Effect of soluble phosphorus on high-strength α-hemihydrate gypsum prepared by atmospheric hydrothermal method

RU Xiaohong; LI Haitao; ZHANG Xin'ai; MA Baoguo; LU Siwen

doi:10.11949/j.issn.0438-1157.20141449

您当前的位置：

首页 >

文章列表页 >

Effect of soluble phosphorus on high-strength α-hemihydrate gypsum prepared by atmospheric hydrothermal method

更新时间：2025-12-10

- Effect of soluble phosphorus on high-strength α-hemihydrate gypsum prepared by atmospheric hydrothermal method
- CIESC Journal Issue 5, Pages: 1983-1988(2015)
- 作者机构：
  
  1. 洛阳理工学院材料科学与工程系,河南,洛阳,471023
  2. 武汉理工大学硅酸盐建筑材料国家重点实验室,湖北,武汉,430070
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20141449
  CLC： Q177.3
- Online First：05 May 2015，
  
  Published：05 May 2015
- 稿件说明：
移动端阅览
RU Xiaohong, LI Haitao, ZHANG Xin'ai, et al. Effect of soluble phosphorus on high-strength α-hemihydrate gypsum prepared by atmospheric hydrothermal method[J]. CIESC Journal, 2015, (5): 1983-1988.
DOI：

RU Xiaohong, LI Haitao, ZHANG Xin'ai, et al. Effect of soluble phosphorus on high-strength α-hemihydrate gypsum prepared by atmospheric hydrothermal method[J]. CIESC Journal, 2015, (5): 1983-1988. DOI： 10.11949/j.issn.0438-1157.20141449.

摘要

研究了水热CaCl2溶液中可溶磷对CaSO4·2H2O脱水形成α-半水石膏相以及晶形调控的影响

并从高强α-半水石膏相的晶体生长角度探讨了可溶磷的作用机理。结果表明:在98℃ 24%的水热CaCl2溶液中

pH 的大小是决定二水石膏能否发生脱水相变反应形成α-半水石膏的主要因素;当pH不超过2.0时

可以得到针状的α-半水石膏

加入多元羧酸类媒晶剂NS后

可以得到长径比0.5～3.0的短柱状高强α-半水石膏

抗压强度超过20 MPa;可溶磷的存在可以降低体系的pH

增大α-半水石膏的过饱和度

降低晶体与液相界面的表面自由能

有利于α-HH相的形成;另一方面

酸根离子会影响到α-HH的结晶习性

减弱羧酸类媒晶剂的吸附效果。

Abstract

The effect of soluble phosphorus on CaSO4·2H2O (DH) dehydration to α-calcium sulfate hemihydrate gypsum (α-HH) in hydrothermal CaCl2 solutions and the crystal shape regulation were investigated. The action mechanism of soluble phosphorus was studied by means of growth of hemihydrate crystal. The system pH was the main factor to determine whether DH could be dehydrated to α-HH in 24% CaCl2 solution at 98℃. Acicular a-HH crystal could be obtained when pH was less than 2.0. High-strength α-HH crystal with aspect ratios from 0.5 to 3.0 could be observed when polycarboxylic crystal habit modifier NS was added. The corresponding compressive strength was more than 20 MPa. The presence of soluble phosphorus was favorable for α-HH formation by lowering system pH

increasing supersaturation degree and reducing interfacial energy. On the other hand

acid radical ions affected α-HH crystallization behavior and adsorption results of medium crystal agent NS.

关键词

Keywords

references

Views

219

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Preparation and performance study of incinerated slag based shape-stable phase change composites

Study on preparation and thermal properties of carbonates composite heat storage materials

Supercooling characteristics of inorganic phase change material CaCl2·6H2O

Improving phase change thermal properties of quaternary bromides by adding SiO2 nanoparticle

Preparation and electrochemical lithium storage properties of Na0.44MnO2 nanorods/graphene cathode

Related Author

Chaoyu SONG

Yaxuan XIONG

Jinhua ZHANG

Yuhe JIN

Chenhua YAO

Huixiang WANG

Yulong DING

SANG Lixia

Related Institution

Beijing Key Laboratory of Heating, Gas Supply, Ventilating and Air Conditioning Engineering, School of Environmental and Energy Engineering, Beijing University of Civil Engineering and Architecture

Beijing Building Research Institute Co., Ltd. of CSCEC

Birmingham Center for Energy Storage, University of Birmingham

Key Laboratory of Enhanced Heat Transfer and Energy Conservation, Ministry of Education and Key Laboratory of Heat Transfer and Energy Conversion of Beijing Municipality, College of Environmental and Energy Engineering, Beijing University of Technology

Technical Institute of Physics and Chemistry, Chinese Academy of Sciences

⁰