REVERSION AND CHEMICAL STRESS RELAXATION BEHAVIOUR OF NR CURED WITH EC

孟宪德; 王名东; 纪奎江; 马培瑜

您当前的位置：

首页 >

文章列表页 >

REVERSION AND CHEMICAL STRESS RELAXATION BEHAVIOUR OF NR CURED WITH EC

更新时间：2025-12-16

- REVERSION AND CHEMICAL STRESS RELAXATION BEHAVIOUR OF NR CURED WITH EC
- CIESC Journal Issue 6, (1995)
- 作者机构：
  
  1. 青岛化工学院橡胶工程学院!青岛266042,青岛化工学院橡胶工程学院,青岛,266042
  2. 化工部北京橡胶研究设计院,青岛化工学院橡胶工程学院!青岛266042,化工部海洋涂料研究所,青岛,266071
- 作者简介：
- 基金信息：
- DOI：
  CLC： Q331
- Online First：25 December 1995，
  
  Published：25 December 1995
- 稿件说明：
移动端阅览
孟宪德, 王名东, 纪奎江, et al. REVERSION AND CHEMICAL STRESS RELAXATION BEHAVIOUR OF NR CURED WITH EC[J]. CIESC Journal, 1995, (6).
DOI：

孟宪德, 王名东, 纪奎江, et al. REVERSION AND CHEMICAL STRESS RELAXATION BEHAVIOUR OF NR CURED WITH EC[J]. CIESC Journal, 1995, (6). DOI：

摘要

WOlff’‘

”采用双（3-三乙氧基甲硅烷基丙基）-四硫化物（St69）与硫黄组成的平衡硫化体系（EC）

既减少了硫化返原的产生

又保留了传统硫黄硫化体系（CV）的优点

同时克服了因采用有效硫化体系（EV）或半有效硫化体系（SEV）所导致的强度等

Abstract

The reversion and chemical stress relaxation behaviour of natural rubber (NR) cured with equilibrium cure system (EC) were studied. The results manifested that the reversion and tensile strength decrease percentage of NR cured with EC after 6 hour were remarkably lower than that of NR cured with conventional vulcanization system (CV). The order of the amount of crosslinking bonds was EC>CV>SEV(semi -effective vulcanization system) during the process of chemical stress relaxation. The thermooxidative aging activation energy values of NR cured with EC

SEV and CV were 159. 5

141. 7 and 114. 6kJ/mol

and their tensile strength values were 26. 9

21. 6 and 24. 7MPa respectively. It could be inferred that one of the main reasons of lower reversion beyond 100 minute curing period was that the vul-canizate cured with EC had a good property of thermooxidative aging resistance.

关键词

Keywords

references

Views

217

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Recent advances and perspectives on sulfide-based photocatalysts for hydrogen production

Mechanism and regulation of supercooling behavior in imidazolium-based ionic liquids

Exothermic characteristics of energy carrier for calcium looping thermo-chemical energy storage

Controlled synthesis of Bi2MoO6/MoO3 composite fibers via in-situ hydrothermal method and their high-efficiency photocatalytic hydrogen production performance

Progress in research of selective oxidation of low carbon polyols over nano-Au catalysts with precise electronic effect regulation

Related Author

No data

Related Institution

No data

⁰