ELECTROCHEMICAL BEHAVIOURS INSIDE STRESS CORROSION CRACKS OF 1Cr13 STAINLESS STEEL

刘幼平; 迟芳; 左景伊

您当前的位置：

首页 >

文章列表页 >

ELECTROCHEMICAL BEHAVIOURS INSIDE STRESS CORROSION CRACKS OF 1Cr13 STAINLESS STEEL

更新时间：2025-12-16

- ELECTROCHEMICAL BEHAVIOURS INSIDE STRESS CORROSION CRACKS OF 1Cr13 STAINLESS STEEL
- CIESC Journal Issue 5, (1993)
- 作者机构：
  
  北京化工学院应用化学系,北京化工学院应用化学系,北京化工学院应用化学系北京100029,北京100029,北京,100029
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Online First：25 October 1993，
  
  Published：25 October 1993
- 稿件说明：
移动端阅览
刘幼平, 迟芳, 左景伊. ELECTROCHEMICAL BEHAVIOURS INSIDE STRESS CORROSION CRACKS OF 1Cr13 STAINLESS STEEL[J]. CIESC Journal, 1993, (5).
DOI：

刘幼平, 迟芳, 左景伊. ELECTROCHEMICAL BEHAVIOURS INSIDE STRESS CORROSION CRACKS OF 1Cr13 STAINLESS STEEL[J]. CIESC Journal, 1993, (5). DOI：

摘要

模拟1Cr13不锈钢在0.5mol/L NaCl溶液中应力腐蚀裂缝尖端的环境变化和受力状态

进行腐蚀及电化学测试

绘制了描述该体系应力腐蚀裂缝内各阶段热力学和动力学行为的实验电位～pH图.腐蚀率～pH曲线、电位～时间曲线和电位～pH图等均表明上述体系应力腐蚀裂缝内存在1个临界pH值(90℃时约为4.1).低于临界值

裂缝尖端发生钝态向活态的转变

腐蚀速度骤增

电位下降.应力和微区酸化都使裂缝内的钝化效果变差

腐蚀率增大.应力使裂缝尖端开始加速腐蚀的临界pH值升高.

Abstract

Specimens stressed at yieiding point in acidic occluded solutions were tested to simulate the mechanical and environmental states within stress corrosion cracks for "1Cr13 steel /0.5mol/L Cl-" system

and to determine the corrosion rates as well as the electrochemical behaviour of crack tips at different propagating stages. The experimental potential / pH diagrams depicting kinetic and thermodynamic behaviours inside cracks as well as mechanical and environmental effects on occluded cell corrosion were constructed. A critical pH value (about 4.1 at 90℃) was found from the "corrosion rate/pH" curve

"potential / time" curves

and potential / pH diagrams

below which passive-active transition occurred at crack tips and corrosion rate increased rapidly. Both stress and acidification caused a higher corrosion rate and a greater critical pH value.

关键词

Keywords

references

Views

403

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Study on performance enhancement and cold retention characteristics of solid packed bed cold energy storage

Study on the residence time distribution characteristics of the TPMS-Diamond static mixer

Study on entropy wave production and dissipation in partially premixed swirl flames subject to inlet perturbations

Advantages and risks of swirling cooling granulation towers

Performance analysis and application of thermal and humidity control system cascade driven by waste heat

Related Author

No data

Related Institution

No data

⁰