Synthesis, characterization of single benzoxazine contained bis-DOPO based on bisphenol A and flame retardant performance of its copolymer with epoxy

LIU Jianhua; SHI Tiejun; LI Ming; XU Guomei; WANG Quan; YU Fu

doi:10.11949/j.issn.0438-1157.20141028

您当前的位置：

首页 >

文章列表页 >

Synthesis, characterization of single benzoxazine contained bis-DOPO based on bisphenol A and flame retardant performance of its copolymer with epoxy

更新时间：2025-12-10

- Synthesis, characterization of single benzoxazine contained bis-DOPO based on bisphenol A and flame retardant performance of its copolymer with epoxy
- CIESC Journal Issue 2, Pages: 820-826(2015)
- 作者机构：
  
  合肥工业大学化工学院,安徽,合肥,230009
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20141028
  CLC： 631
- Online First：05 February 2015，
  
  Published：05 February 2015
- 稿件说明：
移动端阅览
LIU Jianhua, SHI Tiejun, LI Ming, et al. Synthesis, characterization of single benzoxazine contained bis-DOPO based on bisphenol A and flame retardant performance of its copolymer with epoxy[J]. CIESC Journal, 2015, (2): 820-826.
DOI：

LIU Jianhua, SHI Tiejun, LI Ming, et al. Synthesis, characterization of single benzoxazine contained bis-DOPO based on bisphenol A and flame retardant performance of its copolymer with epoxy[J]. CIESC Journal, 2015, (2): 820-826. DOI： 10.11949/j.issn.0438-1157.20141028.

摘要

以含双DOPO-双酚A、苯胺和多聚甲醛为原料

合成了含双DOPO的双酚A-单苯并(口恶)嗪(1DD)。采用红外、核磁(氢谱核磁和碳谱核磁)等分析手段对1DD的化学结构进行了表征;采用DSC对1DD的固化特性进行研究

使用TG分析了所得聚苯并(口恶)嗪的热稳定性。再将1DD与环氧树脂以0.5/1的质量比进行共混

按照一定的程序进行升温固化

得到共聚物P1DD-ER。采用UL94垂直燃烧实验、极限氧指数仪(LOI)测试了共聚物的阻燃性能。结果表明:含双DOPO的双酚A-单苯并(口恶)嗪树脂的起始熔点约为185℃

在222℃处有一个很明显的放热峰。固化后的树脂从348℃开始分解

在463℃分解速率达到最快

在800℃时的残碳率为35.78%。制备的苯并(口恶)嗪可以用作环氧树脂的固化剂

且其共聚物具有很好的阻燃性能

LOI可以达到37

UL94等级为V-0。

Abstract

Single benzoxazine contained bis DOPO based on bisphenol A (1DD) was synthesized from bisphenol A contained double DOPO (2DO)

aniline and paraformaldehyde. FTIR

NMR(1H NMR

13C NMR) were used to characterize chemical structure of 1DD. Curing characteristics were studied with DSC and thermostability was studied with TG. The product was blended with epoxy resin with mass ratio 0.5/1 according to a specific procedure for heat curing to prepare copolymer P1DD-ER. Flame retardant properties of the copolymer was investigated with the UL94 vertical burning test and limit oxygen index (LOI). Starting melting point of 1DD was nearly 185℃. An obvious exothermic peak was observeed at 222℃. Initial decomposition temperature of the copolymer after curing was 348℃. The fastest speed of decomposition was recorded at 463℃. Carbon residue at 800℃ was 35.78%. The prepared benzoxazine could be used as the curing agent of epoxy resin. The copolymer had good flame retardant performance. LOI could reach 37. The grade of UL94 was V-0.

关键词

Keywords

references

Views

729

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Synthesis, characterization and curing characteristics of double benzoxazine contained double DOPO based on bisphenol A

Synthesis, characterization and curing characteristics of single benzoxazine containing DOPO based on bisphenol A

Preparation and properties of norbornene-imide-functionalized bis-benzoxazine

Fabrication and characterization of a novel bismaleimide-benzoxazine resin

Synthesis, characterization and application of sulfonic acid type water-based polyurethane chain extender

Related Author

XU Guomei

WANG Qidong

YUAN Wei

SHI Tiejun

QIAN Ying

CHEN Yang

YUAN Wei

SHI Tiejun

Related Institution

Department of Materials and Chemical Engineering, West Anhui University

School of Chemistry and Chemical Engineering, Hefei University of Technology

School of Chemical Engineering, Hefei University of Technology

School of Resource and Environment, Shaanxi University of Science and Technology

Shaanxi Research Institute of Agricultural Products Processing Technology

⁰