Studies on Ultrasonic Degradation of Methyl Cellulose and Its Copolymerization with Acrylonitrile

更新时间：2025-12-16

- Studies on Ultrasonic Degradation of Methyl Cellulose and Its Copolymerization with Acrylonitrile
- CIESC Journal Issue 3, (1987)
- 作者机构：
  
  成都科技大学高分子研究所,成都科技大学高分子研究所,成都科技大学高分子研究所
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Online First：25 September 1987，
  
  Published：25 September 1987
- 稿件说明：
移动端阅览
宫晓颐, 陈克强, 徐僖. Studies on Ultrasonic Degradation of Methyl Cellulose and Its Copolymerization with Acrylonitrile[J]. CIESC Journal, 1987, (3).
DOI：

宫晓颐, 陈克强, 徐僖. Studies on Ultrasonic Degradation of Methyl Cellulose and Its Copolymerization with Acrylonitrile[J]. CIESC Journal, 1987, (3). DOI：

摘要

本文研究了水溶液中甲基纤维素的超声波辐照降解反应

证实该反应具有一般的力降解特征

发现降解速率不是辐照时间的单调增函数.以水/甲酸为溶剂

在超声波辐照下制得了甲基纤维素-丙烯腈共聚物

考察了共聚过程

提供了获得水溶性共聚物的反应条件.证实所得共聚物是接枝

嵌段兼有的共聚物

共聚点主要发生在甲氧基上

共聚物是非晶态的.初步研究了共聚产物水溶液的热稳定性和抗盐性

与甲基纤维素对比

这些性能均有改善.

Abstract

The ultrasonic degradation reactions of methyl cellulose (MC) in its aqueous solution under different conditions were studied. It was found that the degradation reactions are of a mechanochemical nature and the degradation rate is not an increasing function of irradiating time. The ultrasonic irradiation of MC and acrylonitrile (AN) in H2O/HCOOH resulted in a copolymer of MC and AN. A method for preparing the water-soluble copolymer was suggested. The copolymer is both block and graft with joints mainly located on methoxy groups of MC. This was elucidated by the character of the copolymerization reaction and by analysing the copolymer structure with the help of DTA

PGC and MS.The state of molecular aggregation of the copolymer was identified by XRD and SEM. The surface activety

thermostability

and resistance to salt in the aqueous solution of the copolymerization product were examined. They were found to be better than those of MCs.

关键词

Keywords

references

Views

403

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Optimization of heat storage and release cycle performance of Ca(OH)2/CaO indirect reactor

Identification of gas-liquid two-phase flow patterns in a riser based on recursive characteristics and CNN

Study on synergistic modification of nitrogen-doped carbon coating and Ti⁴⁺ co-doping for lithium vanadium phosphate cathode materials

Thermo-oxidative degradation characteristics of TPT backsheet from end-of-life photovoltaic modules

Methods of adaptive prediction and abnormal states traceability for sulphur content in flue gas desulfurization process

Related Author

No data

Related Institution

No data

⁰