Preparation of CuCl catalyst through ceramic membrane reactor

RAO Hui; ZHANG Feng; ZHONG Zhaoxiang; XING Weihong; JIN Wanqin

doi:10.11949/j.issn.0438-1157.20150801

您当前的位置：

首页 >

文章列表页 >

Preparation of CuCl catalyst through ceramic membrane reactor

更新时间：2025-12-10

- Preparation of CuCl catalyst through ceramic membrane reactor
- CIESC Journal Issue 8, Pages: 3029-3035(2015)
- 作者机构：
  
  南京工业大学膜科学技术研究所, 国家特种分离膜工程技术研究中心,江苏,南京,210009
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20150801
  CLC： Q264.1
- Online First：05 August 2015，
  
  Published：05 August 2015
- 稿件说明：
移动端阅览
RAO Hui, ZHANG Feng, ZHONG Zhaoxiang, et al. Preparation of CuCl catalyst through ceramic membrane reactor[J]. CIESC Journal, 2015, (8): 3029-3035.
DOI：

RAO Hui, ZHANG Feng, ZHONG Zhaoxiang, et al. Preparation of CuCl catalyst through ceramic membrane reactor[J]. CIESC Journal, 2015, (8): 3029-3035. DOI： 10.11949/j.issn.0438-1157.20150801.

摘要

将沉淀反应器与陶瓷膜耦合构成一体式膜反应器

用于制备单分散高活性球形CuCl颗粒。考察陶瓷膜孔径、操作条件和沉淀反应条件对CuCl颗粒形貌和粒径分布的影响

评价氯化亚铜的催化性能。结果表明

陶瓷膜的孔径对CuCl平均粒径影响显著

但对颗粒形貌影响不大;稳定剂对催化剂形貌影响显著

聚乙烯吡咯烷酮K-30 (PVP)的加入使CuCl颗粒由三角形变为球形

使得颗粒粒径更加均一。在铜离子浓度为0.1 mol·L-1

PVP浓度为1 mg·ml-1和进料速率为40 ml·min-1的条件下

采用平均孔径为0.05 mm的陶瓷膜分散Na2SO3溶液

可以制备出平均粒径为5.1 mm的单分散球形CuCl颗粒;该颗粒用于直接法制备有机硅单体的反应中

二甲基二氯硅烷的选择性和硅粉的转化率分别为94%和38%

优于商业化氯化亚铜的催化性能。通过比较不同制备条件下氯化亚铜颗粒的催化性能

发现相比于三角形颗粒

形貌规整的球形氯化亚铜对M2的选择性更高。

Abstract

A direct sediment reactor was coupled with a ceramic membrane for the preparation of high-activity CuCl particles with spherical structure. The effects of the membrane pore size

types of stabilizer

concentration of Cu2+ as well as the dispersed phase flow rate on the size and uniformity of the particles were investigated. The catalytic properties of these CuCl particles were explored via Rochow reaction. The results showed that the average particle size of CuCl decreased with the decrease of membrane pore size. The morphology of the particles changed from triangular structure to spherical when adding polyvinylpyrrolidine(PVP) to the continuous and dispersion phase. The uniform spherical CuCl particles

with the average size of 5.1 mm

were obtained under the conditions that the dispersed phase flow rate of Na2SO3 with a ceramic membrane of 0.05 mm pore size was 40 ml·min-1

the concentration of Cu2+ was 0.1 mol·L-1 and the concentration of PVP was 1 mg·ml-1. The catalytic performance of the uniform spherical CuCl particles

with the dimethyldichlorosilane selectivity of 94% and the Si conversion of 38%

is much better than those of the commercial CuCl particles. Regular spherical particles have a higher selectivity of M2 compared to the triangular particles.

关键词

Keywords

references

Views

291

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Research progress on safety of hydrogen production by alkaline electrolysis of water

Study on continuous alcoholysis of fructose to methyl lactate over TS-1 and In-TS-1

Design of cobalt-nitrogen-carbon/activated carbon rich in zero valent cobalt active site and application of catalytic oxidation of formaldehyde

Study on binder of extruded mordenite catalyst for dimethyl ether carbonylation

Simultaneous removal of NO and soot over La1-xLixMnO3 perovskite catalysts

Related Author

LI Yi

WANG Jiyuan

PAN Xuhai

WANG Zhilei

HUA Min

LI Bolong

JIANG Yuxi

REN Aotian

Related Institution

College of Safety Science and Engineering, Nanjing Tech University

Engineering Laboratory of Hydrogen Safety Technology

Key Laboratory of Biomass Chemical Engineering of Ministry of Education, College of Chemical and Biological Engineering, Zhejiang University

Institute of Zhejiang University-Quzhou

School of Chemical Engineering and Light Industry, Guangdong University of Technology

⁰