Preparation of silica catalyst support with uniform pore sizes

WANG Wenhao; CHEN Shengli; ZHOU Zheng

您当前的位置：

首页 >

文章列表页 >

Preparation of silica catalyst support with uniform pore sizes

更新时间：2025-12-10

- Preparation of silica catalyst support with uniform pore sizes
- CIESC Journal Issue 9, Pages: 2373-2378(2010)
- 作者机构：
  
  中国石油大学重质油国家重点实验室
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Online First：05 September 2010，
  
  Published：05 September 2010
- 稿件说明：
移动端阅览
WANG Wenhao, CHEN Shengli, ZHOU Zheng. Preparation of silica catalyst support with uniform pore sizes[J]. CIESC Journal, 2010, (9): 2373-2378.
DOI：

WANG Wenhao, CHEN Shengli, ZHOU Zheng. Preparation of silica catalyst support with uniform pore sizes[J]. CIESC Journal, 2010, (9): 2373-2378. DOI：

摘要

利用单分散二氧化硅微球的水悬浮液，在一定条件下蒸发自组装合成了孔径均一的SiO2载体。采用低温氮吸附、压汞、SEM表征其孔结构及表面形态。结果表明，对于300 nm以下的单分散微球，都可以利用蒸发组装得到孔径均一的载体材料，且孔径尺寸可根据微球大小调变。实验发现蒸发组装制备的载体，其孔径分布受蒸发温度的影响较大。通过对蒸发温度的考察，发现50℃蒸发组装的样品孔径分布集中有序。

Abstract

Silica support materials with different and uniform pore size were fabricated by ordered-packing of monodisperse SiO2 spheres through evaporation assembling method.The pore structure was characterized with low temperature N2 adsorption-desorption method，mercury porosimeter and SEM.The results showed that the SiO2 spheres were closely and orderly packed with face centered cubic packing structure in the silica materials with uniform pore sizes.This method is especially appropriate for the assembling of small size（D<300 nm)SiO2 microspheres，and the assembly time is about 7 d.It is found that the uniformity of pore sizes of silica materials is affected by assembly condition and the optimal temperature of assembling opal is 50℃.

关键词

Keywords

references

Views

883

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

Properties of SiO2 coated nano SiO2/CaCO3 sorbents by precipitation method

SYNTHESIS AND CHARACTERIZATION OF SILICA-SUPPORTED PEG-400 Mo（Ⅵ）COMPLEX AND ITS CATALYTIC ACTIVITIES IN EPOXIDATION OF CYCLOHEXENE

Study on synergistic modification of nitrogen-doped carbon coating and Ti⁴⁺ co-doping for lithium vanadium phosphate cathode materials

Study on flash evaporation characteristics as well as thermodynamic variation performance in liquid hydrogen tank during on-orbit venting

Recent advances and perspectives on sulfide-based photocatalysts for hydrogen production

Related Author

SHI Qi

WU Sufang

ZHANG Yadong

WANG Zhenxing

CHEN Xia

JIANG Denggao

Related Institution

浙江大学化工系

郑州大学化工学院

山东理工大学

⁰