Effect of modified nanoTiO<sub>2</sub> on properties of coating and coated paper

LI Bin; LI Youming; LU Ruijiang

您当前的位置：

首页 >

文章列表页 >

Effect of modified nanoTiO₂ on properties of coating and coated paper

更新时间：2025-12-10

- Effect of modified nanoTiO₂ on properties of coating and coated paper
- CIESC Journal Issue 1, Pages: 228-234(2010)
- 作者机构：
  
  1. 华南理工大学制浆造纸工程国家重点实验室
  2. 华南理工大学造纸与污染控制国家工程研究中心
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Online First：05 January 2010，
  
  Published：05 January 2010
- 稿件说明：
移动端阅览
LI Bin, LI Youming, LU Ruijiang. Effect of modified nanoTiO₂ on properties of coating and coated paper[J]. CIESC Journal, 2010, (1): 228-234.
DOI：

LI Bin, LI Youming, LU Ruijiang. Effect of modified nanoTiO₂ on properties of coating and coated paper[J]. CIESC Journal, 2010, (1): 228-234. DOI：

摘要

研究了改性纳米TiO2对纸张涂料流变行为和涂布纸性能的影响。研究发现，在同一剪切速率下，随着改性纳米TiO2用量的增加，纸张涂料的表观黏度逐渐增大，且含改性纳米TiO2的纸张涂料具有较高的弹性模量和黏性模量，相位角则较低;随着改性纳米TiO2的用量在0～10%范围内增加，涂布纸的光学性能和印刷适性持续改善，且涂层表面结构的SEM和AFM观察显示，含改性纳米TiO2的纸张涂层表面具有较优的微观孔隙结构。

Abstract

The effect of modified nanoTiO2 on the rheological behavior of paper coating and the properties of coated paper was investigated.The results of rheological behavior experiment showed that at the same shear rate，the more amount of modified nanoTiO2，the higher the viscosity of paper coating.It was also proved that the dynamic elastic storage modulus and viscid loss modulus of paper coating containing modified nanoTiO2 were higher than those of paper coating containing unmodified nanoTiO2，while the phase angle was lower.Furthermore，the results of SEM and AFM showed that the better microscopic pore structure of coating surface could be built when modified nanoTiO2 was added into paper coating.In addition，with the increase of modified nanoTiO2 amount in the coated paper，the optical properties and printability of coated paper can be persistently improved.

关键词

Keywords

references

Views

403

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Phase morphology and rheological behavior of poly（ε-caprolactone）/polylactide blend

Hydrolysis resistance of aluminum nitride powder modified by organic carboxylic acid

Surface modification of graphite/phenolic resin composite plates with expanded graphite for PEMFC

Performance analysis and application of thermal and humidity control system cascade driven by waste heat

Research on the characterization of the molecular weight and its distribution of perfluoropolyether

Related Author

ZHANG Yisheng

WU Defeng

ZHANG Ming

GUO Xingzhong

YANG Hui

ZHANG Lingjie

MA Qi

GAO Lihua

Related Institution

扬州大学化学化工学院

江苏省环境材料与工程重点实验室

浙江大学材料科学与工程学系

浙江东新密封有限公司

天津大学化工学院化学工程研究所，化学工程联合国家重点实验室

⁰

Effect of modified nanoTiO2 on properties of coating and coated paper

DOI：

摘要

Abstract

关键词

Keywords

references

Effect of modified nanoTiO₂ on properties of coating and coated paper