Hybrid supercapacitor with nanosized α-MnO2/activated carbon as electrodes

WANG Xingyan; WANG Xianyou; HOU Tianlan; LI Jun; HUANG Qinghua

您当前的位置：

首页 >

文章列表页 >

Hybrid supercapacitor with nanosized α-MnO2/activated carbon as electrodes

更新时间：2026-03-26

- Hybrid supercapacitor with nanosized α-MnO2/activated carbon as electrodes
- CIESC Journal Vol. 57, Issue 2, (2006)
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Online First：25 February 2006，
  
  Published：2006
- 稿件说明：
移动端阅览
WANG Xingyan, WANG Xianyou, HOU Tianlan, et al. Hybrid supercapacitor with nanosized α-MnO2/activated carbon as electrodes[J]. CIESC Journal, 2006, 57(2).
DOI：

WANG Xingyan, WANG Xianyou, HOU Tianlan, et al. Hybrid supercapacitor with nanosized α-MnO2/activated carbon as electrodes[J]. CIESC Journal, 2006, 57(2). DOI：

摘要

研究了以纳米α-MnO2和活性炭（AC）为电极材料的超级电容器，分别对纳米α-MnO2的制备、电解液浓度的影响进行了研究，组装了MnO2/KOH/MnO2、AC/KOH/AC、MnO2/KOH/AC三种类型的模拟电容器，用循环伏安、恒流充放电、自放电以及时间常数法对电极和电容器进行性能测试，发现当电解液KOH浓度为7 mol8226;L-1时，混合超级电容器性能最佳，α-MnO2单电极比电容可达237 F8226;g-1，混合电容器工作电压高达1.5 V，并且具有良好的大电流放电性能和较好的循环寿命，实验还表明混合超级电容器具有极低的自放电率.

Abstract

The supercapacitor using nanosized α-MnO2 and activated carbon as electrode materials was developed

and the synthesization of nanosized α-MnO2 and the effect of the concentration of electrolyte on the performance were studied in detail. Three kinds of supercapacitors

MnO2/KOH/MnO2

AC/KOH/AC and MnO2/KOH/AC

were prepared. Cyclic voltammetry (CV)

galvanostatic charge-discharge and time constant technology were used to study the performance of the electrodes and the supercapacitors. The results showed that excellent performance of the electrods was found when the concentration of KOH solution was 7 mol8226;L-1.Specific capacitance of α-MnO2 could reach a value of 237 F8226;g-1.The super-capacitors with AC electrode as negative electrode and asymmetric configuration had better characteristics than the ones composed of two identical AC or MnO2 electrodes. The operating voltage of α-MnO2/KOH/AC hybrid super-capacitor was 1.5 V and had low self-discharge rate.

关键词

Keywords

references

Views

783

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Engineering verification and NO emission control of rare earth Y2O3-based catalytic coatings on a metal fiber surface burner

The impact of novel flow channel structure with sudden-expansion ratio on seawater-activated battery

Progress of solar photo-thermo-catalysis for ammonia synthesis and decomposition under mild conditions

Study on entropy wave production and dissipation in partially premixed swirl flames subject to inlet perturbations

Corrosion health status assessment method for refining unit pipeline based on GLAE-MLP

Related Author

No data

Related Institution

No data

⁰