Novel mixed matrix composite membranes containing MCM-41 for CO<sub>2</sub> separation

HE Yupeng; WANG Zhi; QIAO Zhihua; YUAN Shuangjie; WANG Jixiao

doi:10.11949/j.issn.0438-1157.20150257

您当前的位置：

首页 >

文章列表页 >

Novel mixed matrix composite membranes containing MCM-41 for CO₂ separation

更新时间：2025-12-10

- Novel mixed matrix composite membranes containing MCM-41 for CO₂ separation
- CIESC Journal Issue 10, Pages: 3979-3990(2015)
- 作者机构：
  
  1. 天津大学化工学院化学工程研究所, 天津化学化工协同创新中心, 化学工程联合国家重点实验室天津大学, 天津市膜科学与海水淡化技术重点实验室,天津,300072
  2. 中国石油天然气管道工程有限公司,河北,廊坊,065000
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20150257
  CLC： Q028.8
- Online First：05 October 2015，
  
  Published：05 October 2015
- 稿件说明：
移动端阅览
HE Yupeng, WANG Zhi, QIAO Zhihua, et al. Novel mixed matrix composite membranes containing MCM-41 for CO₂ separation[J]. CIESC Journal, 2015, (10): 3979-3990. DOI: 10.11949/j.issn.0438-1157.20150257.
DOI：

HE Yupeng, WANG Zhi, QIAO Zhihua, et al. Novel mixed matrix composite membranes containing MCM-41 for CO₂ separation[J]. CIESC Journal, 2015, (10): 3979-3990. DOI: 10.11949/j.issn.0438-1157.20150257. DOI：

摘要

为了提高CO2分离膜的性能

将接枝了氨基的MCM-41分子筛(MCM-NH2)添加到聚乙烯基胺(PVAm)水溶液中配制涂膜液

并将PVAm-MCM-NH2涂膜液涂覆到聚砜(PSf)超滤膜上制备PVAm-MCM-NH2/PSf混合基质复合膜。复合膜分离层较薄

有利于CO2渗透速率的提高。接枝的胺基提高了分子筛与聚合物的相容性和膜内胺基含量

有利于膜渗透选择性能的提高。使用CO2/N2混合气(15% CO2 + 85% N2

体积分数)考察了不同MCM-NH2添加量的PVAm-MCM-NH2/PSf膜的渗透选择性能。当涂膜液中mMCM-NH2/mPVAm为0.2、湿涂层厚度为50 μm

测试温度为22℃ 、进料气压力为0.11 MPa时

膜的CO2渗透速率可达4.66×10-7 mol·m-2·s-1·Pa-1

CO2/N2分离因子可达150。较高的CO2/N2分离性能表明PVAm-MCM-NH2/PSf膜在烟道气碳捕集领域具有良好的应用前景。此外

考察了湿涂层厚度、热处理、添加小分子胺等条件对膜渗透选择性能的影响。

Abstract

To improve the performance of CO2 separation membrane

MCM-41 modified by amines (MCM-NH2) was filled into polyvinylamine (PVAm) aqueous solution to fabricate PVAm-MCM-NH2 coating solutions. PVAm-MCM-NH2/polysulfone (PSf) mixed matrix composite membranes were prepared by coating PVAm-MCM-NH2 solutions on PSf ultrafiltration membranes. The separation layer of the composite membrane was very thin

which benefited the improvement of CO2 permeance. The amine groups grafted to MCM-41 facilitated the transport of CO2 through reversible reaction and simultaneously improved the filler-polymer interface compatibility. The separation performance of PVAm-MCM-NH2/PSf membranes with different MCM-NH2 content was tested using CO2/N2 mixed gas (15% (vol) CO2 + 85%(vol) N2). When mMCM-NH2/mPVAm in the coating solution was 0.2 at testing temperature of 22℃ and feed gas pressure of 0.11 MPa

the composite membrane exhibited a CO2 permeance of 4.66×10-7 mol·m-2·s-1·Pa-1 and a CO2/N2 selectivity of 150. The high-performance PVAm-MCM-NH2/PSf membrane showed promising applications in CO2 capture from flue gas. Moreover

the effects of the wet coating thickness

the heat treatment and the introduction of the small molecule amines on the separation performance of PVAm-MCM-NH2/PSf membrane were investigated. The results indicated that the increase of wet coating thickness (from 50 μm to 100 μm) with heat treatment under 80℃ or the introduction of ethanediamine would lead to the improvement of the pressure stability

but the loss of CO2/N2 separation performance under low pressures.

关键词

Keywords

references

Views

427

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Simulation, experimentation and analyzation of vacuum pressure swing adsorption process for CO2 capture from dry flue gas

CO2 enrichment characteristics of coal/biomass fluidized oxy-fuel combustion

Absorption performance and stratification mechanism of biphasic CO2 absorbent[Bmim] [BF4]/MEA aqueous mixtures

Chemical looping technology for clean and highly efficient coal processes

Chemical looping combustion of coal in a two-stage fuel reactor

Related Author

YAN Haiyu

FU Qiang

ZHOU Yan

LI Dongdong

ZHANG Donghui

LIU Qinwen

ZHONG Wenqi

LIU Xuejiao

Related Institution

State Key Laboratory of Chemical Engineering, School of Chemical Engineering and Technology, Tianjin University

Key Laboratory of Energy Thermal Conversion and Control of Ministry of Education, School of Energy and Environment, Southeast University

Department of Chemical Engineering, Monash University, Clayton Vic

CSIRO Manufacturing, Clayton

Key Laboratory for Thermal Science and Power Engineering of Ministry of Education, Beijing Engineering Research Center for Ecological Restoration and Carbon Fixation of Saline-Alkaline and Desert Land, Department of Energy and Power Engineering, Tsinghua University

⁰

Novel mixed matrix composite membranes containing MCM-41 for CO2 separation

DOI：10.11949/j.issn.0438-1157.20150257

摘要

Abstract

关键词

Keywords

references

Novel mixed matrix composite membranes containing MCM-41 for CO₂ separation