Preparation of La0.5Pb0.5MnO3 powder by rotating packed bed and its application in synthesis of diphenyl carbonate

LU Chao; JIN Fang; YUAN Hua; DU Zhiping; WU Yuanxin

您当前的位置：

首页 >

文章列表页 >

Preparation of La_0.5Pb_0.5MnO₃ powder by rotating packed bed and its application in synthesis of diphenyl carbonate

更新时间：2025-12-10

- Preparation of La_0.5Pb_0.5MnO₃ powder by rotating packed bed and its application in synthesis of diphenyl carbonate
- CIESC Journal Issue 5, Pages: 1137-1142(2010)
- 作者机构：
  
  武汉工程大学化工与制药学院绿色化工过程省部共建教育部重点实验室，湖北省新型反应器与绿色化学工艺重点实验室
- 作者简介：
- 基金信息：
- DOI：
  CLC：
- Online First：05 May 2010，
  
  Published：05 May 2010
- 稿件说明：
移动端阅览
LU Chao, JIN Fang, YUAN Hua, et al. Preparation of La_0.5Pb_0.5MnO₃ powder by rotating packed bed and its application in synthesis of diphenyl carbonate[J]. CIESC Journal, 2010, (5): 1137-1142.
DOI：

LU Chao, JIN Fang, YUAN Hua, et al. Preparation of La_0.5Pb_0.5MnO₃ powder by rotating packed bed and its application in synthesis of diphenyl carbonate[J]. CIESC Journal, 2010, (5): 1137-1142. DOI：

摘要

采用液液相共沉淀法在旋转填充床中合成钙钛矿型复合氧化物La0.5Pb0.5MnO3的前驱体，再经高温焙烧后制备出碳酸二苯酯合成催化剂的载体材料。考察了旋转填充床转速、反应物流量和添加分散剂PEG对La0.5Pb0.5MnO3物性的影响，通过XRD、BET、SEM、粒度分析手段对载体进行表征。结果表明，旋转填充床转速为1200 r·min-1，反应物流量为80 L·h-1，加入PEG10000时可制备出纯晶相的钙钛矿载体，相应的载钯(Pd占载体质量的0.5%)催化剂在氧化羰基化合成碳酸二苯酯反应中的活性最好。当反应总压为5 MPa、CO/O2分压比为96∶6、反应时间3 h、反应温度65℃时，碳酸二苯酯收率可达13.30%。

Abstract

The precursor of perovskite-type La0.5Pb0.5MnO3 oxide was prepared by co-precipitation method in rotating packed bed (RPB).The effects of rotating speed of RPB

flow rates of reactants and the addition of PEG10000 on properties of La0.5Pb0.5MnO3 powder were investigated in combination with XRD

BET and SEM techniques.The results showed that the suitable conditions for preparation of precursor were as follows: rotating speed of 1200 r·min-1

reactants flow rate of 80 L·h-1 and PEG10000 as disperser.The corresponding La0.5Pb0.5MnO3 powder obtained by calcined was used as supports for Pd- catalytic synthesis of diphenyl carbonate（DPC） and showed good performance.The yield of DPC could achieve 13.30% when reaction temperature was 65℃

p=5 MPa

p(CO)∶p(O2)=94∶6

and reaction time 3 h.

关键词

Keywords

references

Views

640

下载量

CSCD

Alert me when the article has been cited

提交

Tools

Publicity Resources

V-Cu oxide for transesterification of dimethyl carbonate with phenol

Direct synthesis of diphenyl carbonate with heterogeneous catalysis reactionⅨ effect of Ce loading methods on catalytic activity of catalyst

PREPARATION OF NOVEL ULTRAFINE EMBEDDED CATALYST FOR OXIDATIVE CARBONYLATION OF PHENOL TO DIPHENYL CARBONATE

Thermodynamic performance of tower-type solar-assisted supercritical compression CO2 energy storage system

Study on synergistic modification of nitrogen-doped carbon coating and Ti⁴⁺ co-doping for lithium vanadium phosphate cathode materials

Related Author

TONG Dongshen

CHEN Tong

HU Xuteng

YAO Jie

WANG Yue

WANG Gongying

ZHANG Guangxu

WU Yuanxin

Related Institution

中国科学院成都有机化学研究所

武汉化工学院湖北省绿色化学与新型反应器重点实验室

天津大学化工学院一碳化工国家重点实验室

北京化工大学理学院

河北工业大学绿色化工与高效节能河北省重点实验室

⁰