Effects of acid-base catalysts concentration on structures and properties of flexible silica aerogels

CAI Long; PU Qun; QU Kang; SHAN Guorong

doi:10.11949/j.issn.0438-1157.20150600

您当前的位置：

首页 >

文章列表页 >

Effects of acid-base catalysts concentration on structures and properties of flexible silica aerogels

更新时间：2025-12-10

- Effects of acid-base catalysts concentration on structures and properties of flexible silica aerogels
- CIESC Journal Issue 2, Pages: 648-653(2016)
- 作者机构：
  
  浙江大学化学工程与生物工程学院, 化学工程联合国家重点实验室,浙江,杭州,310027
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20150600
  CLC： Q328.9
- Online First：05 February 2016，
  
  Published：05 February 2016
- 稿件说明：
移动端阅览
CAI Long, PU Qun, QU Kang, et al. Effects of acid-base catalysts concentration on structures and properties of flexible silica aerogels[J]. CIESC Journal, 2016, (2): 648-653.
DOI：

CAI Long, PU Qun, QU Kang, et al. Effects of acid-base catalysts concentration on structures and properties of flexible silica aerogels[J]. CIESC Journal, 2016, (2): 648-653. DOI： 10.11949/j.issn.0438-1157.20150600.

摘要

以甲基三甲氧基硅烷(MTMS)和正硅酸乙酯(TEOS)作为混合硅源

甲醇为溶剂

十六烷基三甲基溴化铵(CTAB)为表面活性剂

通过酸碱两步催化溶胶凝胶法制备醇凝胶

经超临界干燥可以制备高弹性疏水块状硅气凝胶。分别采用0.1 mol·L-1 和0.01 mol·L-1 的草酸作为酸催化剂

5 mol·L-1 和10 mol·L-1 的氨水作为碱催化剂

研究不同酸碱催化剂浓度对其网络结构的影响。发现高浓度酸和高浓度碱以及低浓度酸和低浓度碱作为催化剂合成的硅气凝胶的网络结构更加均匀

孔径分布更窄。其中

在草酸浓度为0.01 mol·L-1、氨水浓度为5mol·L-1 时

所得硅气凝胶密度为0.135 g·cm-3、比表面积为807 m2·g-1、孔隙率约为93%

凝胶最大可压缩至其起始长度的60%

压缩回弹率为100%。

Abstract

Flexible silica aerogels with super-hydrophobicity and elasticity were successfully prepared via acid-base two-step sol-gel method

followed by supercritical drying process. They were synthesized with tetraethoxysilane (TEOS) and methyltrimethoxysilane (MTMS) as coprecursors

methyl alcohol as solvent and cetyl trimethyl ammonium bromide (CTAB) as surfactant. The influence of acid-base catalysts concentration on silica aerogels was studied in detail. Aerogels prepared with higher base concentration and lower acid concentration were found to have more uniform pore structures and narrower pore size distributions. It was observed that the optimum aerogels can be obtained with 0.01 mol·L-1 oxalic acid and 5 mol·L-1 ammonia as acid-base catalysts

respectively. The density of the as-prepared aerogel was as low as 0.135 g·cm-3

the porosity was around 93% and the specific surface area was as high as 807 m2·g-1. The maximum compression ratio of the aerogel was as high as 60% with 100% compression resilience ratio.

关键词

Keywords

references

Views

312

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Effect of ammonia evaporation time on the reaction performance of hydrogenation of dimethyl oxalate to ethylene glycol over Cu/SiO2

A study on production of silica from CO2 mineralization by wollastonite promoted via air-driven membrane electrolysis technology

Preparation of molecularly imprinted-TiO2 and its properties of photoelectrocatalytic degradation of solubilized PHE

AFM study of the interaction forces between micro-oil droplets and modified silica surfaces in multiphase dispersion systems

Effect of Si-doped Cu/ZrO2 on the performance of catalysts for CO2 hydrogenation to methanol

Related Author

FANG Song

XIE Dongmin

SUN Houze

CHEN Liuyun

JIN Yong

XIAO Benduan

XU Chao

SU Tongming

Related Institution

School of Chemistry and Chemical Engineering, Guangxi University

Guangxi Huayi Energy Chemical Co., Ltd.

Institute of Green Petroleum Processing and Light Hydrocarbon Conversion, College of Chemical Engineering, Zhejiang University of Technology

School of Chemistry and Chemical Engineering, Chongqing University

College of Chemical Engineering and Materials Science, Tianjin University of Science & Technology

⁰