Ultrasonic Degradation of Polyvinyl Alcohol and Copolymerization of PVA with Acrylonitrile

沈埜; 陈克强; 王琪; 李惠林; 徐僖

您当前的位置：

首页 >

文章列表页 >

Ultrasonic Degradation of Polyvinyl Alcohol and Copolymerization of PVA with Acrylonitrile

更新时间：2025-12-16

- Ultrasonic Degradation of Polyvinyl Alcohol and Copolymerization of PVA with Acrylonitrile
- CIESC Journal Issue 4, (1988)
- 作者机构：
  
  成都科技大学高分子研究所,成都科技大学高分子研究所,成都科技大学高分子研究所,成都科技大学高分子研究所,成都科技大学高分子研究所 ,成都,成都,成都,成都,成都
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Online First：25 August 1988，
  
  Published：25 August 1988
- 稿件说明：
移动端阅览
沈埜, 陈克强, 王琪, et al. Ultrasonic Degradation of Polyvinyl Alcohol and Copolymerization of PVA with Acrylonitrile[J]. CIESC Journal, 1988, (4).
DOI：

沈埜, 陈克强, 王琪, et al. Ultrasonic Degradation of Polyvinyl Alcohol and Copolymerization of PVA with Acrylonitrile[J]. CIESC Journal, 1988, (4). DOI：

摘要

本文研究了超声波辐照下聚乙烯醇(PVA)在水溶液中的降解规律

结果表明PVA在水溶液中的超声降解速率遵循Baramboim动力学方程.本文还研究了丙烯腈(AN)与PVA在水溶液中的超声波辐照共聚反应.改变超声辐照时间或溶液中AN的量

可得到水溶性和水不溶性两类共聚物.用IR、MS、PGC和X-射线衍射研究了共聚物的结构

证明所得产物主要为嵌段共聚物.在2%的PVA/AN(1/1.6

质量比)水溶液中

以频率为21.5kHz、声强为490W的超声波在20±1℃下辐照28min

水溶性共聚物产率[共聚物产率=(共聚物重/PVA加入量)×100%〕为25.49%

共聚物中AN含量为13.98%;在相同条件下

对2%的PVA/AN(1/4

质量比)水溶液

辐照100min

水不溶性共聚物产率为296.01%

共聚物中AN含量为75.56%.

Abstract

The ultrasonic degradation of polyvinyl alcohol (PVA) in aqueous solution and the copolymerization of PVA with acrylonitrile (AN) were studied. It was confirmed that the rate of degradation of PVA followed the kinetic equation suggested by N. K. Baramboim. Both water-soluble and water-insoluble copoly-mers could be obtained by changing the irradiation time or the amount of AN added to the aqueous solution of PVA. The structure of the copolymer was identified by IR

PGC and X-ray diffraction. The copolymer prepared was mainly a blocked one. By irradiating 2% PVA/AN (1/1.6

by mass) at 20±1℃ and 21.5 kHz with 490W for a period of 28 min.

the yield of the water-soluble copolymer was 25.49%

with a AN content of 13.98%. When the irradiating period was extended to 100 min.

with the mass ratio between PVA and AN at 1/4

the yield of the water-insoluble copolymer amounted to 296.01%

with a AN content 75.56%.

关键词

Keywords

references

Views

162

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Engineering verification and NO emission control of rare earth Y2O3-based catalytic coatings on a metal fiber surface burner

Methods of adaptive prediction and abnormal states traceability for sulphur content in flue gas desulfurization process

Study on performance enhancement and cold retention characteristics of solid packed bed cold energy storage

Mechanism and regulation of supercooling behavior in imidazolium-based ionic liquids

Effect of belt structure design on the vulcanization characteristics of all-steel radial tires

Related Author

No data

Related Institution

No data

⁰