Electrochemical performance of titanium negative electrolyte for redox flow battery application at different temperature

LI Hongpeng; PAN Jianxin; LI Xue; LI Baoshan; WANG Shubo; XIE Xiaofeng

doi:10.11949/j.issn.0438-1157.20150363

您当前的位置：

首页 >

文章列表页 >

Electrochemical performance of titanium negative electrolyte for redox flow battery application at different temperature

更新时间：2025-12-10

- Electrochemical performance of titanium negative electrolyte for redox flow battery application at different temperature
- CIESC Journal Issue S1, Pages: 287-291(2015)
- 作者机构：
  
  1. 北京化工大学理学院,北京,100029
  2. 清华大学核能与新能源技术研究院,北京,100084
- 作者简介：
- 基金信息：
  
  supported by the National High Technology Research and Development Program of China (2012AA052201).
- DOI：10.11949/j.issn.0438-1157.20150363
  CLC： 614.41
- Online First：30 June 2015，
  
  Published：30 June 2015
- 稿件说明：
移动端阅览
LI Hongpeng, PAN Jianxin, LI Xue, et al. Electrochemical performance of titanium negative electrolyte for redox flow battery application at different temperature[J]. CIESC Journal, 2015, (S1): 287-291.
DOI：

LI Hongpeng, PAN Jianxin, LI Xue, et al. Electrochemical performance of titanium negative electrolyte for redox flow battery application at different temperature[J]. CIESC Journal, 2015, (S1): 287-291. DOI： 10.11949/j.issn.0438-1157.20150363.

摘要

探究了钛基-盐酸水溶液体系电解液的电化学性能。分别采用循环伏安法、电化学交流阻抗法和动电位扫描法研究了不同温度下电解液电对的电化学反应的可逆性和反应的内部作用机理

以及TiCl3的盐酸水溶液体系在石墨电极上的反应平衡电位、交换电流、传递系数等电极反应的动力学参数。循环伏安结果表明温度上升有利于体系的电化学反应的可逆性

40℃时反应的可逆性最好。交流阻抗实验结果采用LRs(Q(RctW))等效电路模型进行了拟合

结果显示随着温度由10℃上升至40℃

电化学阻抗Rct 值由4.192 W·cm2降低到0.5321 W·cm2

表明温度上升可以显著降低电对在石墨电极上的电化学反应阻抗。动电位测试结果发现Ti(Ⅲ)/Ti(Ⅳ)的平衡电位随温度上升发生正方向的偏移

可能是由于温度上升使得Ti在HCl溶液中的形态发生变化;交换电流也随温度上升而增加是由于温度上升有促进电极表面电化学反应的电荷传递。各种电化学测试结果显示TiCl3的HCl水溶液是一种有应用前景的液流电池负极电解液。

Abstract

In this study

electrochemical performance of titanium-trichloride-hydrochloride acid aqueous solution was investiageted. Cyclic voltammetry(CV)

electrochemical impedance Spectroscopy (EIS) and potentiodynamic polarization curve tests were applied to study the electrochemical dynamics of Ti3+/Ti2+ such as reversibility and intrinsic mechanism at various temperatures. The CV results show that the oxide and reduce peak currents of Ti3+/Ti2+ couples increase with increasing temperature and the electrochemical reversibility become better as well. The EIS measured data were simulated by the LRs(Q(RctW)) equivalent circuit model

and the results indicate that reaction impedance reduced sharply from 4.192 W ·cm2 to 0.5321 W·cm2 with the temperature increasing from 10℃ to 40℃. The potentiodynamic polarization curve results show the equilibrium potential shifted towards positively promoting negative electrolyte alternative for titanium based redox flow battery.

关键词

Keywords

references

Views

273

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Research progress on the H+/Zn2+ interfacial transport regulation and reaction mechanisms in aqueous Zn/MnO2 system

Synthesis of a high-efficacy medium-entropy alloy catalyst via the recycling of spent batteries and its subsequent performance evaluation

Effect of electrolyte types on the storage behaviors of anions and cations for dual-ion batteries

Exploration and optimization of extraction process of bromine from underground brine by electrooxidation

Electrochemically reductive dechlorination of six dichlorophenol isomers:comparison of apparent kinetics

Related Author

CAO Lei

XU Zixiao

XU Chenxuan

SHAO Zhuo

JI Shiyu

GUO Shan

TIAN Yu

XU Yongbin

Related Institution

PowerChina Huadong Engineering Corporation Limited

College of Electromechanical Engineering, Qingdao University of Science & Technology

School of Chemical Engineering, Dalian University of Technology

National-Local Joint Engineering Laboratory of Chemical Energy Saving Process Integration and Resource Utilization, School of Chemical Engineering and Technology, Hebei University of Technology

Engineering Research Center of Seawater Utilization of Ministry of Education, School of Chemical Engineering and Technology, Hebei University of Technology

⁰