Ultrasonic Degradation and Copolymerizationof Polyvinyl Acetate with PartiallyHydrolyzed Polyacrylamide

Cao Zhiqiang and Xu Xi(Polymer Research Institute; Chengdu University of Science and Technology)

您当前的位置：

首页 >

文章列表页 >

Ultrasonic Degradation and Copolymerizationof Polyvinyl Acetate with PartiallyHydrolyzed Polyacrylamide

更新时间：2025-12-16

- Ultrasonic Degradation and Copolymerizationof Polyvinyl Acetate with PartiallyHydrolyzed Polyacrylamide
- CIESC Journal Issue 1, (1985)
- 作者机构：
  
  成都科技大学高分子研究所,成都科技大学高分子研究所
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Online First：25 March 1985，
  
  Published：25 March 1985
- 稿件说明：
移动端阅览
Cao Zhiqiang and Xu Xi(Polymer Research Institute, Chengdu University of Science and Technology). Ultrasonic Degradation and Copolymerizationof Polyvinyl Acetate with PartiallyHydrolyzed Polyacrylamide[J]. CIESC Journal, 1985, (1).
DOI：

Cao Zhiqiang and Xu Xi(Polymer Research Institute, Chengdu University of Science and Technology). Ultrasonic Degradation and Copolymerizationof Polyvinyl Acetate with PartiallyHydrolyzed Polyacrylamide[J]. CIESC Journal, 1985, (1). DOI：

摘要

本文分别研究了在超声波辐照作用下聚乙酸乙烯酯(PVAc)和部分水解聚丙烯酰胺(HPAM)在乙醇/水(55/45)中的降解和两者的嵌段共聚反应.结果表明:PVAc的降解速率大致可以用Ovenall方程表示

而HPAM的偏离较大.在25℃、频率为18.2kHz、逆变器主回路输入电流为2.4A的超声强度下

将浓度为0.50%的PVAc/HPAM(1/1)乙醇/水(55/45)溶液辐照10分钟

所得共聚物产率为4.3%.通过溶解试验、电子显微镜、相差显微镜、元素分析、IR和NMR分析了共聚物的结构

证明该共聚物主要为嵌段体.

Abstract

The ultrasonic degradation and copolymerization of polyvinyl acetate (PVAc) with partially hydrolyzed polyacrylamide (HPAM) in ethanol/water (55/45) have been studied. The experimental results showed that the rate of degradation of PVAc follows Ovenalls equation approximately and that of HPAM deviates from the equation. The effects of the ultrasonic intensity and reaction temperature on the rates of degradation are the same. By irradiating 0.50% PVAc/HPAM (1/1 by weight) at 25℃ by ultrasound of 18.2 kHz with 2.4 A imput current on reversed main circuit for a period of 10 min

the yield of copolymer amounted to 4.3%. Its structure was identified by means of solubility test

NMR

element analysis

electron microscope and phase contrast microscope

and the copolymer was proved to be mainly a block one.

关键词

Keywords

references

Views

166

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Study on performance enhancement and cold retention characteristics of solid packed bed cold energy storage

Analysis of flow field characteristics and mixing performance of different SK-type static mixers

New universal corresponding state equation for correlation and extrapolation of saturated vapor-liquid density

Multi objective optimization of flow and heat transfer characteristics of modified manifold microchannel heat sink based on machine learning

Study on dissolution kinetics of erythromycin thiocyanate

Related Author

No data

Related Institution

No data

⁰