Synthesis and structural characterization of layered double hydroxide usingsteel slag as raw material

CHEN Yan; WANG Liqiu; WANG Chenye; LI Huiquan

doi:10.11949/j.issn.0438-1157.20150658

您当前的位置：

首页 >

文章列表页 >

Synthesis and structural characterization of layered double hydroxide usingsteel slag as raw material

更新时间：2025-12-10

- Synthesis and structural characterization of layered double hydroxide usingsteel slag as raw material
- CIESC Journal Issue 12, Pages: 5149-5156(2015)
- 作者机构：
  
  1. 燕山大学环境与化学工程学院,河北,秦皇岛,066004
  2. 中国科学院过程工程研究所绿色过程与工程重点实验室, 湿法冶金清洁生产技术国家工程实验室,北京,100190
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20150658
  CLC： 705
- Online First：05 December 2015，
  
  Published：05 December 2015
- 稿件说明：
移动端阅览
CHEN Yan, WANG Liqiu, WANG Chenye, et al. Synthesis and structural characterization of layered double hydroxide usingsteel slag as raw material[J]. CIESC Journal, 2015, (12): 5149-5156.
DOI：

CHEN Yan, WANG Liqiu, WANG Chenye, et al. Synthesis and structural characterization of layered double hydroxide usingsteel slag as raw material[J]. CIESC Journal, 2015, (12): 5149-5156. DOI： 10.11949/j.issn.0438-1157.20150658.

摘要

以钢渣为原料

醋酸为浸出介质

在一定条件下得到浸出液

利用共沉淀法合成了Ca-Mg-Al-Fe四元层状双金属氢氧化物(LDHs)

探讨了pH、晶化温度和晶化时间对Ca-Mg-Al-Fe四元LDHs层状材料合成的影响

采用XRD、XRF、SEM、FT-IR、TEM、DTA/TG和BET对样品进行了表征。研究表明

pH对层状材料合成的影响最大

pH在10.5～11.8可形成纯相水滑石;晶化温度和晶化时间是影响晶格参数和层间距的重要因素

随温度及时间的增加

其晶格参数a、c及层间距均先减小后增大;LDHs的晶粒尺寸沿a轴方向比沿c轴方向大。当pH 11.8

晶化温度150℃

晶化时间16 h时

合成的LDHs层状材料结构规整、晶型良好、层状结构明显、孔径较大且热稳定性良好。

Abstract

Ca-Mg-Al-Fe quaternary layered double hydroxide (LDHs) was successfully synthesized using the abundant and cheap steel slag as raw material via a convenient chemical process: acetic acid-leaching and coprecipitation. The influences of pH value

crystallization temperature and time on the synthesis of Ca-Mg-Al-Fe quaternary LDHs were investigated. The samples were characterized by XRD

XRF

SEM

FT-IR

TEM

DTA/TG and BET. The results showed that pH was the dominant factor for the synthesis of LDHs

and pure LDHs could be synthesized when pH value was controlled in the range of 10.5-11.8 during coprecipitation process. Crystallization temperature and time were important factors influencing the crystal cell parameters and layer spacing. As the crystallization temperature and time increased

lattice parameters a

c and the spacing of layer first reduced and then increased. Crystal grain size of LDHs along the axis of a was larger than that along the axis of c. When LDHs was synthesized at the conditions of pH of 11.8

crystallization temperature of 150℃ and crystallization time of 16 h

it presented well-defined structure and crystal shape

clear layered structure

large aperture and well thermal stability.

关键词

Keywords

references

Views

302

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Research progress on the modification, processing and applications of medical-grade polyether ether ketone materials

Current status and research progress of crystallization technology of electronic grade phosphoric acid

Current status and research progress of purification technology of electronic grade phosphoric acid

Progress on pharmaceutical engineering of peptide-based drugs

Study on the crystallization thermodynamics and chiral resolution of penicillamine

Related Author

ZHOU Wenbin

LIU Junfeng

DU Biao

ZHOU Lei

LU Chuanjun

PAN Pengju

DONG Ju

YU Liuyang

Related Institution

College of Chemical and Biological Engineering, State Key Laboratory of Chemical Engineering and Low-carbon Technology， Zhejiang University

Zillion New Material Technology (Xi’an) Company Limited

Jiangsu Qiyi Technology Company Limited

State Key Laboratory of Chemical Engineering, School of Chemical Engineering and Technology, Tianjin University

State Key Laboratory of Efficient Utilization for Low Grade Phosphate Rock and Its Associated Resources

⁰