANG Yan

WANG Yutong

CHEN Miaomiao

HE Yiming

LIU Wei

DING Dejun

MA Chenbo

ZHANG Chening

Related Institution

Sinoseal Holding Co., Ltd.

School of Mechanical and Electronic Engineering, Nanjing Forestry University

Ningbo Fangli Seals Co., Ltd.

School of Mechanical Engineering, Jiangsu Ocean University

School of Chemical Engineering and Light Industry, Guangdong University of Technology

⁰