Preparation of nano TiO<sub>2</sub> from Ti-bearing blast furnace slag by molten salt method

LI Xin; YU Honghao; ZHANG Houfang; XUE Xiangxin

doi:10.11949/j.issn.0438-1157.20141029

您当前的位置：

首页 >

文章列表页 >

Preparation of nano TiO₂ from Ti-bearing blast furnace slag by molten salt method

更新时间：2025-12-10

- Preparation of nano TiO₂ from Ti-bearing blast furnace slag by molten salt method
- CIESC Journal Issue 2, Pages: 827-833(2015)
- 作者机构：
  
  1. 沈阳理工大学材料科学与工程学院,辽宁,沈阳,110159
  2. 东北大学冶金资源与生态环境研究所,辽宁,沈阳,110819
  3. 辽宁省冶金资源循环科学重点实验室,辽宁,沈阳,110819
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20141029
  CLC： Q110.2
- Online First：05 February 2015，
  
  Published：05 February 2015
- 稿件说明：
移动端阅览
LI Xin, YU Honghao, ZHANG Houfang, et al. Preparation of nano TiO₂ from Ti-bearing blast furnace slag by molten salt method[J]. CIESC Journal, 2015, (2): 827-833. DOI: 10.11949/j.issn.0438-1157.20141029.
DOI：

LI Xin, YU Honghao, ZHANG Houfang, et al. Preparation of nano TiO₂ from Ti-bearing blast furnace slag by molten salt method[J]. CIESC Journal, 2015, (2): 827-833. DOI: 10.11949/j.issn.0438-1157.20141029. DOI：

摘要

采用熔盐法对含钛高炉渣进行高效分解并提取含钛组分

利用含钛滤液为原料制备了纳米二氧化钛粉体。对熔盐分解含钛高炉渣进行了热力学分析

并研究了碱渣比、熔盐反应温度及熔盐反应时间对钛组分浸出率的影响和pH及水解温度对二氧化钛产品纯度的影响。实验结果表明高炉钛渣在氢氧化钠熔盐中反应生成钛酸钠在热力学上是可行的。确定了最佳的碱渣比为3:1

最佳熔盐反应温度为500℃

最佳反应时间为3 h

在此条件下钛元素的浸出率为99.8%。得出较佳的水解pH范围为0.1～0.2

最佳水解温度为100℃。实验中制备的纳米二氧化钛粒子球形度好

粒度大小均匀且分散性好

颗粒直径为100 nm左右。

Abstract

A novel process was proposed for preparing titanium dioxide by decomposition of titanium-bearing blast furnace slag (TBBFS) in molten NaOH-NaF system. Thermodynamic analysis was conducted on the molten salt decomposition of TBBFS. The effects of mass ratio of alkali and slag

reaction time and reaction temperature on titanium extraction and the effects of pH and hydrolysis temperature on purity of titanium dioxide were discussed. The reaction of sodium titanate from TBBFS with sodium hydroxide was feasible thermodynamically. When optimum mass ratio of alkali and slag was 3:1

reaction temperature was 500℃

and reaction time was 3 h

titanium extraction was 99.8%. Optimum pH and hydrolysis temperature were 0.1—0.2 and 100℃ respectively. Analysis results indicated good sphericity and dispersibility of TiO2 particles with diameter about 100 nm.

关键词

Keywords

references

Views

407

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Au/TiO2-B catalyst for low-temperature CO oxidation

Thermodynamic study of germanium-impurity competitive deposition in GeCl4-MxCly-H2 system

Thermodynamic performance of tower-type solar-assisted supercritical compression CO2 energy storage system

Optimization method of coal-based cooling, heating and power co-generation

Research on aluminum oxide nanofluid liquid cooling battery thermal management performance

Related Author

WANG Xibing

JI Tuo

LI Licheng

YANG Zhuhong

LU Xiaohua

LIU Qihong

CHEN Fengyang

LYU Qinghui

Related Institution

State Key Laboratory of Materials-Oriented Chemical Engineering, Nanjing Tech University

School of Chemical Engineering, Nanjing Forestry University

State Key Laboratory of Complex Nonferrous Metal Resources Clean Utilization, School of Metallurgical and Energy Engineering, Kunming University of Science and Technology

State Key Laboratory of Advanced Metallurgy for Non-ferrous Metals, Kunming Metallurgical Research Institute Co., Ltd.

School of Energy and Power Engineering, Lanzhou University of Technology

⁰

Preparation of nano TiO2 from Ti-bearing blast furnace slag by molten salt method

DOI：10.11949/j.issn.0438-1157.20141029

摘要

Abstract

关键词

Keywords

references

Preparation of nano TiO₂ from Ti-bearing blast furnace slag by molten salt method